An Easy-Made, Economical and Efficient Carbon-Doped Amorphous TiO2 Photocatalyst Obtained by Microwave Assisted Synthesis for the Degradation of Rhodamine B.

The search for novel materials and the development of improved processes for water purification have attracted the interest of researchers worldwide and the use of titanium dioxide in photocatalytic processes for the degradation of organic pollutants contained in water has been one of the benchmarks. Compared to crystalline titanium dioxide (cTiO2), the amorphous material has the advantages of having a higher adsorption capacity and being easier to dope with metal and non-metal elements. In this work, we take advantage of these two features to improve its photocatalytic properties in the degradation of Rhodamine B. The structural characterization by XRD analysis gives evidence of its amorphous nature and the SEM micrographs portray the disc morphology of 300 nm in diameter with heterogeneous grain boundaries. The degradation of Rhodamine B tests with the amorphous TiO2 using visible light confirm its improved catalytic activity compared to that of a commercial product, Degussa P25, which is a well-known crystalline material.

Synthesis and characterization of PbSe nanoparticles obtained by a colloidal route using Extran as a surfactant at low temperature.

Lead selenide nanoparticles (PbSe NPs) have been obtained through an easy and low cost route using colloidal synthesis in aqueous solution. The synthesis was carried out at room temperature using Extran (Na5P3O10, NaOH and H2O) as surfactant. Hydrochloric acid (HCl) was used to eliminate the generated by-products. The size of PbSe NPs was varied by changing the Pb:Se molar concentration. The PbSe NPs were characterized by powder x-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive x-ray analysis (EDAX), high-resolution transmission electron microscopy (HRTEM) and Raman spectroscopy. The XRD measurements showed that the PbSe NPs have the face-centered cubic phase structure. The crystal size was found to be between 14 and 20 nm as calculated from the XRD patterns and these values were corroborated with SEM and TEM. Additionally, HRTEM micrographs showed crystalline planes at (200), (220) and (111) of the PbSe NPs, in agreement with the XRD results.

DC and AC electroluminescence in silicon nanoparticles embedded in silicon-rich oxide films.

Electroluminescent properties of silicon-rich oxide (SRO) films were studied using metal oxide semiconductor-(MOS)-like devices. Thin SRO films with 4 at.% of silicon excess were deposited by low pressure chemical vapour deposition followed by a thermal annealing at 1100 degrees C. Intense continuous visible and infrared luminescence has been observed when devices are reversely and forwardly bias, respectively. After an electrical stress, the continuous electroluminescence (EL) is quenched but devices show strong field-effect EL with pulsed polarization. A model based on conductive paths--across the SRO film--has been proposed to explain the EL behaviour in these devices.