RESUMEN
A topological magnetic material showcases a multitude of intriguing properties resulting from the compelling interplay between topology and magnetism. These include notable phenomena such as a large anomalous Nernst effect (ANE), an anomalous Hall effect (AHE), and a topological Hall effect (THE). In most cases, topological transport phenomena are prevalent at temperatures considerably lower than room temperature, presenting a challenge for practical applications. However, the noncollinear ferromagnetic (FM) LaMn2Ge2, characterized by a Mn square-net lattice and a notably high Curie temperature (TC) of approximately 325 K, defies this trend as a topological semimetal. This work observes a giant topological Hall resistivity, ρ y x T $\rho _{yx}^T$ , of ≈4.5 µΩ cm at room temperature when the angle between the applied field and the c-axis is 75°, which is significantly higher than state-of-the-art materials with noncoplanar spin structures. The single crystal neutron diffraction measurements agree with an incommensurate conical magnetic structure as the ground state. This observation suggests the enhanced spin chirality resulting from the noncoplanar spin configuration when the applied field is away from the magnetic easy axis as the origin of a large contribution to the observed THE. The findings unequivocally demonstrate that the FM LaMn2Ge2 holds great promise as a potential topological semimetal for spintronic applications even at room temperature.
RESUMEN
Binary metal hydrides can act as low-temperature reducing agents for complex oxides in the solid state, facilitating the synthesis of anion-deficient oxide or oxyhydride phases. The reaction of LaSrCoRuO6, with CaH2 in a sealed tube yields the face-centered cubic phase LaSrCoRuO3.2H1.9. The reaction with LiH under similar conditions converts LaSrCoRuO6 to a mixture of tetragonal LaSrCoRuO4.8H1.2 and cubic LaSrCoRuO3.3H2.13. The formation of the LaSrCoRuOxHy oxyhydride phases proceeds directly from the parent oxide, with no evidence for anion-deficient LaSrCoRuO6-x intermediates, in contrast with many other topochemically synthesized transition-metal oxyhydrides. However, the reaction between LaSrCoRuO6 and LiH under flowing argon yields a mixture of LaSrCoRuO5 and the infinite layer phase LaSrCoRuO4. The change to all-oxide products when reactions are performed under flowing argon is attributed to the lower hydrogen partial pressure under these conditions. The implications for the reaction mechanism of these topochemical transformations is discussed along with the role of the hydrogen partial pressure in oxyhydride synthesis. Magnetization measurements indicate the LaSrCoRuOxHy phases exhibit local moments on Co and Ru centers, which are coupled antiferromagnetically. In contrast, LaSrCoRuO4 exhibits ferromagnetic behavior with a Curie temperature above 350 K, which can be rationalized on the basis of superexchange coupling between the Co1+ and Ru2+ centers.
RESUMEN
We report the high adsorption of NH3 in a titanium-based metal-organic framework, MFM-300(Ti), comprising extended [TiO6]∞ chains linked by biphenyl-3,3',5,5'-tetracarboxylate ligands. At 273 K and 1 bar, MFM-300(Ti) shows an exceptional NH3 uptake of 23.4 mmol g-1 with a record-high packing density of 0.84 g cm-3. Dynamic breakthrough experiments confirm the excellent uptake and separation of NH3 at low concentration (1000 ppm). The combination of in situ neutron powder diffraction and spectroscopic studies reveal strong, yet reversible binding interactions of NH3 to the framework oxygen sites.
RESUMEN
NdGa hydride and deuteride phases were prepared from high-quality NdGa samples and their structures characterized by powder and single-crystal X-ray diffraction and neutron powder diffraction. NdGa with the orthorhombic CrB-type structure absorbs hydrogen at hydrogen pressures ≤â 1â bar until reaching the composition NdGaH(D)1.1, which maintains a CrB-type structure. At elevated hydrogen pressure additional hydrogen is absorbed and the maximum composition recovered under standard temperature and pressure conditions is NdGaH(D)1.6 with the Cmcm LaGaH1.66-type structure. This structure is a threefold superstructure with respect to the CrB-type structure. The hydrogen atoms are ordered and distributed on three fully occupied Wyckoff positions corresponding to tetrahedral (4c, 8g) and trigonal-bipyramidal (8g) voids in the parent structure. The threefold superstructure is maintained in the H-deficient phases NaGaH(D)x until 1.6 ≥ x ≥ 1.2. At lower H concentrations, coinciding with the composition of the hydride obtained from hydrogenation at atmospheric pressure, the unit cell of the CrB-type structure is resumed. This phase can also display H deficiency, NdGaH(D)y (1.1 ≥ y ≥ 0.9), with H(D) exclusively situated in partially empty tetrahedral voids. The phase boundary between the threefold superstructure (LaGaH1.66 type) and the onefold structure (NdGaH1.1 type) is estimated on the basis of phase-composition isotherms and neutron powder diffraction to be x = 1.15.
RESUMEN
Complex transition-metal oxides exhibit a wide variety of chemical and physical properties which are a strong function the local electronic states of the transition-metal centres, as determined by a combination of metal oxidation state and local coordination environment. Topochemical reduction of the double perovskite oxide, LaSrCoRuO6 , using Zr, yields LaSrCoRuO5 . This reduced phase contains an ordered array of apex-linked square-based pyramidal Ru3+ O5 , square-planar Co1+ O4 and octahedral Co3+ O6 units, consistent with the coordination-geometry driven disproportionation of Co2+ . Coordination-geometry driven disproportionation of d7 transition-metal cations (e.g. Rh2+ , Pd3+ , Pt3+ ) is common in complex oxides containing 4d and 5d metals. However, the weak ligand field experienced by a 3d transition-metal such as cobalt leads to the expectation that d7+ Co2+ should be stable to disproportionation in oxide environments, so the presence of Co1+ O4 and Co3+ O6 units in LaSrCoRuO5 is surprising. Low-temperature measurements indicate LaSrCoRuO5 adopts a ferromagnetically ordered state below 120â K due to couplings between S=1 /2 Ru3+ and S=1 Co1+ .
RESUMEN
The selective capture of methane (CH4) at low concentrations and its separation from N2 are extremely challenging owing to the weak host-guest interactions between CH4 molecules and any sorbent material. Here, we report the exceptional adsorption of CH4 at low pressure and the efficient separation of CH4/N2 by MFM-300(Fe). MFM-300(Fe) shows a very high uptake for CH4 of 0.85â mmol g-1 at 1â mbar and 298â K and a record CH4/N2 selectivity of 45 for porous solids, representing a new benchmark for CH4 capture and CH4/N2 separation. The excellent separation of CH4/N2 by MFM-300(Fe) has been confirmed by dynamic breakthrough experiments. Inâ situ neutron powder diffraction, and solid-state nuclear magnetic resonance and diffuse reflectance infrared Fourier transform spectroscopies, coupled with modelling, reveal a unique and strong binding of CH4 molecules involving Fe-OHâ¯CH4 and Câ¯phenyl ring interactions within the pores of MFM-300(Fe), thus promoting the exceptional adsorption of CH4 at low pressure.
RESUMEN
Reaction between the pseudo-Ruddlesden-Popper phase Li2CaTa2O7 and MnCl2 at 375 °C yields MnCaTa2O7, a paramagnetic polar phase (space group P21nm), which adopts an a-b-c+/b-a-c+ distorted, layered perovskite structure. Magnetization and neutron diffraction data show that MnCaTa2O7 adopts an antiferromagnetically ordered state below TN = 56 K and exhibits large lattice parameter anomalies and a transient increase in its polar distortion mode at TA = 50 K. However, in contrast to the related phase MnSrTa2O7, MnCaTa2O7 shows no strong signature of weak ferromagnetism and thus shows no signs of magnetoelectric coupling. The differences in physical behavior between the two MnATa2O7 phases appear to be related to their differing Mn cation-order and differing TaO6 tilting schemes and demonstrate that even subtle changes to these orderings can have large effects on the distortion-mode couplings, which drive complex behavior of this class of "hybrid improper" ferroelectric material.
RESUMEN
Conversion of methane (CH4) to ethylene (C2H4) and/or acetylene (C2H2) enables routes to a wide range of products directly from natural gas. However, high reaction temperatures and pressures are often required to activate and convert CH4 controllably, and separating C2+ products from unreacted CH4 can be challenging. Here, we report the direct conversion of CH4 to C2H4 and C2H2 driven by non-thermal plasma under ambient (25 °C and 1 atm) and flow conditions over a metal-organic framework material, MFM-300(Fe). The selectivity for the formation of C2H4 and C2H2 reaches 96% with a high time yield of 334 µmol gcat-1 h-1. At a conversion of 10%, the selectivity to C2+ hydrocarbons and time yield exceed 98% and 2056 µmol gcat-1 h-1, respectively, representing a new benchmark for conversion of CH4. In situ neutron powder diffraction, inelastic neutron scattering and solid-state nuclear magnetic resonance, electron paramagnetic resonance (EPR), and diffuse reflectance infrared Fourier transform spectroscopies, coupled with modeling studies, reveal the crucial role of Fe-O(H)-Fe sites in activating CH4 and stabilizing reaction intermediates via the formation of an Fe-O(CH3)-Fe adduct. In addition, a cascade fixed-bed system has been developed to achieve online separation of C2H4 and C2H2 from unreacted CH4 for direct use. Integrating the processes of CH4 activation, conversion, and product separation within one system opens a new avenue for natural gas utility, bridging the gap between fundamental studies and practical applications in this area.
RESUMEN
The development of stable sorbent materials to deliver reversible adsorption of ammonia (NH3) is a challenging task. Here, we report the efficient capture and storage of NH3 in a series of robust microporous aluminium-based metal-organic framework materials, namely MIL-160, CAU-10-H, Al-fum, and MIL-53(Al). In particular, MIL-160 shows high uptakes of NH3 of 4.8 and 12.8 mmol g-1 at both low and high pressure (0.001 and 1.0 bar, respectively) at 298 K. The combination of in situ neutron powder diffraction, synchrotron infrared micro-spectroscopy and solid-state nuclear magnetic resonance spectroscopy reveals the preferred adsorption domains of NH3 molecules in MIL-160, with H/D site-exchange between the host and guest and an unusual distortion of the local structure of [AlO6] moieties being observed. Dynamic breakthrough experiments confirm the excellent ability of MIL-160 to capture of NH3 with a dynamic uptake of 4.2 mmol g-1 at 1000 ppm. The combination of high porosity, pore aperture size and multiple binding sites promotes the significant binding affinity and capacity for NH3, which makes it a promising candidate for practical applications.
RESUMEN
According to previous theoretical work, the binary oxide CuO can become a room-temperature multiferroic via tuning of the superexchange interactions by application of pressure. Thus far, however, there has been no experimental evidence for the predicted room-temperature multiferroicity. Here, we show by neutron diffraction that the multiferroic phase in CuO reaches 295 K with the application of 18.5 GPa pressure. We also develop a spin Hamiltonian based on density functional theory and employing superexchange theory for the magnetic interactions, which can reproduce the experimental results. The present Letter provides a stimulus to develop room-temperature multiferroic materials by alternative methods based on existing low temperature compounds, such as epitaxial strain, for tunable multifunctional devices and memory applications.
RESUMEN
We study near-neighbor and dipolar Ising models on a lattice of corner-sharing octahedra. In an extended parameter range of both models, frustration between antiferromagnetism and a spin-ice-like three-in-three-out rule stabilizes a Coulomb phase with correlated dipolar and quadrupolar spin textures, both yielding distinctive neutron-scattering signatures. Strong further-neighbor perturbations cause the two components to order independently, resulting in unusual multi-k orders. We propose experimental realizations of our model in rare-earth antiperovskites.
RESUMEN
Iron phosphate materials have attracted a lot of attention due to their potential as cathode materials for lithium-ion rechargeable batteries. It has been shown that lithium insertion or extraction depends on the Fe mixed valence and reduction or oxidation of the Fe ions' valences. In this paper, we report a new synthesis method for the Fe3(PO3OH)4(H2O)4 mixed valence iron phosphate. In addition, we perform temperature-dependent measurements of structural and physical properties in order to obtain an understanding of electronic-structural interplay in this compound. Scanning electron microscope images show needle-like single crystals of 50 µm to 200 µm length which are stable up to approximately 200 °C, as revealed by thermogravimetric analysis. The crystal structure of Fe3(PO3OH)4(H2O)4 single crystals has been determined in the temperature range of 90 K to 470 K. A monoclinic isostructural phase transition was found at ~213 K, with unit cell volume doubling in the low temperature phase. While the local environment of the Fe2+ ions does not change significantly across the structural phase transition, small antiphase rotations occur for the Fe3+ octahedra, implying some kind of electronic order. These results are corroborated by first principle calculations within density functional theory, which also point to ordering of the electronic degrees of freedom across the transition. The structural phase transition is confirmed by specific heat measurements. Moreover, hints of 3D antiferromagnetic ordering appear below ~11 K in the magnetic susceptibility measurements. Room temperature visible light absorption is consistent with the Fe2+/Fe3+ mixed valence.
RESUMEN
Sr2NiO2Cu2Se2, comprising alternating [Sr2NiO2]2+ and [Cu2Se2]2- layers, is reported. Powder neutron diffraction shows that the Ni2+ ions, which are in a highly elongated NiO4Se2 environment with D4h symmetry, adopt a high-spin configuration and carry localized magnetic moments which order antiferromagnetically below â¼160 K in a â2a × â2a × 2c expansion of the nuclear cell with an ordered moment of 1.31(2) µB per Ni2+ ion. The adoption of the high-spin configuration for this d 8 cation in a pseudo-square-planar ligand field is supported by consideration of the experimental bond lengths and the results of density functional theory (DFT) calculations. This is in contrast to the sulfide analogue Sr2NiO2Cu2S2, which, according to both experiment and DFT calculations, has a much more elongated ligand field, more consistent with the low-spin configuration commonly found for square-planar Ni2+, and accordingly, there is no evidence for magnetic moment on the Ni2+ ions. Examination of the solid solution Sr2NiO2Cu2(Se1-x S x )2 shows direct evidence from the evolution of the crystal structure and the magnetic ordering for the transition from high-spin selenide-rich compounds to low-spin sulfide-rich compounds as a function of composition. Compression of Sr2NiO2Cu2Se2 up to 7.2 GPa does not show any structural signature of a change in the spin state. Consideration of the experimental and computed Ni2+ coordination environments and their subtle changes as a function of temperature, in addition to transitions evident in the transport properties and magnetic susceptibilities in the end members, Sr2NiO2Cu2Se2 and Sr2NiO2Cu2S2, suggest that simple high-spin and low-spin models for Ni2+ may not be entirely appropriate and point to further complexities in these compounds.
RESUMEN
Kagome networks of ferromagnetically or antiferromagnetically coupled magnetic moments represent important models in the pursuit of a diverse array of novel quantum and topological states of matter. Here, we explore a family of Cu2+-containing metal-organic frameworks (MOFs) bearing kagome layers pillared by ditopic organic linkers with the general formula Cu3(CO3)2(x)3·2ClO4 (MOF-x), where x is 1,2-bis(4-pyridyl)ethane (bpe), 1,2-bis(4-pyridyl)ethylene (bpy), or 4,4'-azopyridine (azpy). Despite more than a decade of investigation, the nature of the magnetic exchange interactions in these materials remained unclear, meaning that whether the underlying magnetic model is that of an kagome ferromagnet or antiferromagnet is unknown. Using single-crystal X-ray diffraction, we have developed a chemically intuitive crystal structure for this family of materials. Then, through a combination of magnetic susceptibility, powder neutron diffraction, and muon-spin spectroscopy measurements, we show that the magnetic ground state of this family consists of ferromagnetic kagome layers that are coupled antiferromagnetically via their extended organic pillaring linkers.
RESUMEN
The development of efficient sorbent materials for sulfur dioxide (SO2) is of key industrial interest. However, due to the corrosive nature of SO2, conventional porous materials often exhibit poor reversibility and limited uptake toward SO2 sorption. Here, we report high adsorption of SO2 in a series of Cu(II)-carboxylate-based metal-organic framework materials. We describe the impact of ligand functionalization and open metal sites on the uptake and reversibility of SO2 adsorption. Specifically, MFM-101 and MFM-190(F) show fully reversible SO2 adsorption with remarkable capacities of 18.7 and 18.3 mmol g-1, respectively, at 298 K and 1 bar; the former represents the highest reversible uptake of SO2 under ambient conditions among all porous solids reported to date. In situ neutron powder diffraction and synchrotron infrared microspectroscopy enable the direct visualization of binding domains of adsorbed SO2 molecules as well as host-guest binding dynamics. We have found that the combination of open Cu(II) sites and ligand functionalization, together with the size and geometry of metal-ligand cages, plays an integral role in the enhancement of SO2 binding.
RESUMEN
Two novel chromium oxide arsenide materials have been synthesized, Sr2CrO2Cr2OAs2 (i.e., Sr2Cr3As2O3) and Sr2CrO3CrAs (i.e., Sr2Cr2AsO3), both of which contain chromium ions in two distinct layers. Sr2CrO2Cr2OAs2 was targeted following electron microscopy measurements on a related phase. It crystallizes in the space group P4/mmm and accommodates distorted CrO4As2 octahedra containing Cr2+ and distorted CrO2As4 octahedra containing Cr3+. In contrast, Sr2CrO3CrAs incorporates Cr3+ in CrO5 square-pyramidal coordination in [Sr2CrO3]+ layers and Cr2+ ions in CrAs4 tetrahedra in [CrAs]- layers and crystallizes in the space group P4/nmm. Powder neutron diffraction data reveal antiferromagnetic ordering in both compounds. In Sr2CrO3CrAs the Cr2+ moments in the [CrAs]- layers exhibit long-range ordering, while the Cr3+ moments in the [Sr2CrO3]+ layers only exhibit short-range ordering. However, in Sr2CrO2Cr2OAs2, both the Cr2+ moments in the CrO4As2 environments and the Cr3+ moments in the CrO2As4 polyhedra are long-range-ordered below 530(10) K. Above this temperature, only the Cr3+ moments are ordered with a Néel temperature slightly in excess of 600 K. A subtle structural change is evident in Sr2CrO2Cr2OAs2 below the magnetic ordering transitions.
RESUMEN
The development of materials showing rapid proton conduction with a low activation energy and stable performance over a wide temperature range is an important and challenging line of research. Here, we report confinement of sulfuric acid within porous MFM-300(Cr) to give MFM-300(Cr)·SO4(H3O)2, which exhibits a record-low activation energy of 0.04 eV, resulting in stable proton conductivity between 25 and 80 °C of >10-2 S cm-1. In situ synchrotron X-ray powder diffraction (SXPD), neutron powder diffraction (NPD), quasielastic neutron scattering (QENS), and molecular dynamics (MD) simulation reveal the pathways of proton transport and the molecular mechanism of proton diffusion within the pores. Confined sulfuric acid species together with adsorbed water molecules play a critical role in promoting the proton transfer through this robust network to afford a material in which proton conductivity is almost temperature-independent.
RESUMEN
The purification of light olefins is one of the most important chemical separations globally and consumes large amounts of energy. Porous materials have the capability to improve the efficiency of this process by acting as solid, regenerable adsorbents. However, to develop translational systems, the underlying mechanisms of adsorption in porous materials must be fully understood. Herein, we report the adsorption and dynamic separation of C2 and C3 hydrocarbons in the metal-organic framework MFM-300(In), which exhibits excellent performance in the separation of mixtures of ethane/ethylene and propyne/propylene. Unusually selective adsorption of ethane over ethylene at low pressure is observed, resulting in selective retention of ethane from a mixture of ethylene/ethane, thus demonstrating its potential for a one-step purification of ethylene (purity > 99.9%). In situ neutron powder diffraction and inelastic neutron scattering reveal the preferred adsorption domains and host-guest binding dynamics of adsorption of C2 and C3 hydrocarbons in MFM-300(In).
RESUMEN
The development of cost-effective sorbents for direct capture of trace CO2 (<1 %) from the atmosphere is an important and challenging task. Natural or commercial zeolites are promising sorbents, but their performance in adsorption of trace CO2 has been poorly explored to date. A systematic study on capture of trace CO2 by commercial faujasite zeolites reveals that the extra-framework cations play a key role on their performance. Under dry conditions, Ba-X displays high dynamic uptake of 1.79 and 0.69â mmol g-1 at CO2 concentrations of 10000 and 1000â ppm, respectively, and shows excellent recyclability in the temperature-swing adsorption processes. K-X exhibits perfect moisture resistance, and >95 % dry CO2 uptake can be preserved under relative humidity of 74 %. In situ solid-state NMR spectroscopy, synchrotron X-ray diffraction and neutron diffraction reveal two binding sites for CO2 in these zeolites, namely the basic framework oxygen atoms and the divalent alkaline earth metal ions. This study unlocks the potential of low-cost natural zeolites for applications in direct air capture.
RESUMEN
The presence of active sites in metal-organic framework (MOF) materials can control and affect their performance significantly in adsorption and catalysis. However, revealing the interactions between the substrate and active sites in MOFs at atomic precision remains a challenging task. Here, we report the direct observation of binding of NH3 in a series of UiO-66 materials containing atomically dispersed defects and open Cu(I) and Cu(II) sites. While all MOFs in this series exhibit similar surface areas (1111-1135 m2 g-1), decoration of the -OH site in UiO-66-defect with Cu(II) results in a 43% enhancement of the isothermal uptake of NH3 at 273 K and 1.0 bar from 11.8 in UiO-66-defect to 16.9 mmol g-1 in UiO-66-CuII. A 100% enhancement of dynamic adsorption of NH3 at a concentration level of 630 ppm from 2.07 mmol g-1 in UiO-66-defect to 4.15 mmol g-1 in UiO-66-CuII at 298 K is observed. In situ neutron powder diffraction, inelastic neutron scattering, and electron paramagnetic resonance, solid-state nuclear magnetic resonance, and infrared spectroscopies, coupled with modeling reveal that the enhanced NH3 uptake in UiO-66-CuII originates from a {Cu(II)···NH3} interaction, with a reversible change in geometry at Cu(II) from near-linear to trigonal coordination. This work represents the first example of structural elucidation of NH3 binding in MOFs containing open metal sites and will inform the design of new efficient MOF sorbents by targeted control of active sites for NH3 capture and storage.