In this study, the effect of ultrasound (US) on the quartz-amine flotation system was investigated in detail by considering various surface chemistry techniques. The effect of ultrasound on particle size, shape factor, and surface roughness were characterized by using Brunauer-Emmett-Teller (BET) surface area measurements and scanning electron microscopy (SEM) analyses. The contact angle and bubble-particle attachment time, as well as adsorption density measurements was carried out to evaluate the effect of ultrasound on quartz surface wetting ability. In addition, atomic force microscopy (AFM) analyses were conducted, and finally micro-flotation studies were performed. As a result, it was found that the micro-flotation recovery at 2â¯×â¯10-5â¯M dodecyl amine hydrochloride (DAH) concentration increased from 45.45% to 63.64% with 30â¯W ultrasonic application at conditioning step. However, the micro-flotation recovery decreased to 37.50% when the ultrasonic power increased to 150â¯W. The results showed some effect of ultrasound on particle size, particle shape, and surface roughness in some extent. The increase in the contact angle and the decrease in the bubble-particle attachment time were observed. A slightly high adsorption density was measured. All these show a positive effect of ultrasound on quartz flotation with amine as a collector.
RESUMEN
In this work, the impact of water type on borate ore flotation was investigated, while various physical parameters during flotation were considered in order to compare the results. Two different colemanite samples from Emet deposits of Turkey, named as Emet-A and Emet-B contained 44% B(2)O(3) and 40% B(2)O(3), respectively. The flotation tests were performed at feed particle size range of -210 +20 microm. Optimal consumption values for the reagents were determined as 2000 gt(-1) for AeroPromoter R825 from Cytec Company, a sulphonate type collector, 1500 gt(-1) for Procol CA927 from Allied Colloids Company, a sulphosuccinamate type collector and 100 gt(-1) for AeroFrother 70 from Cytec Company, an alcohol-type frother. In the tests, the impeller speed of the Denver-type flotation machine was set to 1200 rpm and the samples were fed into a litre cell at 25% solid/liquid ratio and at natural pH value of the slurry at room temperature. The flotation results obtained from the tests with use of tap water, demineralised water and the artificial water prepared with Ca(2+) and Mg(2+) cations deliberately added into demineralised water were compared to each other in optimal flotation conditions.