RESUMEN
Further improvements in perovskite solar cells require better control of ionic defects in the perovskite photoactive layer during the manufacturing stage and their usage1-5. Here we report a living passivation strategy using a hindered urea/thiocarbamate bond6-8 Lewis acid-base material (HUBLA), where dynamic covalent bonds with water and heat-activated characteristics can dynamically heal the perovskite to ensure device performance and stability. Upon exposure to moisture or heat, HUBLA generates new agents and further passivates defects in the perovskite. This passivation strategy achieved high-performance devices with a power conversion efficiency (PCE) of 25.1 per cent. HUBLA devices retained 94 per cent of their initial PCE for approximately 1,500 hours of ageing at 85 degrees Celsius in nitrogen and maintained 88 per cent of their initial PCE after 1,000 hours of ageing at 85 degrees Celsius and 30 per cent relative humidity in air.
RESUMEN
In this study, butadiene sulfone (BS) was selected as an efficient electrolyte additive to stabilize the solid electrolyte interface (SEI) film on the lithium titanium oxide (LTO) electrodes in Li-ion batteries (LIBs). It was found that the use of BS as an additive could accelerate the growth of stable SEI film on the LTO surface, leading to the improved electrochemical stability of LTO electrodes. It can be supported by the BS additive to effectively reduce the thickness of SEI film, and it significantly enhances the electron migration in the SEI film. Consequently, the LIB-based LTO anode in the electrolyte containing 0.5 wt.% BS showed a superior electrochemical performance to that in the absence of BS. This work provides a new prospect for an efficient electrolyte additive for next-generation LIBs-based LTO anodes, especially when discharged to low voltage.
RESUMEN
In this paper, a facile and rapid aqueous-based electrochemical technique was used for the phase conversion of Ni into Ni(OH)2 thin film. The Ni(OH)2 thin film was directly converted and coated onto the network surface of Ni foam (NF) via the self-hydroxylation process under alkaline conditions using a simple cyclic voltammetry (CV) strategy. The as-formed and coated Ni(OH)2 thin film on the NF was used as the catalyst layer for the direct growth of carbon nanotubes (CNTs). The self-converted Ni(OH)2 thin film is a good catalytic layer for the growth of CNTs due to the fact that the OH- of the Ni(OH)2 can be reduced to H2O to promote the growth of CNTs during the CVD process, and therefore enabling the dense and uniform CNTs growth on the NF substrate. This binder-free CNTs/NF electrode displayed outstanding behavior as an electric double-layer capacitor (EDLC) due to the large surface area of the CNTs, showing excellent specific capacitance values of 737.4 mF cm-2 in the three-electrode configuration and 319.1 mF cm-2 in the two-electrode configuration, at the current density of 1 mA cm-2 in a 6 M KOH electrolyte. The CNTs/NF electrode also displayed good cycling stability, with a capacitance retention of 96.41% after 10,000 cycles, and this the excellent cycling performance can be attributed to the stable structure of the direct growth of CNTs with a strong attachment to the NF current collector, ensuring a good mechanical and electrical connection between the NF collector and the CNTs.
RESUMEN
In this current work, propargyl methacrylate (PMA) was successfully adopted to be an efficient electrolyte additive to stabilize the formation of a solid electrolyte interface (SEI) layer on mesoporous carbon microbeads (MCMB) in Li-ion batteries, especially at elevated temperatures. According to a series of material and electrochemical characterizations, the optimized concentration of PMA additive in the electrolyte was found to be 0.5 wt.%. The MCMB electrode cycled with the optimized 0.5 wt.% PMA-containing electrolyte exhibited impressive capacity retention of 90.3% after 50 cycles at 0.1C at elevated temperature, which was remarkably higher than that using the PMA-free electrolyte (83.5%). The improved electrochemical stability at elevated temperature could be ascribed to the rapid formation of stable and thin SEI layer on MCMB surface, which were investigated and suggested to be formed via PMA copolymerization reactions.
RESUMEN
Recently, urea electrolysis has been regarded as an up-and-coming pathway for the sustainability of hydrogen fuel production according to its far lower theoretical and thermodynamic electrolytic cell potential (0.37 V) compared to water electrolysis (1.23 V) and rectification of urea-rich wastewater pollution. The new era of the "hydrogen energy economy" involving urea electrolysis can efficiently promote the development of a low-carbon future. In recent decades, numerous inexpensive and fruitful nickel-based materials (metallic Ni, Ni-alloys, oxides/hydroxides, chalcogenides, nitrides and phosphides) have been explored as potential energy saving monofunctional and bifunctional electrocatalysts for urea electrolysis in alkaline solution. In this review, we start with a discussion about the basics and fundamentals of urea electrolysis, including the urea oxidation reaction (UOR) and the hydrogen evolution reaction (HER), and then discuss the strategies for designing electrocatalysts for the UOR, HER and both reactions (bifunctional). Next, the catalytic performance, mechanisms and factors including morphology, composition and electrode/electrolyte kinetics for the ameliorated and diminished activity of the various aforementioned nickel-based electrocatalysts for urea electrolysis, including monofunctional (UOR or HER) and bifunctional (UOR and HER) types, are summarized. Lastly, the features of persisting challenges, future prospects and expectations of unravelling the bifunctional electrocatalysts for urea-based energy conversion technologies, including urea electrolysis, urea fuel cells and photoelectrochemical urea splitting, are illuminated.
RESUMEN
The design and discovery of free-standing hybrid electrode materials with large absolute capacity and high cycling stability for energy storage become desirable and are still challenging. In this work, we demonstrate that the hybrid supercapacitor (HSC) device is assembled by 3D core-shell hierarchical nanorod arrays of Ni3S2@NiCoP nanocomposite for the first time. The Ni3S2@NiCoP nanocomposite is successfully synthesized through a facile stratagem containing hydrothermal process and the subsequent electrodeposition method. The 3D architecture of Ni3S2@NiCoP hybrid electrode composed of vertically aligned "hyperchannel" 1D Ni3S2 nanorods and highly conductive interconnected 2D nanosheets of NiCoP is beneficial to fast electron transfer kinetics, thus leading to enhancing the ionic and electronic conductivity, kinetics of redox reaction, and synergistic behavior of active species. The fabricated HSC device with Ni3S2@NiCoP electrode delivers outstanding areal capacity of 109 µAh cm-2 at a current density of 1 mA cm-2, brilliant energy density of 74.9 Wh kg-1 at a power density of 700 W kg-1, and prominent cyclic performance of 92% capacity retention even after 144-h floating test. This work demonstrates that the core-shell hierarchical nanorod arrays of Ni3S2@NiCoP can be viewed as one of the novel battery-type electrode materials for high-performance HSCs.
RESUMEN
NiSe nanoparticles are electrodeposited over a forest of carbon nanotubes (CNTs) to form an intertwined and porous network. The assynthesized composite (denoted as CNT@NiSe/SS) is used as a free-standing and multifunctional electrode for bothsupercapacitorsand overallwater splitting applications. For a supercapacitor application, CNT@NiSe/SS exhibits higher specific capacity and improved rate capability compared with individual NiSe and CNTs. A hybrid supercapacitor device consisting of battery-like CNT@NiSe/SS and EDLC-like graphene delivers a maximum energy density of 32.1 Wh kg-1 at a power density of 823 W kg-1 and has excellent stability after a floating test of 50 h. On the other hand, CNT@NiSe/SS also serves as a bifunctional electrocatalyst with high activity for overall water splitting. The CNT@NiSe/SS electrode displays excellent hydrogen and oxygen evolution reaction performance with the lowest overpotential of 174 mV at 10 mA cm-2 and 267 mV at 50 mA cm-2, respectively. The symmetrical two-electrode system requires an operating potential of 1.71 V to achieve a current density of 10 mA cm-2. Furthermore, this electrolyzer shows a negligible increment in potential after 24 hof continuouswater splitting. The outstanding performances of CNT@NiSe/SS can be attributed to the synergistic effect of NiSe and CNTs.
RESUMEN
The emerging dye-sensitized solar cells, perovskite solar cells, and organic solar cells have been regarded as promising photovoltaic technologies. The device structures and components of these solar cells are imperative to the device's efficiency and stability. Polymers can be used to adjust the device components and structures of these solar cells purposefully, due to their diversified properties. In dye-sensitized solar cells, polymers can be used as flexible substrates, pore- and film-forming agents of photoanode films, platinum-free counter electrodes, and the frameworks of quasi-solid-state electrolytes. In perovskite solar cells, polymers can be used as the additives to adjust the nucleation and crystallization processes in perovskite films. The polymers can also be used as hole transfer materials, electron transfer materials, and interface layer to enhance the carrier separation efficiency and reduce the recombination. In organic solar cells, polymers are often used as donor layers, buffer layers, and other polymer-based micro/nanostructures in binary or ternary devices to influence device performances. The current achievements about the applications of polymers in solar cells are reviewed and analyzed. In addition, the benefits of polymers for solar cells, the challenges for practical application, and possible solutions are also assessed.
RESUMEN
In this study, we reported an efficient, flexible, and low-cost (Pt-free and transparent conducting oxide (TCO)-free) counter electrode (CE) made of a polyimide (PI) substrate coated with a Ni3S2/Ni-P bilayer for dye-sensitized solar cells (DSCs). The bilayer Ni3S2/Ni-P hybrid film was deposited on a PI plastic substrate via a series of wet chemical/electrochemical processes. The bottom Ni-P layer was deposited on a PI to replace conventional TCO as a conductive layer, and the top Ni3S2 layer was employed as the electrocatalyst for I3(-) reduction. On the basis of the extensive electrochemical measurments, the as-prepared Ni3S2/Ni-P coated PI flexible CE demonstrated a Pt-like electrocatalytic for I3(-) reduction. As a result, the DSC assembled with the Ni3S2/Ni-P coated PI flexible CE exhibited an impressive photovoltaic conversion efficiency of 6.28% accompanied by a fill factor of 0.63 under 1 sun illumination (100 mW cm(-2), AM 1.5), which is comparative to that of the DSC based on the Pt coated indium tin oxide/polyethylene naphthalate (ITO/PEN) CE.
RESUMEN
The Ni3S2 nanoparticles with the diameters ranging from 10 to 80 nm are grown on the backbone of conductive multiwalled carbon nanotubes (MWCNTs) using a glucose-assisted hydrothermal method. It is found that the Ni3S2 nanoparticles deposited on MWCNTs disassemble into smaller components after the composite electrode is activated by the consecutive cyclic voltammetry scan in a 2 M KOH solution. Therefore, the active surface area of the Ni3S2 nanoparticles is increased, which further enhances the capacitive performance of the composite electrode. Because the synergistic effect of the Ni3S2 nanoparticles and MWCNTs on the capacitive performance of the composite electrode is pronounced, the composite electrode shows a high specific capacitance of 800 F/g and great cycling stability at a current density of 3.2 A/g. To examine the capacitive performance of the composite electrode in a full-cell configuration, an asymmetric supercapacitor device was fabricated by using the composite of Ni3S2 and MWCNTs as the cathode and activated carbon as the anode. The fabricated device can be operated reversibly between 0 and 1.6 V, and obtain a high specific capacitance of 55.8 F/g at 1 A/g, which delivers a maximum energy density of 19.8 Wh/kg at a power density of 798 W/kg. Furthermore, the asymmetric supercapacitor shows great stability based on the fact that the device retains 90% of its initial capacitance after a consecutive 5000 cycles of galvanostatic charge-discharge performed at a current density of 4 A/g.
RESUMEN
A transparent MoS(2)-graphene nanosheet (GNS) nanocomposite counter electrode (CE) was incorporated into a Pt-free dye-sensitized solar cell (DSC). The DSC assembled with the transparent MoS(2)-GNS CE therefore exhibited an impressive photovoltaic conversion efficiency of 5.81%, up to 93% of that obtained using the conventional Pt CE (6.24%).
RESUMEN
The tungsten sulfide/multi-wall carbon nanotube (WS(2)/MWCNT) hybrid was prepared in the presence of glucose by the hydrothermal route. The hybrid materials were used as counter electrode in the dye-sensitized solar cell (DSSC). The results of cyclic voltammetry measurement and electrochemical impedance spectroscopy indicated that the glucose aided prepared (G-A) WS(2)/MWCNT electrode had low charge-transfer resistance (R(ct)) and high electrocatalytic activity for triiodide reduction. The excellent electrochemical properties for (G-A) WS(2)/MWCNT electrode is due to the synergistic effects of WS(2) and MWCNTs, as well as amorphous carbon introduced by glucose. The DSSC based on the G-A WS(2)/MWCNT counter electrode achieved a high power conversion efficiency of 7.36%, which is comparable with the performance of the DSSC using Pt counter electrode (7.54%).
RESUMEN
We have applied a reusable silicon nanowire field-effect transistor (SiNW-FET) as a biosensor to conduct ultrasensitive detection of H5N2 avian influenza virus (AIV) in very dilute solution. The reversible surface functionalization of SiNW-FET was made possible using a disulfide linker. In the surface functionalization, 3-mercaptopropyltrimethoxysilane (MPTMS) was first modified on the SiNW-FET (referred to as MPTMS/SiNW-FET), with subsequent dithiothreitol washing to reduce any possible disulfide bonding between the thiol groups of MPTMS. Subsequently, receptor molecules could be immobilized on the MPTMS/SiNW-FET by the formation of a disulfide bond. The success of the reversible surface functionalization was verified with fluorescence examination and electrical measurements. A surface topograph of the SiNW-FET biosensor modified with a monoclonal antibody against H5N2 virus (referred to as mAb(H5)/SiNW-FET) after detecting approximately 10(-17) M H5N2 AIVs was scanned by atomic force microscopy to demonstrate that the SiNW-FET is capable of detecting very few H5N2 AIV particles.