Assessing the Effect of Cellulose Nanocrystal Content on the Biodegradation Kinetics of Multiscale Polylactic Acid Composites under Controlled Thermophilic Composting Conditions.

This work studied the effect of cellulose nanocrystal (NCC) content on the biodegradation kinetics of PLA-based multiscale cellulosic biocomposites (PLAMCBs). To facilitate biodegradation, the materials were subjected to thermo-oxidation before composting. Biodegradation was carried out for 180 days under controlled thermophilic composting conditions according to the ASTM D 5338 standard. A first-order model based on Monod's kinetics under limiting substrate conditions was used to study the effect of cellulose nanocrystal (NCC) content on the biodegradation kinetics of multiscale composite materials. It was found that thermo-oxidation at 70 °C for 160 h increased the biodegradability of PLA. Also, it was found that the incorporation of cellulosic fibrous reinforcements increased the biodegradability of PLA by promoting hydrolysis during the first stage of composting. Likewise, it was found that partial substitution of micro cellulose (MFC) by cellulose nanocrystals (NCCs) increased the biodegradability of the biocomposite. This increase was more evident as the NCC content increased, which was attributed to the fact that the incorporation of cellulose nanocrystals facilitated the entry of water into the material and therefore promoted the hydrolytic degradation of the most recalcitrant fraction of PLA from the bulk and not only by surface erosion.

Effect of Cellulose and Cellulose Nanocrystal Contents on the Biodegradation, under Composting Conditions, of Hierarchical PLA Biocomposites.

In this work, the effect of microfibrillated cellulose (MFC) and cellulose nanocrystals (CNCs) on the biodegradation, under composting conditions, of hierarchical PLA biocomposites (HBCs) was studied using a full 22 factorial experimental design. The HBCs were prepared by extrusion processing and were composted for 180 days. At certain time intervals, the specimens were removed from the compost for their chemical, thermal and morphological characterizations. An ANOVA analysis was carried out at different composting times to study MFC and CNCs' effects on biodegradation. The specimen's mass loss and molecular weight loss were selected as independent variables. The results show that the presence of MFC enhances the PLA biodegradation, while with CNCs it decreases. However, when both cellulosic fibers are present, a synergistic effect was evident-i.e., in the presence of the MFC, the inclusion of the CNCs accelerates the HBCs biodegradation. Analysis of the ANOVA results confirms the relevance of the synergistic role between both cellulosic fibers over the HBC biodegradation under composting conditions. The results also suggest that during the first 90 days of incubation, the hydrolytic PLA degradation prevails, whereas, beyond that, the enzymatic microbial biodegradation dominates. The SEM results show MFC's presence enhances the surface biodeterioration to a greater extent than the CNCs and that their simultaneous presence enhances PLA biodegradation. The SEM results also indicate that the biodegradation process begins from hydrophilic cellulosic fibers and promotes PLA biodegradation.