Protective effect of a nanofilled resin-based coating on wear resistance of glass ionomer cement restorative materials.

BACKGROUND: The effect of nanofilled resin-based coating on the wear resistance of glass ionomer cements (GICs) is still controversial. This study aims to compare the wear resistance of four encapsulated GICs including two conventional and two resin-modified, and to evaluate the effect of G-Coat Plus on the wear resistance of GICs. METHODS: A total of 80 disk-shaped specimens were prepared from two CGICs (riva self cure (SDI) and Equia Forte Fil (GC) and two RM- GICs (Ketac Nano (3 M/ESPE) and Fuji II LC (GC). The specimens of each material were divided into two groups (n = 10) based on the surface protection: no coating (NC), and coating with G-Coat Plus (GCP). All specimens were then placed in distilled water for 24 h at 37 °C. The specimens were subjected to thermocycling for 120,000 cycles using a chewing simulator. Wear resistance was measured using a specific formula. Data was analyzed using Kruskal-Wallis test. RESULTS: There was no significant difference in volume loss (mm3) between coated and uncoated groups for all materials (P > 0.05). Ketac Nano showed significantly lower volume loss (0.65 ± 0.12) compared to all other groups (P < 0.05) among uncoated specimen, and significantly lower than Fuji II LC (P = 0.035) and Equia Forte Fil (P = 0.040) among coated groups. However, no statically significant difference was observed between volume loss of coated Ketac Nano with that of riva self cure (P = 0.087). CONCLUSIONS: Coating with GCP did not affect the wear depth of GICs, and Ketac Nano showed significantly lower volume loss regardless of coating.

Evaluating the Mechanical Properties of Zinc-Coated Stainless Steel Orthodontic Wires Using Physical Vapor Deposition.

The aim of this study was to evaluate the mechanical properties of stainless steel (SS) orthodontic wires coated with zinc (Zn), using a Physical Vapored Deposition (PVD) machine. A total of 100 straight SS orthodontic wires were cut into pieces of 5 centimeters in length and were divided into two groups. Half of the wires were coated with Zn using a PVD machine, and the others remained uncoated. Tensile strength (n = 15), three-point bending (n = 15), and frictional resistance at 0° (n = 10) and 10° (n = 10) were measured to compare the mechanical properties of the Zn-coated and uncoated orthodontic wires using the universal testing machine. The surface of the coated wires was observed by SEM and AFM. An independent t-test, multivariate ANOVA, and measurement ANOVA were used for data analysis. SEM and AFM showed a homogenous Zn layer of 0.28 ± 0.006 µm on the SS wires. The tensile strength and three-point bending strength significantly increased after Zn coating of wires with the PVD method (P < 0.05). The friction resistance significantly reduced at both angulations following the coating procedure. The angle between the wire and bracket had no significant effect on the frictional resistance (P > 0.05). Coating with Zn improved the tensile and load-bending strength of SS orthodontic wires and reduced their frictional resistance which might be advantageous in terms of reducing the risk of root resorption during the orthodontic treatment.