A new beta TiNbSn alloy with a low Young's modulus of approximately 40 GPa has been developed to resolve the stress shielding by Young's modulus divergence. In this study, the efficacy of TiNbSn alloy locking plates on bone repair is compared to that of commercially pure titanium (CP-Ti). The TiNbSn alloy and CP-Ti, which have Young's moduli of 49.1 GPa and 107 GPa, respectively, were compared. Male Japanese white rabbits were anesthetized, and osteotomy and osteosynthesis with locking plates were performed on the right tibia. The bone repair was assessed using micro-computed tomography (CT), histomorphometry, immunohistochemistry, and mechanical testing. Micro-CT, histomorphometry, immunohistochemistry, and mechanical testing were performed four weeks after osteotomy. Six weeks after surgery, micro-CT and mechanical testing were performed. Micro-CT analysis at four weeks after surgery showed that the intramedullary fracture callus in the TiNbSn alloy group had more bone volume and numerous bridging structures compared to the CP-Ti group (CP-Ti vs. TiNbSn alloy, 34.3 ± 13.1 mm3 vs. 61.3 ± 19.6 mm3, p = 0.02; mean ± standard deviation). At four weeks post-osteotomy, the healed tibia showed significantly higher strength in the TiNbSn alloy group compared with CP-Ti (CP-Ti vs. TiNbSn alloy, 81.3 ± 31.2 N vs. 133.7 ± 46.6 N, p = 0.04). TiNbSn alloy locking plates had a more positive impact on bone formation and bone strength restoration than the CP-Ti locking plates during the early phase of bone healing.
Asunto(s)
Fijación Interna de Fracturas , Tibia , Masculino , Animales , Conejos , Módulo de Elasticidad , Tibia/diagnóstico por imagen , Tibia/cirugía , Microtomografía por Rayos X , AleacionesRESUMEN
BACKGROUND: The difference between Young's moduli of the femur and the stem causes stress shielding (SS). TiNbSn (TNS) stem has a low Young's modulus and strength with gradient functional properties during the change in elastic modulus with heat treatment. The aim of this study was to investigate the inhibitory effect of TNS stems on SS and their clinical outcomes compared to conventional stems. METHODS: This study was a clinical trial. Primary THA was performed using a TNS stem from April 2016 to September 2017 for patients in the TNS group. Unilateral THA was performed using a Ti6Al4V alloy stem from January 2007 to February 2011 for patients in the control group. The TNS and Ti6Al4V stems were matched in shape. Radiographs were obtained at the 1- and 3-year follow-ups. Two surgeons independently checked the SS grade and appearance of cortical hypertrophy (CH). The Japanese Orthopaedic Association (JOA) scores before and 1 year after surgery were assessed as clinical scores. RESULTS: None of the patients in the TNS group had grade 3 or 4 SS. In contrast, in the control group, 24% and 40% of patients had grade 3 and 4 SS at the 1- and 3-year follow-ups, respectively. The SS grade was lower in the TNS group than in the control group at the 1- and 3-year follow-ups (p < 0.001). The frequencies of CH in both groups were no significant difference at the 1- and 3-year follow-ups. The JOA scores of the TNS group significantly improved at 1 year after surgery and were comparable to control group. CONCLUSION: The TNS stem reduced SS at 1 and 3 years after THA compared to the proximal-engaging cementless stem, although the shapes of the stems matched. The TNS stem could reduce SS, stem loosening, and periprosthetic fractures. TRIAL REGISTRATION: Current Controlled Trials. ISRCTN21241251. https://www.isrctn.com/search?q=21241251 . The date of registration was October 26, 2021. Retrospectively registered.
Asunto(s)
Artroplastia de Reemplazo de Cadera , Prótesis de Cadera , Humanos , Aleaciones , Módulo de Elasticidad , Fémur/cirugíaRESUMEN
TiNbSn alloy is a high-performance titanium alloy which is biosafe, strong, and has a low Young's modulus. TiNbSn alloy has been clinically applied as a material for orthopedic prosthesis. Anodized TiNbSn alloys with acetic and sulfuric acid electrolytes have excellent biocompatibility for osseointegration. Herein, TiNbSn alloy was anodized in a sulfuric acid electrolyte to determine the antimicrobial activity. The photocatalytic activities of the anodic oxide alloys were investigated based on their electronic band structure and crystallinity. In addition, the cytotoxicity of the anodized TiNbSn alloy was evaluated using cell lines of the osteoblast and fibroblast lineages. The antimicrobial activity of the anodic oxide alloy was assessed according to the ISO 27447 using methicillin-susceptible Staphylococcus aureus, methicillin-resistant Staphylococcus aureus, and Escherichia coli. The anodic oxide comprised rutile and anatase titanium dioxide (TiO2) and exhibited a porous microstructure. A well-crystallized rutile TiO2 phase was observed in the anodized TiNbSn alloy. The methylene blue degradation tests under ultraviolet illumination exhibited photocatalytic activity. In antimicrobial tests, the anodized TiNbSn alloy exhibited robust antimicrobial activities under ultraviolet illumination for all bacterial species, regardless of drug resistance. Therefore, the anodized TiNbSn alloy can be used as a functional biomaterial with low Young's modulus and excellent antimicrobial activity.
RESUMEN
Titanium alloys are useful for application in orthopedic implants. However, complications, such as prosthetic infections and aseptic loosening, often occur after orthopedic devices are implanted. Therefore, innovation in surface modification techniques is essential to develop orthopedic materials with optimal properties at the biomaterial-bone interface. In this review, we present recent research on the improvement in the osteoconductivity and antibacterial effect of the Ti-33.6% Nb-4% Sn (TiNbSn) alloy by anodic oxidation and other related studies. TiNbSn alloys are excellent new titanium alloys with a low Young's modulus, high tensile strength, and with gradient functional properties such as a thermally adjustable Young's modulus and strength. Titanium dioxide (TiO2), when obtained by the anodic oxidation of a TiNbSn alloy, improves bone affinity and provides antibacterial performance owing to its photocatalytic activity. The safety of TiO2 and its strong bonding with metal materials make its method of preparation a promising alternative to conventional methods for improving the surface quality of orthopedic implants. Implementing anodization technology for TiNbSn alloys may alleviate orthopedic surgery-related complications, such as loosening, stress shielding, and infection after arthroplasty.
RESUMEN
BACKGROUND: Ti6Al4V alloy, which is commonly used for biomedical applications, has a Young modulus (110 GPa) that is higher than that of human cortical bone (11 to 20 GPa). Using an implant with a material with a low Young modulus that enhances load sharing by the bone even more than those made of Ti6Al4V could be beneficial for bone healing and further reduce the potential for stress shielding. A new ß-type TiNbSn alloy has a low Young modulus of approximately 40 to 49 GPa. However, whether the new titanium alloy with a lower Young modulus is advantageous in terms of fracture healing has not been assessed, and a small-animal model seems a reasonable first step in its assessment. QUESTIONS/PURPOSES: To assess the impact of a TiNbSn alloy plate with a lower Young modulus compared with a Ti6Al4V alloy plate on fracture healing, we evaluated: (1) bony bridging and callus volume, (2) new bone formation and remaining cartilage tissue, (3) osteoblast activity in the callus, and (4) mechanical strength and stiffness of the callus in bending. METHODS: Fracture plates manufactured from TiNbSn and Ti6Al4V alloys, which have Young moduli of 49 GPa and 110 GPa, respectively, were compared. The main reason for using rabbits was the high reliability of the three-point bending mechanical test of the rabbit tibia. Forty-two male Japanese white rabbits weighing 2.8 to 3.4 kg were anesthetized. A 5-cm skin incision was made on the medial side in the mid-diaphysis of the right tibia. Eight-hole plates were used, which were 42 mm long, 5 mm wide, and 1.2 mm thick. Plate fixation was performed using three proximal and three distal screws. After the plate was installed, an osteotomy was performed using a 1-mm-wide wire saw to create a standardized tibial transverse osteotomy model with a 1-mm gap. Bone healing was quantitatively assessed by two nonblinded observers using micro-CT (bony bridging and callus volume), histomorphometry (new bone formation and remaining cartilage tissue), immunohistochemistry (osteoblast activity), and mechanical testing (mechanical strength and stiffness in bending). Measurements on nondemineralized specimens were descriptive statistics due to their small number. Four weeks after osteotomy and fixation, 30 rabbits were euthanized to undergo micro-CT and subsequent mechanical testing (n = 12), histomorphometry and immunohistochemistry with demineralized specimens (n = 12), and histomorphometry with a nondemineralized specimen (n = 6). Eight weeks postoperatively, 12 rabbits were euthanized for micro-CT and subsequent mechanical testing. RESULTS: Intramedullary fracture calluses treated with TiNbSn alloy plates had larger bone volumes and more numerous bridging structures than those treated with Ti6Al4V alloy plates at 4 weeks after osteotomy (Ti6Al4V alloy versus TiNbSn alloy: 30 ± 7 mm 3 versus 52 ± 14 mm 3 , mean difference 22 [95% CI 9 to 37]; p = 0.005; ICC 0.98 [95% CI 0.95 to 0.99]). Histologic assessments demonstrated there was greater new bone formation (total callus: Ti6Al4V versus TiNbSn: 16 ± 4 mm 2 versus 24 ± 7 mm 2 , mean difference 8 [95% CI 1 to 16]; p = 0.04; ICC 0.98 [95% CI 0.93 to 0.99]; intramedullary callus: Ti6Al4V versus TiNbSn: 6 ± 4 mm 2 versus 13 ± 5 mm 2 , mean difference 7 [95% CI 1 to 13]; p = 0.02; ICC 0.98 [95% CI 0.95 to 0.99]) and a higher number of osteocalcin-positive cells (Ti6Al4V alloy versus TiNbSn alloy: 1397 ± 197 cells/mm 2 versus 2044 ± 183 cells/mm 2 , mean difference 647 [95% CI 402 to 892]; p < 0.001; ICC 0.98 [95% CI 0.95 to 0.99]) in the TiNbSn alloy group than in the Ti6Al4V alloy group. At 4 weeks after osteotomy, both bone strength and stiffness of the healed bone in the TiNbSn alloy group were higher than those in the Ti6Al4V alloy group (maximum load: Ti6Al4V alloy versus TiNbSn alloy: 83 ± 30 N versus 127 ± 26 N; mean difference 44 [95% CI 8 to 80]; p = 0.02; stiffness: Ti6Al4V alloy versus TiNbSn alloy: 92 ± 43 N/mm versus 165 ± 63 N/mm; mean difference 73 [95% CI 4 to 143]; p = 0.047). Eight weeks after osteotomy, no between-group differences were observed in the strength and stiffness of the healed bone. CONCLUSION: The results of this study indicate that TiNbSn alloy plate with a lower Young modulus resulted in improved bone formation and stiffer callus during the early phase (4 weeks after surgery) but not the later phase (8 weeks after surgery) of bone healing. CLINICAL RELEVANCE: An overly stiff plate may impair callus formation and bone healing. The TiNbSn alloy plate with a low Young modulus improves the early formation of new bone and stiff callus at the osteotomy site compared with the Ti6Al4V alloy plate in the healing process, which may promote bone repair. TiNbSn alloy may be a promising biomaterial for fracture treatment devices. Further research to address concerns about the strength of TiNbSn alloy plates, such as fatigue life and plate fracture, will be necessary for clinical applications, including mechanical tests to verify fatigue life and validation in larger animals with greater body weight.
Asunto(s)
Placas Óseas , Tibia , Aleaciones/química , Animales , Fenómenos Biomecánicos , Módulo de Elasticidad , Curación de Fractura , Humanos , Masculino , Conejos , Reproducibilidad de los Resultados , Tibia/cirugíaRESUMEN
In this study, we anodized a TiNbSn alloy with low Young's modulus in an electrolyte of sodium tartrate with and without hydrogen peroxide (H2O2). The photo-induced characteristics of the anodized alloy were analyzed for crystallinity and electrochemical conditions with comparisons to the effect with the addition of H2O2. The antibacterial activity was evaluated using methicillin-resistant Staphylococcus aureus and other pathogenic bacteria according to ISO 27447, and time decay antibacterial tests were also conducted. The anodized oxide had a porous microstructure with anatase- and rutile-structured titanium dioxide (TiO2). In contrast, the peaks of rutile-structured TiO2 were accelerated in the anodized TiNbSn alloy with H2O2. The formation of hydroxyl radicals and methylene blue breaching performance under ultraviolet irradiation was confirmed in the anodic oxide on TiNbSn alloy with and without H2O2. The anodic oxide on TiNbSn alloy had a robust antibacterial activity, and no significant difference was detected with or without H2O2. We conclude that anodized TiNbSn alloy with sodium tartrate electrolyte may be a functional biomaterial with a low Young's modulus and an antibacterial function.
RESUMEN
The optimal Young's modulus of material of orthopedic devices for fracture treatment is still unknown. The purpose of present study was to evaluate the impacts of intramedullary nails composed of a titanium alloy with low Young's modulus, on accelerating fracture healing compared with stainless steel with high Young's modulus. A ß-type TiNbSn alloy with a low Young's modulus close to that of human cortical bone was developed for clinical application. TiNbSn alloy with a Young's modulus of 45 GPa and stainless steel with a Young's modulus of 205 GPa were compared, with respect to the impacts on fracture healing. Fracture and fixation using intramedullary nail were performed on the right tibiae of C57BL/6 mice. The assessment of bone healing was performed via micro-computed tomography, histomorphometry, and quantitative reverse transcription polymerase chain reaction. In micro-computed tomography, larger bone volumes were observed in the fracture callus treated with TiNbSn alloy in comparison with those treated with stainless steel. Histological assessments confirmed accelerated cartilage absorption and new bone formation in the TiNbSn alloy group compared with the stainless steel group. The expression of Col1a1, Runx2, Dkk1, and Acp5 was higher in the TiNbSn alloy group, while that of Col2a1 and Col10a1 was lower in the late phase. The present study demonstrated that the fixation by intramedullary nails with TiNbSn alloy offered an accelerated fracture healing with promotion of bone formation via increased Runx2 expression. TiNbSn alloy might be a promising material for fracture treatment devices.
Asunto(s)
Aleaciones , Curación de Fractura , Aceleración , Animales , Subunidad alfa 1 del Factor de Unión al Sitio Principal , Módulo de Elasticidad , Ratones , Ratones Endogámicos C57BL , Acero Inoxidable , Microtomografía por Rayos XRESUMEN
Ti6Al4V alloy orthopedic implants are widely used as Ti6Al4V alloy is a biocompatible material and resistant to corrosion. However, Ti6Al4V alloy has higher Young's modulus compared with human bone. The difference of elastic modulus between bone and titanium alloy may evoke clinical problems because of stress shielding. To resolve this, we previously developed a TiNbSn alloy offering low Young's modulus and improved biocompatibility. In the present study, the effects of sulfuric acid anodic oxidation on the osseointegration of TiNbSn alloy were assessed. The apatite formation was evaluated with Scanning electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy and transmission electron microscopy analyses. The biocompatibility of TiNbSN alloy was evaluated in experimental animal models using pull-out tests and quantitative histological analyses. The results of the surface analyses indicated that sulfuric anodic oxidation induced abundant superficial apatite formation of the TiNbSn alloy disks and rods, with a 5.1-µm-thick oxide layer and submicron-sized pores. In vivo, treated rods showed increased mature lamellar bone formation and higher failure loads compared with untreated rods. Overall, our findings indicate that anodic oxidation with sulfuric acid may help to improve the biocompatibility of TiNbSn alloys for osseointegration.
RESUMEN
Intramedullary nailing is widely performed for internal fixation of fractures. The applicable elasticity of materials composing intramedullary nails remains unclear. The present study aimed to evaluate the effects of the elastic property of ß-type titanium alloy nails on fracture healing compared with conventional Ti-6Al-4V alloy nails using a rabbit tibial osteotomy model. Two types of intramedullary nails composed of ß-type Ti-Nb-Sn alloy (Young's modulus: 37 GPa) or Ti-6Al-4V alloy (Young's modulus: 110 GPa) were used for osteotomy fixation in the tibiae of rabbits. At 4, 8, and 16 weeks postoperatively, microcomputed tomography (micro-CT) and three-point bending tests were performed. Micro-CT images showed that the callus volume was significantly larger in the Ti-Nb-Sn alloy group at 4 and 8 weeks. The callus bone mineral density did not differ at each time point. In mechanical testing, the maximum load was significantly higher at all time points in the Ti-Nb-Sn alloy group. Taken together, the elastic intramedullary nails composed of Ti-Nb-Sn alloy improved the mechanical properties of the bone healing site from the early phase to the remodeling phase. Adequate Young's modulus of the Ti-Nb-Sn alloy enhanced fracture union and bone strength restoration. The Ti-Nb-Sn alloy is a promising biomaterial for fracture fixation devices. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 2018. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 107B: 700-707, 2019.
Asunto(s)
Aleaciones/química , Clavos Ortopédicos , Regeneración Ósea , Módulo de Elasticidad , Ensayo de Materiales , Osteotomía , Tibia , Animales , Niobio/química , Conejos , Tibia/metabolismo , Tibia/patología , Tibia/cirugía , Estaño/química , Titanio/químicaRESUMEN
The influence of Young's moduli of materials on the fracture healing process remains unclear. This study aimed to assess the effects of intramedullary nails composed of materials with low Young's moduli on fracture repair. We previously developed a ß-type Ti-Nb-Sn alloy with low Young's modulus close to that of human cortical bone. Here, we prepared two Ti-Nb-Sn alloys with Young's moduli of 45 and 78 GPa by heat treatment, and compared their effects on fracture healing. Fracture and nailing were performed in the right tibiae of C57BL/6 mice. The bone healing process was evaluated by microcomputed tomography (micro-CT), histomorphometry, and RT-PCR. We found larger bone volumes of fracture callus in the mice treated with the 45-GPa Ti-Nb-Sn alloy as compared with the 78-GPa Ti-Nb-Sn alloy in micro-CT analyses. This was confirmed with histology at day 14, with accelerated new bone formation and cartilage absorption in the 45-GPa Ti-Nb-Sn group compared with the 78-GPa Ti-Nb-Sn group. Acp5 expression was lower in the 45-GPa Ti-Nb-Sn group than in the 78-GPa Ti-Nb-Sn group at day 10. These findings indicate that intramedullary fixation with nails with a lower Young's modulus offer a greater capacity for fracture repair. Our 45-GPa Ti-Nb-Sn alloy is a promising material for fracture treatment implants. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 106B: 2841-2848, 2018.
Asunto(s)
Aleaciones/química , Clavos Ortopédicos , Módulo de Elasticidad , Curación de Fractura , Fracturas de la Tibia/terapia , Animales , Ratones , Niobio/química , Estaño/química , Titanio/químicaRESUMEN
Ti-6Al-4V alloy is widely prevalent as a material for orthopaedic implants because of its good corrosion resistance and biocompatibility. However, the discrepancy in Young's modulus between metal prosthesis and human cortical bone sometimes induces clinical problems, thigh pain and bone atrophy due to stress shielding. We designed a Ti-Nb-Sn alloy with a low Young's modulus to address problems of stress disproportion. In this study, we assessed effects of anodic oxidation with or without hot water treatment on the bone-bonding characteristics of a Ti-Nb-Sn alloy. We examined surface analyses and apatite formation by SEM micrographs, XPS and XRD analyses. We also evaluated biocompatibility in experimental animal models by measuring failure loads with a pull-out test and by quantitative histomorphometric analyses. By SEM, abundant apatite formation was observed on the surface of Ti-Nb-Sn alloy discs treated with anodic oxidation and hot water after incubation in Hank's solution. A strong peak of apatite formation was detected on the surface using XRD analyses. XPS analysis revealed an increase of the H2O fraction in O 1s XPS. Results of the pull-out test showed that the failure loads of Ti-Nb-Sn alloy rods treated with anodic oxidation and hot water was greater than those of untreated rods. Quantitative histomorphometric analyses indicated that anodic oxidation and hot water treatment induced higher new bone formation around the rods. Our findings indicate that Ti-Nb-Sn alloy treated with anodic oxidation and hot water showed greater capacity for apatite formation, stronger bone bonding and higher biocompatibility for osteosynthesis. Ti-Nb-Sn alloy treated with anodic oxidation and hot water treatment is a promising material for orthopaedic implants enabling higher osteosynthesis and lower stress disproportion.
Asunto(s)
Aleaciones/farmacología , Apatitas/metabolismo , Sustitutos de Huesos/farmacología , Módulo de Elasticidad/fisiología , Fijación Interna de Fracturas , Animales , Fémur/crecimiento & desarrollo , Fémur/fisiología , Humanos , Masculino , Ensayo de Materiales , Niobio/química , Oxidación-Reducción , Prótesis e Implantes , Conejos , Propiedades de Superficie , Estaño/química , Titanio/química , Titanio/farmacología , Agua/químicaRESUMEN
Stress shielding-related proximal femoral bone loss after total hip arthroplasty occurs because of the different stiffness of metallic alloy stems and host bone. To overcome this, we fabricated a low-modulus cementless hip stem from ß-type Ti-33.6Nb-4Sn alloy (TNS). Then we evaluated its stiffness, stress shielding, and initial stability compared with a similar Ti-6Al-4V alloy stem. Stiffness was determined by axial compression and cantilever-bending tests. Thirteen triaxial strain gages measured cortical strain. Stress shielding was defined as the percentage of intact strain after stem insertion. To evaluate initial stability, displacement transducers measured axial relative displacement and rotation. Intact and implanted femurs underwent single-leg-stance loading. Axial stiffness was 56% lower in the TNS stem than in the Ti-6Al-4V stem, and bending stiffness of the TNS stem decreased gradually from the proximal region to the distal region, being ≤ 53% that of the Ti-6Al-4V stem, indicating gradation of Young's modulus. The TNS stem decreased stress shielding in the proximal calcar region (A1: 83%, B1: 85% relative to intact cortical strain) without affecting the proximal lateral region (B3: 53%). The initial stabilities of the stems were comparable. These findings indicate that the TNS stem with gradation of Young's modulus minimizes proximal femoral bone loss and biological fixation, improving long-term stability.
Asunto(s)
Aleaciones , Prótesis de Cadera , Estaño , Titanio , Artroplastia de Reemplazo de Cadera , Módulo de Elasticidad , Elasticidad , Fémur , Humanos , Ensayo de Materiales , Diseño de Prótesis , Estrés MecánicoRESUMEN
The effect of swaging on the Young's modulus of ß Ti-33.6Nb-4Sn rods was investigated by X-ray diffraction, thermography, microstructural observations, deformation simulator analysis and cyclic tensile deformation. Stress-induced αâ³ martensite was stabilized by swaging, dependent on the diameter reduction rate during swaging. Thermography and deformation simulator analysis revealed that swaged rods were adiabatically heated, and consequently, stress-induced αâ³ underwent reverse transformation. Young's modulus, which was measured by the slope of the initial portion of the stress-strain curve, decreased from 56GPa in the hot-forged/quenched rod to 44GPa in the rapidly swaged rod with a high reduction rate and to 45GPa in the gradually swaged rod with a low reduction rate. The tangent modulus, which was measured by the slope of the tangent to any point on the stress-strain curve, decreased with strain even in the linear range of the stress-strain curve of the hot-forged/quenched rod and the rapidly swaged rod, while the tangent modulus remained unchanged for the gradually swaged rod. It was found that Young's moduli in swaged ß Ti-33.6Nb-4Sn rods were affected by stabilized αâ³ martensite. Low Young's modulus of 45GPa and high strength over 800MPa were obtained when the reverse transformation by adiabatic heating was suppressed and the stress-induced αâ³ was sufficiently stabilized by gradual swaging to a 75% reduction in cross section area.
Asunto(s)
Aleaciones/química , Módulo de Elasticidad , Calor , Ensayo de Materiales , Estrés Mecánico , Aleaciones Dentales/química , Niobio/química , Estaño/química , Titanio/químicaRESUMEN
This study used severe cold rolling followed by cold swaging of ß Ti-33.6% Nb-4% Sn rods to form a characteristic fiber structure composed of stress-induced αâ³ martensite with <010> texture and a ß phase with <101> texture, resulting in a material with a low Young's modulus of 40GPa. The material's tensile strength of 1270MPa and fatigue strength of 850MPa were attained by heat treatment at 673K for 5h through fine α precipitation in the fiber structure. A new method of fabricating a high-performance hip prosthetic stem was investigated based on the low Young's modulus and high strength obtained. After fabricating the stem by cold rolling, cold swaging, cold die-forging and machining, its neck region was given higher strength through local heat treatment, while the low Young's modulus remained almost unchanged in a distal portion of the stem. When a stem tip in the distal part was heat treated at 423K, reverse αâ³âß transformation occurred and the tangent modulus decreased to less than 30GPa, accompanied by stress-induced ßâαâ³. It was concluded that the method presented herein provided a low Young's modulus of approximately 40GPa in the distal part and high fatigue strength of approximately 850MPa in the neck region of a high-performance hip prosthetic stem.
Asunto(s)
Prótesis de Cadera , Niobio/química , Estaño/química , Titanio/química , Módulo de Elasticidad , Calor , Ensayo de Materiales , Resistencia a la TracciónRESUMEN
The mechanical properties and microstructures of ß Ti-25%Nb-11%Sn ternary alloy rods were investigated for biomedical applications as a function of heat treatment temperature after swaging by an 86% reduction in cross-section area. An as-swaged rod consisting of a ß (bcc) single phase shows a low Young's modulus of 53 GPa, which is interpreted in terms of both the metastable composition of the ß alloy undergoing neither an athermal ω transformation nor a deformation-induced ω transformation and <110>texture development during swaging. Heat treatment at 673 K (400 °C) for 2h leads to a high strength of approximately 1330 MPa and a high spring-back ratio of yield stress to Young's modulus over 15×10(-3), with acceptable elongation. This high strength is attributable to needle-like α precipitates, which are identified by high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) and high-resolution electron microscopy (HREM).
Asunto(s)
Aleaciones/química , Tecnología Biomédica/métodos , Fenómenos Mecánicos , Módulo de Elasticidad , Análisis de Fourier , Microscopía Electrónica de Rastreo , Tamaño de la Partícula , Estrés Mecánico , Temperatura , Resistencia a la Tracción , Difracción de Rayos XRESUMEN
This paper presents valuable evidence in support of the removal of a contaminant hydrocarbon layer adsorbed on photocatalytic TiO2 film by the latter's photo-oxidization. UV light was radiated on an anodic TiO2 film in an atmosphere-controlled chamber, and the film was then transferred to an ultrahigh-vacuum chamber for X-ray photoelectron spectroscopic (XPS) analysis; during the transfer, care was taken to ensure that the film was not exposed to air. This "in situ" setting eliminates the influence of carbon and water adsorptions during the transfer, thus enabling the accurate analysis of the UV-induced surface reaction. The spectral and quantitative results clearly revealed that the adsorbed hydrocarbon was removed from the photocatalytic TiO2 film when the film was irradiated in an oxygen atmosphere. Such removal occurs only in the case of TiO2 films that exhibit superhydrophilicity. This indicates that the removal of hydrocarbon is dependent on the UV-induced hydrophilicity on the film. In situ XPS measurement also presented evidence for UV-induced hydroxide group adsorption, where the adsorption was observed on both the surfaces showing superhydrophilicity and devoid of it.
RESUMEN
Magnetic iron oxide nanoparticles were successfully prepared by a novel reverse precipitation method with the irradiation of ultrasound. TEM, XRD and SQUID analyses showed that the formed particles were magnetite (Fe(3)O(4)) with about 10nm in their diameter. The magnetite nanoparticles exhibited superparamagnetism above 200K, and the saturation magnetization was 32.8 emu/g at 300 K. The sizes and size distributions could be controlled by the feeding conditions of FeSO(4).7H(2)O aqueous solution, and slower feeding rate and lower concentration lead to smaller and more uniform magnetite nanoparticles. The mechanisms of sonochemical oxidation were also discussed. The analyses of sonochemically produced oxidants in the presence of various gases suggested that besides sonochemically formed hydrogen peroxide, nitrite and nitrate ions contributed to Fe(II) ion oxidation.
Asunto(s)
Óxido Ferrosoférrico/química , Nanopartículas del Metal/química , Oxidantes/síntesis química , Ultrasonido , Precipitación Química , Nanopartículas del Metal/ultraestructura , Microscopía Electrónica de Transmisión , Oxidantes/química , Tamaño de la Partícula , Agua/química , Difracción de Rayos XRESUMEN
Aqueous sample solutions containing noble metal ions (HAuCl4, Na2PdCl4, H2PtCl6), polyethyleneglycol monostearate, and magnetic maghemite nanoparticles were irradiated with high power ultrasound. Analyses of the products showed that noble metal ions were reduced by the effects of ultrasound, and the formed noble metal nanoparticles were uniformly immobilized on the surface of the maghemite. The present "one pot process" significantly simplifies the immobilization of noble metal nanoparticles on the surface of supports, compared with the conventional impregnation method. The average diameter of immobilized Au was 7-13 nm, and the diameters of Pd and Pt were several nm. The diameters depended upon the concentration of polyethyleneglycol monostearate and the concentration of noble metal ions, but not upon the maghemite concentration, indicating the possibility of the morphological controls of the products by adjusting these preparation conditions. The measurements of the average diameters and the numbers of immobilized Au nanoparticles obtained under various conditions suggest that the nucleation of Au does not occur on the surface of maghemite, but it might occur in the homogeneous bulk solution.