RESUMEN
Polyamide 6 (PA6) film as a typical viscoelastic material, satisfies the time-temperature superposition (TTS), and demonstrates obvious dynamic strain amplitude and frequency correlation under dynamic load. The investigation of the dynamic mechanical behavior of PA6 film is essential to ensure the safety of these materials in practical applications. In addition, dynamic mechanical property testing under conventional experimental conditions generally focuses on the short-term mechanical performance of materials. Therefore, the dynamic viscoelasticity of PA6 film was tested using a dynamic thermo-mechanical analyzer (DMA) in this study, and the complex modulus master curve was constructed based on time-temperature superposition (TTS) to realize the accelerated characterization of long-term mechanical properties. Furthermore, according to experimentally obtained asymmetric characteristics of the Cole-Cole diagram and the loss modulus master curve of the PA6 film, the parameter distribution of the fractional Zener model and the modified fractional Zener model were compared, and the asymmetric dynamic viscoelastic response of PA6 film under different conditions was systematically investigated using these models. The results indicate that the modified fractional Zener model can truly describe the dynamic asymmetric characteristics of PA6 film, verify the feasibility and advantages of the modified fractional rheological model, and provide some theoretical guidance for exploring the tensile rheological mechanism of PA6 film.
RESUMEN
Biaxially oriented polyamide 6 (BOPA6) films were prepared by extrusion casting and biaxial stretching with polyamide 6. The effects of different biaxially oriented on the macroscopic properties of BOPA6 were investigated by characterizing the rheological, crystallization, optical, barrier and mechanical properties. The results show that the increase of stretching temperature leads to the diffusion and regular stacking rate of BOPA6 chain segments towards crystal nuclei increases, the relative crystallinity increases, reaching 27.87% at 180 °C, and the mechanical strength and optical performance decrease. Heat-induced crystallization promotes the transformation of ß-crystals to α-crystals in BOPA6, resulting in a more perfect crystalline structure and enhancing oxygen barrier properties. BOPA6 chains are oriented, and strain-induced crystallization (SIC) occurs during the biaxial stretching. Further increasing the stretch ratio, the relative crystallinity increased to 30.34%. The machine direction (MD) and transverse direction (TD) tensile strength of BOPA6 (B-33) are nearly two times higher than the unstretched film, reaching 134.33 MPa and 155.28 MPa, respectively. In addition, the permeation decreases to 57.61 cc·mil/(m2 day), and the oxygen barrier performance has improved by nearly 30% compared to the sample B-22. BOPA6 has a high storage modulus at a high stretching rate (300%/s). Rapid chain relaxation would promote the molecular chain disorientation, destroy the entangled network of the molecular chain, and lead to a decrease in tensile strength, reducing to about 110 MPa.
RESUMEN
The biaxially-oriented PA56/512 has excellent mechanical strength, extensibility and water-oxygen barrier properties and has broad application prospects in green packaging, lithium battery diaphragm and medical equipment materials. The correlation between the aggregation structure evolution and macroscopic comprehensive properties of copolymer PA56/512 under biaxial stretching has been demonstrated in this work. The structure of the random copolymerization sequence was characterized by 13C Nuclear magnetic resonance (NMR). The typical isodimorphism behavior of the co-crystallization system of PA56/512 and its BOPA-56/512 films was revealed by differential scanning calorimetry (DSC) and X-ray diffraction (XRD) tests. And the aggregation structure, including the hydrogen bond arrangement, crystal structure and crystal morphology of PA56/512 before and after biaxial stretching, was investigated by XRD, Fourier-transform infrared spectroscopy (FTIR) and polarized optical microscopy (POM) tests. Furthermore, the effect of the biaxially-oriented stretching process on the mechanical properties of PA56/512 has been demonstrated. In addition, a deep insight into the influence of the structure on the crystallization process and physical-mechanical performance has been presented. The lowest melting point at a 512 content of 60 mol% is regarded as a "eutectic" point of the isodimorphism system. Due to the high disorder of the structural units in the polymer chain, the transition degree of the folded chain (gauche conformation) is relatively lowest when it is straightened to form an extended chain (trans conformation) during biaxially-oriented stretching, and part of the folded chain can be retained. This explains why biaxially stretched PA56/512 has high strength, outstanding toughness and excellent barrier properties at the pseudo-eutectic point. In this study, using the unique multi-scale aggregation structure characteristics of a heterohomodymite polyamide at the pseudo-eutectic point, combined with the new material design scheme and the idea of biaxial-stretching processing, a new idea for customized design of high-performance multifunctional polyamide synthetic materials is provided.