RESUMEN
OBJECTIVE: The current study aimed to evaluate the effects of different combinations of chemical and mechanical challenges on the failure load, failure mode and composition of the resulting fracture surfaces of resin-composite restorations. METHODS: Three resin composites were used to fill dentin disks (2 mm inner diameter, 5 mm outer diameter, and 2 mm thick) made from bovine incisor roots. The model restorations, half of which were preconditioned with a low-pH buffer (48 h under pH 4.5), were subjected to diametral compression with either a monotonically increasing load (fast fracture) or a cyclic load with a continuously increasing amplitude (accelerated fatigue). The load or number of cycles to failure was noted. SEM was performed on the fracture surfaces to determine the proportions of dentin, adhesive, and resin composite. RESULTS: Both cyclic fatigue and acid preconditioning significantly reduced the failure load and increased the proportion of interfacial failure in almost all the cases, with cyclic fatigue having a more pronounced effect. Cyclic fatigue also increased the amount of adhesive/hybrid layer present on the fracture surfaces, but the effect of acid preconditioning on the composition of the fracture surfaces varied among the resin composites. SIGNIFICANCE: The adhesive or hybrid layer was found to be the least resistant against the chemomechanical challenges among the components forming the model restoration. Increasing such resistance of the tooth-restoration interface, or its ability to combat the bacterial actions that lead to secondary caries following interfacial debonding, can enhance the longevity of resin-composite restorations.
RESUMEN
Methods: 12 impressions were made of a resin maxillary model (second premolar and second molar) with two prepared abutment teeth using vinyl polysiloxane (VPS); the margin of the second premolar was 0.5 mm subgingivally; and the margin of the second molar tooth was at the level of the gingiva. Impressions were made using two techniques: one-step and two-step putty/light materials. A three-unit metal framework was fabricated on the master model using the computer-aided design/computer-aided manufacturing (CAD/CAM) technique. The vertical marginal misfit was evaluated in the buccal, lingual, and mesial and distal surfaces of the abutments on the gypsum casts using a light microscope. Data were analyzed using the independent t-test (α < 0.05). Results: The results showed significantly lower vertical marginal misfit in all six areas evaluated around the two abutments in the two-step impression technique compared with the corresponding values in the one-step technique. Conclusion: Vertical marginal misfit in the two-step technique with a preliminary putty impression was significantly lower than in the one-step putty/light-body technique.
RESUMEN
Background: Non-Syndromic Cleft Lip with or without cleft Palate (NSCL/P) is a common developmental disorder of the head and neck with a multifactorial etiology. The current study aimed to evaluate the potential association of PTCH1 (rs10512248) and RAD54B (rs12681366) polymorphisms with NSCL/P in the Northeast Iranian population. Methods: In the present study, blood samples were taken from 122 subjects with NSCL/P and 161 healthy controls. Polymerase Chain Reaction (PCR) followed by Restriction Fragment Length Polymorphism (RFLP) were used to conduct genotyping of single-nucleotide polymorphisms. Results: Although differences were observed between cases and controls in rs10512248 and rs12681366, our data did not support a significant association of these polymorphisms with NSCL/P in our population. Conclusion: Our findings suggest that polymorphisms of rs10512248 and rs12681366 may not be potential risk factors for NSCL/P in the Northeast Iranian population due to the multifactorial and multiethnicity characteristics of some genes.
RESUMEN
Background: The aim of the current study was to evaluate and compare the influence of Dycal, Lime-Lite, TheraCal LC, Biodentine, resin-modified glass ionomer cement (RMGIC), and Activa BioActive as the pulp capping material on the shear bond strength of resin composite to dentin. Methods: A total of 70 extracted caries-free molars were randomly assigned to seven groups. Six test groups were covered with various protective liners: Dycal, TheraCal LC, Lime-Lite, Activa BioActive, Biodentine, and RMGIC. The control group received no liner pretreatment. Each sample was bonded to resin composite using the total-etch Tetric N bond adhesive. The samples were then tested for shear bond strength using the universal testing machine at a cross-head speed of 1 mm/min until bond failure occurred. The data were analyzed using the one-way ANOVA test followed by the Tamhane post hoc test for pairwise comparisons of the groups. Results: Independent of the type of the applied liner, all groups exhibited inferior SBS to dentin compared to the control group. TheraCal and RMGIC showed significantly higher shear bond strength than Biodentine and Dycal, which showed the lowest shear bond strength. Lime-Lite and Activa also had significantly lower SBS results than TheraCal. The mode of fracture was predominantly cohesive in Dycal, Biodentine, and TheraCal and adhesive in Activa. Conclusion: This present study concludes that the bond strength of resin composite to dentin can be affected differently using various types of liners.