RESUMEN
A poly(3-dodecylthiophene-2,5-diyl) film having in-plane anisotropic molecular arrangement was successfully fabricated by transferring its Langmuir-Blodgett film onto a step-bunched Si(111) substrate. Polarized near-edge X-ray absorption fine structure measurements revealed that the polythiophene main chains are preferentially orientated along periodic facet/terrace nanostructures on the step-bunched substrate, whereas less anisotropy was found on a flat substrate. The step-bunched Si substrate has been proved to be effective for controlling the in-plane molecular arrangement in the polymer thin film.
RESUMEN
Alternating facet/terrace nanostructures were fabricated on a SiO2 surface by step-bunching and thermal oxidation of a vicinal Si(111) substrate, and their influence upon the polymerization direction of a long-chain diacetylene derivative monolayer film was investigated by angle-dependent polarized near-edge X-ray absorption fine structure (NEXAFS) spectroscopy. It was found that the peak intensity of the C 1s-pi transition was stronger when the electric vector plane of the incident X-ray was parallel to the direction of the periodic facet/terrace structures rather than perpendicular to them. On the contrary, a polymer film fabricated on a flat SiO2 surface showed no in-plane anisotropy of the peak intensity. These results indicate that the diacetylene groups in the diacetylene derivative monolayer are preferentially photopolymerized in the direction not across but along the periodic one-dimensional structures on the step-bunched and thermally oxidized SiO2/Si(111) surface.