RESUMEN
The demand for durable, resistant, and high-strength structural material has led to the use of fibers as reinforcing elements. This paper presents an investigation into the inclusion of chopped steel wool fibers (CSWFs) in cement to form a high-flexural strength cementitious composite matrix (CCM). CSWFs were used as the primary reinforcement in CCM at increments of 0.5 wt%, from 0.5-6 wt%, with ratios of cement to sand of 1:1.5 and water to cement of 0.45. The inclusion of CSWFs resulted in an excellent optimization of the physicomechanical properties of the CCM, such as its density (2.302 g/cm3), compressive strength (61.452 MPa), and maximum flexural strength (10.64 MPa), all of which exceeded the performances of other reinforcement elements reported in the literature.
RESUMEN
Renewable solar energy is the key target to reduce fossil fuel consumption, minimize global warming issues, and indirectly minimizes erratic weather patterns. Herein, the authors synthesized an ultrathin reduced graphene oxide (rGO) nanosheet with ~47 nm via an improved Hummer's method. The TiO2 was deposited by RF sputtering onto an rGO nanosheet with a variation of temperature to enhance the photogenerated electron or charge carrier mobility transport for the photoanode component. The morphology, topologies, element composition, crystallinity as well as dye-sensitized solar cells' (DSSCs) performance were determined accordingly. Based on the results, FTIR spectra revealed presence of Ti-O-C bonds in every rGO-TiO2 nanocomposite samples at 800 cm-1. Besides, XRD revealed that a broad peak of anatase TiO2 was detected at ~25.4° after incorporation with the rGO. Furthermore, it was discovered that sputtering temperature of 120 °C created a desired power conversion energy (PCE) of 7.27% based on the J-V plot. Further increase of the sputtering temperature to 160 °C and 200 °C led to excessive TiO2 growth on the rGO nanosheet, thus resulting in undesirable charge recombination formed at the photoanode in the DSSC device.