Biobased Polymers via Radical Homopolymerization and Copolymerization of a Series of Terpenoid-Derived Conjugated Dienes with exo-Methylene and 6-Membered Ring.

A series of exo-methylene 6-membered ring conjugated dienes, which are directly or indirectly obtained from terpenoids, such as ß-phellandrene, carvone, piperitone, and verbenone, were radically polymerized. Although their radical homopolymerizations were very slow, radical copolymerizations proceeded well with various common vinyl monomers, such as methyl acrylate (MA), acrylonitrile (AN), methyl methacrylate (MMA), and styrene (St), resulting in copolymers with comparable incorporation ratios of bio-based cyclic conjugated monomer units ranging from 40 to 60 mol% at a 1:1 feed ratio. The monomer reactivity ratios when using AN as a comonomer were close to 0, whereas those with St were approximately 0.5 to 1, indicating that these diene monomers can be considered electron-rich monomers. Reversible addition fragmentation chain-transfer (RAFT) copolymerizations with MA, AN, MMA, and St were all successful when using S-cumyl-S'-butyl trithiocarbonate (CBTC) as the RAFT agent resulting in copolymers with controlled molecular weights. The copolymers obtained with AN, MMA, or St showed glass transition temperatures (Tg) similar to those of common vinyl polymers (Tg ~ 100 °C), indicating that biobased cyclic structures were successfully incorporated into commodity polymers without losing good thermal properties.

Biobased Cycloolefin Polymers: Carvone-Derived Cyclic Conjugated Diene with Reactive exo-Methylene Group for Regioselective and Stereospecific Living Cationic Polymerization.

Carvone, a naturally abundant chiral cyclic α,ß-unsaturated carbonyl compound, was chemically transformed into cyclic exo-methylene conjugated dienes. The exo-methylene group had high reactivity in cationic polymerization and was efficiently polymerized in a controlled manner via regioselective 1,4-conjugated additions using initiating systems effective for living cationic polymerization of vinyl ethers. The obtained polymers with 1,3-cyclohexenyl units and tetra-substituted olefins in the main chain showed high glass transition temperatures over 110 °C. The chiral monomer underwent stereospecific polymerization to result in polymers with low solubility and weak packing of the rigid main chain in the lamellar layers. The racemic mixture resulted in soluble amorphous polymers, which were subsequently hydrogenated into cycloolefin polymers with enhanced thermal properties.