RESUMEN
Thin films of the wide band gap semiconductor ß-Ga2O3 have a high potential for applications in transparent electronics and high power devices. However, the role of interfaces remains to be explored. Here, we report on fundamental limits of transport properties in thin films. The conductivities, Hall densities and mobilities in thin homoepitaxially MOVPE grown (100)-orientated ß-Ga2O3 films were measured as a function of temperature and film thickness. At room temperature, the electron mobilities ((115 ± 10) cm2/Vs) in thicker films (>150 nm) are comparable to the best of bulk. However, the mobility is strongly reduced by more than two orders of magnitude with decreasing film thickness ((5.5 ± 0.5) cm2/Vs for a 28 nm thin film). We find that the commonly applied classical Fuchs-Sondheimer model does not explain sufficiently the contribution of electron scattering at the film surfaces. Instead, by applying an electron wave model by Bergmann, a contribution to the mobility suppression due to the large de Broglie wavelength in ß-Ga2O3 is proposed as a limiting quantum mechanical size effect.
RESUMEN
Physical vapour deposition (PVD) is used to grow millimetre-long Bi2Te3 sub-micron belts catalysed by TiO2 nanoparticles. The catalytic efficiency of TiO2 nanoparticles for the nanostructure growth is compared with the catalyst-free growth employing scanning electron microscopy. The catalyst-coated and catalyst-free substrates are arranged side-by-side, and overgrown at the same time, to assure identical growth conditions in the PVD furnace. It is found that the catalyst enhances the yield of the belts. Very long belts were achieved with a growth rate of 28 nm/min. A â¼1-mm-long belt with a rectangular cross section was obtained after 8 h of growth. The thickness and width were determined by atomic force microscopy, and their ratio is â¼1:10. The chemical composition was determined to be stoichiometric Bi2Te3 using energy-dispersive X-ray spectroscopy. Temperature-dependent conductivity measurements show a characteristic increase of the conductivity at low temperatures. The room temperature conductivity of 0.20 × 10(5) S m (-1) indicates an excellent sample quality.
RESUMEN
In this article a microfabricated thermoelectric nanowire characterization platform to investigate the thermoelectric and structural properties of single nanowires is presented. By means of dielectrophoresis (DEP), a method to manipulate and orient nanowires in a controlled way to assemble them onto our measurement platform is introduced. The thermoelectric platform fabricated with optimally designed DEP electrodes results in a yield of nanowire assembly of approximately 90% under an applied peak-to-peak ac signal Vpp = 10 V and frequency f = 20 MHz within a series of 200 experiments. Ohmic contacts between the aligned single nanowire and the electrodes on the platform are established by electron beam-induced deposition. The Seebeck coefficient and electrical conductivity of electrochemically synthesized Bi2Te3 nanowires are measured to be -51 µV K(-1) and (943 ± 160)/(Ω(-1) cm(-1)), respectively. Chemical composition and crystallographic structure are obtained using transmission electron microscopy. The selected nanowire is observed to be single crystalline over its entire length and no grain boundaries are detected. At the surface of the nanowire, 66.1 ± 1.1 at.% Te and 34.9 ± 1.1 at.% Bi are observed. In contrast, chemical composition of 64.2 at.% Te and 35.8 at.% Bi is detected in the thick center of the nanowire.