RESUMEN
Inverted organic cells are promising devices for sustainable and low-cost future electric generation. In this work, we present the degradation mechanisms studied in ITO/TiO2/PTB7:PC70BM/V2O5/Ag inverted organic solar cells (iOSCs) by impedance spectroscopy (IS). Measurements were performed on encapsulated (controlled environment) and nonencapsulated (ambient condition) cells following their temporal evolution under AM1.5 illumination for several voltage biases. From the impedance spectra, analyzed in terms of resistive/capacitive equivalent circuits, we were able to identify that the most sensitive layers inside of the device are contact layers. According with presented, IS technique is useful for determining the materials that have more influence on the degradation of organic solar cells. We demonstrate that IS is a powerful technique to identify the limiting mechanisms and to establish the limiting materials inside of the iOSCs.
RESUMEN
This work presents a novel technique to deposit ZnO thin films through a metal vacuum evaporation technique using colloidal nanoparticles (average size of 30 nm), which were synthesized by our research group, as source. These thin films had a thickness between 45 and 123 nm as measured by profilometry. XRD patterns of the deposited thin films were obtained. According to the HRSEM micrographs worm-shaped nanostructures are observed in samples annealed at 600 °C and this characteristic disappears as the annealing temperature increases. The films obtained were annealed from 25 to 1000 °C, showing a gradual increase in transmittance spectra up to 85%. The optical band gaps obtained for these films are about 3.22 eV. The PL measurement shows an emission in the red and in the violet region and there is a correlation with the annealing process.