Particle Shedding from Cotton and Cotton-Polyester Fabrics in the Dry State and in Washes.

The influence of 3, 10 and 50 washing cycles on the properties of cotton fabric and cotton-polyester blend in plain weave, was investigated in this study. In addition to the analysis of tensile properties in weft and warp directions and thickness, the number of particles produced in the dry state was also measured after 3, 10 and 50 washes. After washing, the entire effluent was analysed by determining the total suspended solids (TSS), the total solids (TS), the pH value and the conductivity. To determine the similarity of the observed wash cycles and properties of all processed samples, hierarchical cluster analysis (HCA) was performed. The fabric changes indicated by total wear in the warp direction after 50 washing cycles compared to unwashed ones amounting to 41.2% for cotton and 30.9% for cotton-polyester blend, may be attributed to the synergy of washing factors and raw material composition. Cotton fabric produced significantly more particles than cotton-polyester fabric in the dry state after the examined washing cycles in all size categories. A smaller number of released particles are in the larger size category >25 µm. The obtained TSS values confirm the degree of loading of the effluent with particulate matter from the analysed fabrics, since the detergent consists of water-soluble components. The HCA dendrograms confirmed that the release of particles during the first washing cycles is mainly determined by the structural properties of fabrics, while in the subsequent cycles the synergistic effect of chemical, mechanical and thermal effects in the interaction with the material prevailed.

The Effect of Ultrasonic Treatment on the Binding of the Inclusion Complex ß-Cyclodextrin-peppermint Oil with Cellulose Material.

The purpose of the research was to measure the increase in the binding of inclusion complexes ß-cyclodextrin-peppermint oil (ß-CD_PM) to cellulose in cotton and cotton/polyester material with BTCA as the crosslinking agent by applying an ultrasonic bath at room temperature and a frequency of 80 kHz for 10 min. After sonication, the samples were left in a bath for 24 h after which they were dried, thermocondensed and subjected to a number of wash cycles. The treated samples were analysed with Attenuated total reflection (ATR) units heated up to 300 °C (Golden Gate (FTIR-ATR)) to monitor chemical changes indicative of crosslinking, while physico-chemical changes in the samples were monitored by using Fourier transform infrared spectroscopy (FTIR-ATR). Mechanical properties were measured according to EN ISO 13934-1:1999, and coloristic changes were evaluated by the whiteness degree according to CIE (WCIE) and the yellowing index (YI), while antimicrobial activity was determined according to AATCC TM 147-2016. The results show a physico-chemical modification of the UZV-treated cellulosic material. Moreover, partial antimicrobial efficacy on Gram-negative bacteria was confirmed for treated fabrics.