RESUMEN
Nano-engineering III-nitride semiconductors offers a route to further control the optoelectronic properties, enabling novel functionalities and applications. Although a variety of lithography techniques are currently employed to nano-engineer these materials, the scalability and cost of the fabrication process can be an obstacle for large-scale manufacturing. In this paper, we report on the use of a fast, robust and flexible emerging patterning technique called Displacement Talbot lithography (DTL), to successfully nano-engineer III-nitride materials. DTL, along with its novel and unique combination with a lateral planar displacement (D2TL), allow the fabrication of a variety of periodic nanopatterns with a broad range of filling factors such as nanoholes, nanodots, nanorings and nanolines; all these features being achievable from one single mask. To illustrate the enormous possibilities opened by DTL/D2TL, dielectric and metal masks with a number of nanopatterns have been generated, allowing for the selective area growth of InGaN/GaN core-shell nanorods, the top-down plasma etching of III-nitride nanostructures, the top-down sublimation of GaN nanostructures, the hybrid top-down/bottom-up growth of AlN nanorods and GaN nanotubes, and the fabrication of nanopatterned sapphire substrates for AlN growth. Compared with their planar counterparts, these 3D nanostructures enable the reduction or filtering of structural defects and/or the enhancement of the light extraction, therefore improving the efficiency of the final device. These results, achieved on a wafer scale via DTL and upscalable to larger surfaces, have the potential to unlock the manufacturing of nano-engineered III-nitride materials.
RESUMEN
We investigate the optical properties of porous GaN films of different porosities, focusing on the behaviors of the excitonic features in time-integrated and time-resolved photoluminescence. A substantial enhancement of both excitonic emission intensity and recombination rate, along with insignificant intensity weakening under temperature rise, is observed in the porous GaN films. These observations are in line with (i) the local concentration of electric field at GaN nanoparticles and pores due to the depolarization effect, (ii) the efficient light extraction from the nanoparticles. Besides, the porosification enlarges the surface of the air/semiconductor interface, which further promotes the extraction efficiency and suppresses non-radiative recombination channels. Our findings open a way to increasing the emission efficiency of nanophotonic devices based on porous GaN.