RESUMEN
Carbon allotrope materials (i.e. carbon nanotubes (CNTs), graphene, graphene oxide (GO)), have been used to reinforce acrylic bone cement. Nevertheless, the intrinsic incompatibility among the above materials produces a deficient interphase. Thus, in this work, the effect of the content of functionalized graphene oxide with a reactive silane on the mechanical properties and cell adhesion of acrylic bone cement was studied. GO was obtained by an oxidative process on natural graphite; subsequently, GO was functionalized with 3-methacryloxypropyltrimethoxysilane (MPS) to enhance the interphase between the graphenic material and acrylic polymeric matrix. Pristine GO and functionalized graphene oxide (GO-MPS) were characterized physicochemically (XPS, XRD, FTIR, and Raman) and morphologically (SEM and TEM). Silanized GO was added into the acrylic bone cement at different concentrations; the resulting materials were characterized mechanically, and their biocompatibility was also evaluated. The physicochemical characterization results showed that graphite was successfully oxidized, and the obtained GO was successfully functionalized with the silane coupling agent (MPS). SEM and TEM images showed that the GO is composed of few stacked layers. Compression testing results indicated a tendency of increasing stiffness and toughness of the acrylic bone cements at low concentration of functionalized GO. Additionally, the bending testing results showed a slightly increase in bone cement strain with the incorporation of GO-MPS. Finally, all samples exhibited cell viability higher than 70%, which means that materials are considered non-cytotoxic, according to the ISO 10993-5 standard.
Asunto(s)
Grafito , Nanotubos de Carbono , Polimetil Metacrilato/química , Grafito/química , Ensayo de Materiales , Silanos , Cementos para Huesos/farmacología , Cementos para Huesos/químicaRESUMEN
Grafting polyethylene glycol (PEG) onto a polymer's surface is widely used to improve biocompatibility by reducing protein and cell adhesion. Although PEG is considered to be bioinert, its incorporation onto biomaterials has shown to improve cell viability depending on the amount and molecular weight (MW) used. This phenomenon was studied here by grafting PEG of three MW onto polyurethane (PU) substrata at three molar concentrations to assess their effect on PU surface properties and on the viability of osteoblasts and fibroblasts. PEG formed a covering on the substrata which increased the hydrophilicity and surface energy of PUs. Among the results, it was observed that osteoblast viability increased for all MW and grafting densities of PEG employed compared with unmodified PU. However, fibroblast viability only increased at certain combinations of MW and grafting densities of PEG, suggesting an optimal level of these parameters. PEG grafting also promoted a more spread cell morphology than that exhibited by unmodified PU; nevertheless, cells became apoptotic-like as PEG MW and grafting density were increased. These effects on cells could be due to PEG affecting culture medium pH, which became more alkaline at higher MW and concentrations of PEG. Results support the hypothesis that surface energy of PU substrates can be tuned by controlling the MW and grafting density of PEG, but these parameters should be optimized to promote cell viability without inducing apoptotic-like behavior.
RESUMEN
Natural fiber-reinforced composite (NFRC) filaments for 3D printing were fabricated using polylactic acid (PLA) reinforced with 1-5 wt% henequen flour comprising particles with sizes between 90-250 µm. The flour was obtained from natural henequen fibers. NFRCs and pristine PLA specimens were printed with a 0° raster angle for tension tests. The results showed that the NFRCs' measured density, porosity, and degree of crystallinity increased with flour content. The tensile tests showed that the NFRC Young's modulus was lower than that of the printed pristine PLA. For 1 wt% flour content, the NFRCs' maximum stress and strain to failure were higher than those of the printed PLA, which was attributed to the henequen fibers acting as reinforcement and delaying crack growth. However, for 2 wt% and higher flour contents, the NFRCs' maximum stress was lower than that of the printed PLA. Microscopic characterization after testing showed an increase in voids and defects, with the increase in flour content attributed to particle agglomeration. For 1 wt% flour content, the NFRCs were also printed with raster angles of ±45° and 90° for comparison; the highest tensile properties were obtained with a 0° raster angle. Finally, adding 3 wt% content of maleic anhydride to the NFRC with 1 wt% flour content slightly increased the maximum stress. The results presented herein warrant further research to fully understand the mechanical properties of printed NFRCs made of PLA reinforced with natural henequen fibers.
RESUMEN
The properties of biological-chemical chitosan (BCh) films from marine-industrial waste and a non-conventional Ramon starch (RS) (Brosimum alicastrum) were investigated. Blended films of BCh/RS were prepared to a volume ratio of 4:1 and 1:4, named (BChRS-80+q, biological-chemical chitosan 80% v/v and Ramon starch, BChRS-20+q, biological-chemical chitosan 20% v/v and Ramon starch, both with quercetin), Films from commercial chitosan (CCh) and corn starch (CS), alone or blended (CChCS-80+q, commercial chitosan 80% v/v and corn starch, CChCS-20+q commercial chitosan 20% v/v and corn starch, both with quercetin) were also prepared for comparison purposes. Films were investigated for their physicochemical characteristics such as thickness, moisture, swelling, water-vapor permeability, and water solubility. In addition, their mechanical and structural properties were studied using Fourier Transform Infrared Spectroscopy (FTIR), Thermogravimetric analysis (TGA) and Scanning Electron Microscopy (SEM) techniques. Antioxidant activity was evaluated as radical scavenging, and antimicrobial effect was also determined. The BCh and RS films presented similar tensile strength values compared with commercial biopolymers. Only films with chitosan presented antioxidant and antimicrobial activity. The FTIR spectra confirmed the interactions between functional groups of the biopolymers. Although, BChRS-80+q and BChRS-20+q films exhibited poor mechanical performance compared to their commercial counterparts, they showed good thermal stability, and improved antioxidant and antimicrobial activity in the presence of quercetin. BChRS-80+q and BChRS-20+q films have promising applications due to their biological activity and mechanical properties, based on a novel material that has been underutilized (Ramon starch) that does not compete with materials for human feeding and may be used as a coating for food products.
RESUMEN
Recently, different carbon-based nanomaterials have been used as reinforcing agents in acrylic bone cement formulations. Among them, graphene oxide (GO) has attracted the attention of scientific community since it could improve not only the mechanical properties but also the biocompatibility characteristics of these materials. However, using GO presents some drawbacks, such as its poor dispersion and lack of interaction with polymeric matrices, which should be prior resolved to achieve its optimal performance in acrylic bone cement. Thus, in this work, GO was treated with 3-methacryloxy propyl trimethoxy silane at various concentrations (1, 3 and 5 wt.%) to improve the interaction between the nanofiller and the poly (methyl methacrylate) matrix. Modified GO was incorporated at different percentages (0.1, 0.5 and 0.75 wt.%) into acrylic bone cement formulations and some properties were evaluated. The silanization process of the GO was confirmed by FTIR, TGA and EDX. The improvement in the mechanical performance was monitored on the compression properties whereas those related with biological properties were evaluated by osteoblast cell viability and hemocompatibility tests. Results suggest that using a 1 wt.% of the silane coupling agent, during surface treatment of GO, yields the best mechanical performance in this type of materials. It was also found that the presence of neat GO or silanized GO does not compromise the cytocompatibility and hemocompatibility of acrylic bone cement formulations.
Asunto(s)
Grafito , Polimetil Metacrilato , Cementos para Huesos , Ensayo de MaterialesRESUMEN
In this work, the effect of the incorporation of comonomers containing amine groups on the mechanical and fracture properties of acrylic bone cements was studied. Cements were prepared with either diethyl amino ethyl acrylate (DEAEA), dimethyl amino ethyl methacrylate (DMAEM) or diethyl amino ethyl methacrylate (DEAEM) as comonomer in the liquid phase. It was found that strength and modulus decreased with increasing comonomer content in the bending and compressive tests. It was also observed that fracture toughness (K(IC)) and the critical strain energy release rate (G(IC)) increase with increasing comonomer concentration and are significantly higher compared to the control formulation. The mechanical and fracture properties of cements were also evaluated after soaking the specimens in Simulated Body Fluid (SBF) for 3 and 6 months. It was found that the mechanical properties of cements decreased when the samples were stored in SBF, although the impact strength increased in the first 3 months and then decreased. SEM micrographs were in agreement with the results obtained during mechanical characterization as the increase in toughness was confirmed by the appearance of ductile tearing pattern which is associated with plastic deformation.