RESUMEN
Three-dimensional (3D) microfabrication techniques play a crucial role across various research fields. These techniques enable the creation of functional 3D structures on the microscale, unlocking possibilities for diverse applications. However, conventional fabrication methods have limits in producing complex 3D structures, which require numerous fabrication steps that increase the costs. Graphene is an atomically thin material known for its deformability and impermeability to small gases and molecules, including reactive gases like XeF2. These features make graphene a potential candidate as an etch mask for 3D microfabrication. Here, we report the fabrication of various 3D microstructures using graphene etch masks directly grown and patterned on a Si substrate. The patterned graphene deforms and wraps the etched structures, allowing for the fabrication of complicated 3D microstructures, such as mushroom-like and step-like microstructures. As a practical demonstration of the graphene etch mask, we fabricate an omniphobic surface of reentrant 3D structures on a Si substrate. Our work provides a method for fabricating complex 3D microstructures using a graphene etch mask, contributing to advancements in etching and fabrication processes.
RESUMEN
A gate stack that facilitates a high-quality interface and tight electrostatic control is crucial for realizing high-performance and low-power field-effect transistors (FETs). However, when constructing conventional metal-oxide-semiconductor structures with two-dimensional (2D) transition metal dichalcogenide channels, achieving these requirements becomes challenging due to inherent difficulties in obtaining high-quality gate dielectrics through native oxidation or film deposition. Here, a gate-dielectric-less device architecture of van der Waals Schottky gated metal-semiconductor FETs (vdW-SG MESFETs) using a molybdenum disulfide (MoS2) channel and surface-oxidized metal gates such as nickel and copper is reported. Benefiting from the strong SG coupling, these MESFETs operate at remarkably low gate voltages, <0.5 V. Notably, they also exhibit Boltzmann-limited switching behavior featured by a subthreshold swing of ≈60 mV dec-1 and negligible hysteresis. These ideal FET characteristics are attributed to the formation of a Fermi-level (EF) pinning-free gate stack at the Schottky-Mott limit. Furthermore, authors experimentally and theoretically confirm that EF depinning can be achieved by suppressing both metal-induced and disorder-induced gap states at the interface between the monolithic-oxide-gapped metal gate and the MoS2 channel. This work paves a new route for designing high-performance and energy-efficient 2D electronics.
RESUMEN
Two-dimensional (2D) materials and their heterostructures are promising for next-generation optoelectronics, spintronics, valleytronics, and electronics. Despite recent progress in various growth studies of 2D materials, mechanical exfoliation of flakes is still the most common method to obtain high-quality 2D materials because precisely controlling material growth and synthesizing a single domain during the growth process of 2D materials, for the desired shape and quality, is challenging. Here, we report the nucleation and growth behaviors of monolayer MoS2 by sulfurizing a faceted monoclinic MoO2 crystal. The MoS2 layers nucleated at the thickness steps of the MoO2 crystal and grew epitaxially with crystalline correlation to the MoO2 surface. The epitaxially grown MoS2 layer expands outwardly on the SiO2 substrate, resulting in a monolayer single-crystal film, despite multiple nucleations of MoS2 layers on the MoO2 surface owing to several thickness steps. Although the photoluminescence of MoS2 is quenched owing to efficient charge transfer between MoS2 and metallic MoO2, the MoS2 stretched out to the SiO2 substrate shows a high carrier mobility of (15 cm2 V-1 s-1), indicating that a high-quality monolayer MoS2 film can be grown using the MoO2 crystal as a seed and precursor. Our work shows a method to grow high-quality MoS2 using a faceted MoO2 crystal and provides a deeper understanding of the nucleation and growth of 2D materials on a step-like surface.