RESUMEN
Facile, one-step dispersion polymerization of heptafluoro-n-butyl methacrylate is shown to provide microparticles that can be made transparent in the bio-friendly medium of water/sucrose with a refractive index of 1.3770. Fluorescently labeled particles can be imaged 80 µm deep into the dispersion with 1 vol% concentration, using confocal fluorescence microscopy. Such particles can provide insights into (bio-)physical processes in aqueous environments.
RESUMEN
In this work we prepare Langmuir-Blodgett monolayers with a trifunctional amphiphilic anthraphane monomer. Upon spreading at the air/water interface, the monomers self-assemble into 1 nm-thin monolayer islands, which are highly fluorescent and can be visualized by the naked eye upon excitation. In situ fluorescence spectroscopy indicates that in the monolayers, all the anthracene units of the monomers are stacked face-to-face forming excimer pairs, whereas at the edges of the monolayers, free anthracenes are present acting as edge groups. Irradiation of the monolayer triggers [4 + 4]-cycloadditions among the excimer pairs, effectively resulting in a two-dimensional (2D) polymerization. The polymerization reaction also completely quenches the fluorescence, allowing to draw patterns on the monomer monolayers. More interestingly, after transferring the monomer monolayer on a solid substrate, by employing masks or the laser of a confocal scanning microscope, it is possible to arbitrarily select the parts of the monolayer that one wants to polymerize. The unpolymerized regions can then be washed away from the substrate, leaving 2D macromolecular monolayer objects of the desired shape. This photolithographic process employs 2D polymerizations and affords 1 nm-thin coatings.
RESUMEN
A Langmuir-Blodgett film consisting of a dense array of trifunctional monomers bearing three 1,8-diazaanthracene units is polymerized at an air/water interface or after transfer on solid substrates. The transfer does not affect the excimer fluorescence of the film, indicating that the monomers' packing with their diazaanthracene units stacked face-to-face is retained-a prerequisite for successful polymerization. The monomer film can be polymerized in confined areas on solid substrates by UV irradiation with a confocal microscope laser. The underlying chemistry of the polymerization, a [4+4]-cycloaddition of the diazaanthracene units, leads to disappearance of the fluorescence in the irradiated regions which enables writing into the monolayer on a µm scale-thus the term "molecular paper." The reaction can be reversed by heating which leads to a recovery of the fluorescence and to erasing of the writing. Alternative pathways for this phenomenon are discussed and control experiments are conducted to rule them out.
RESUMEN
Scaling behavior of one-dimensional (1D) and two-dimensional (2D) polymers in dilute solution is discussed with the goal of stimulating experimental work by chemists, physicists, and material scientists in the emerging field of 2D polymers. The arguments are based on renormalization-group theory, which is explained for a general audience. Many ideas and methods successfully applied to 1D polymers are found not to work if one goes to 2D polymers. The role of the various states exhibiting universal behavior is turned upside down. It is expected that solubility will be a serious challenge for 2D polymers. Therefore, given the crucial importance of solutions in characterization and processing, synthetic concepts are proposed that allow the local bending rigidity and the molar mass to be tuned and the long-range interactions to be engineered, all with the goal of preventing the polymer from falling into flat or compact states.
Asunto(s)
Polímeros/química , Polímeros/síntesis química , SolucionesRESUMEN
Creation of polymers comprised of repeat units that can create topologically planar macromolecules (rather than linear) has been the topic of several recent studies in the field of synthetic polymer chemistry. Such novel macromolecules, known as 2D polymers, are the result of advanced synthetic methodology which allows creation of monolayer sheets with a periodic internal structure and functional groups placed at predetermined sites under mild conditions. Given the promising potentials of 2D polymers, this feature paper aims at discussing the concept of these novel macromolecules from a topological viewpoint in Section 1. This is followed by spotlighting the expected behavior of 2D polymers in the context of polymer physics (entropy elasticity, strength, percolation, and persistence) and polymer chemistry (copolymers and growth kinetics) in Section 2. Section 3 delineates synthetic and analytical matters associated with 2D polymers followed by a brief final section highlighting the potential of these sheet-like macromolecules for application purposes. We hope this article will trigger the interest of chemists, physicists and engineers to help develop this encouraging new class of materials further such that societally relevant applications will be accessible in the market soon.
RESUMEN
Synthetic covalent monolayer sheets and their subclass, two-dimensional polymers are of particular interest in materials science because of their special dimensionality which renders them very different from any bulk matter. However, structural analysis of such entities is rather challenging, and there is a clear need for additional analytical methods. The present study shows how tip-enhanced Raman spectroscopy (TERS) can be performed on monomer monolayers and the covalent sheets prepared from them by [4 + 4]-cycloaddition to explore rather complex structural and mechanistic issues. TERS is a surface analytical method that combines the high lateral resolution of scanning probe microscopy (SPM) with a greatly enhanced Raman scattering intensity. The high spatial resolution (<60 nm) and the significantly improved sensitivity (contrast factor of >4000) compared to confocal Raman microscopy provides new insights into the formation of this new and exciting material, namely significant consumption of the reactive units (anthracenes) and exclusion of the alternative [4 + 2]-cycloaddition. Moreover, due to the high lateral resolution, it was possible to find a first spectroscopic hint for step growth as the dominant mechanism in the formation of these novel monolayer sheets. In addition, TERS was used to get first insights into the phase behavior of a comonomer mixture.
RESUMEN
We present the synthesis of a two-dimensional polymer at the air/water interface and its nm-resolution imaging. Trigonal star, amphiphilic monomers bearing three anthraceno groups on a central triptycene core are confined at the air/water interface. Compression followed by photopolymerization on the interface provides the two-dimensional polymer. Analysis by scanning tunneling microscopy suggests that the polymer is periodic with ultrahigh pore density.
RESUMEN
Alignment of nanowires over a large area of flat and patterned substrates is a prerequisite to use their collective properties in devices such as gas sensors. In this work, uniform single-crystalline ultrathin W18 O49 nanowires with diameters less than 2â nm and aspect ratios larger than 100 have been synthesized, and, despite their flexibility, assembled into thin films with high orientational order over a macroscopic area by the Langmuir-Blodgett technique. Alignment of the tungsten oxide nanowires was also possible on top of sensor substrates equipped with electrodes. Such sensor devices were found to exhibit outstanding sensitivity to H2 at room temperature.
RESUMEN
By using structurally similar amphiphilic monomers, it is shown that compressed monolayers of varying amounts of such monomers at the air/water interface can be converted by photo-irradiation into the corresponding covalently connected monolayer sheets. Since one of the monomers carries three anthracene units and the other three 1,8-diaza-anthracene units, the growth reaction is proposed to take place through photochemically achieved [4+4]-cycloaddition between pairs of these units that are co-facially (face-to-face) arranged, to furnish the corresponding covalent dimers. While evidence for both homodimers is amply available, the existence of the heterodimer needs to be established with the help of a model reaction to support the conceptual aspect of this work, copolymerization in two dimensions. The sheet copolymers exhibit substantial robustness in that they can be spanned over 20 × 20 µm(2)-sized holes without rupturing under their own weight. X-ray photoelectron spectroscopy (XPS) studies reveal that the monomers are incorporated into the sheet copolymers according to feed. These results establish existence of the first covalent sheet copolymer, which is considered a step ahead towards novel 2D materials.
Asunto(s)
Antracenos/química , Compuestos Aza/química , Procesos Fotoquímicos , Polímeros/química , Ciclización/efectos de la radiación , Dimerización , Microscopía Electrónica de Rastreo , Estructura Molecular , Espectroscopía de Fotoelectrones , Propiedades de Superficie/efectos de la radiación , TermodinámicaRESUMEN
The rise of graphene, a natural two-dimensional polymer (2DP) with topologically planar repeat units, has challenged synthetic chemistry, and has highlighted that accessing equivalent covalently bonded sheet-like macromolecules has, until recently, not been achieved. Here we show that non-centrosymmetric, enantiomorphic single crystals of a simple-to-make monomer can be photochemically converted into chiral 2DP crystals and cleanly reversed back to the monomer. X-ray diffraction established unequivocal structural proof for this synthetic 2DP, which has an all-carbon scaffold and can be synthesized on the gram scale. The monomer crystals are highly robust, can be easily grown to sizes greater than 1â mm and the resulting 2DP crystals exfoliated into nanometre-thin sheets. This unique combination of features suggests that these 2DPs could find use in membranes and nonlinear optics.
RESUMEN
Covalent monolayer sheets in 2 hours: spreading of threefold anthracene-equipped shape-persistent and amphiphilic monomers at the air/water interface followed by a short photochemical treatment provides access to infinitely sized, strictly monolayered, covalent sheets with in-plane elastic modulus in the range of 19 N/m.
RESUMEN
The formation of polydopamine under mild oxidation conditions from dopamine solutions with mechanical agitation leads to the formation of films that can functionalize all kinds of materials. In the absence of stirring of the solution, we report the formation of polydopamine films at the air/water interface (PDA A/W) and suggest that it arises from an homogeneous nucleation process. These films grow two times faster than in solution and can be deposited on hydrophilic or hydrophobic substrates by the Langmuir-Schaeffer technique. Thanks to this new method, porous and hydrophobic materials like polytetrafluoroethylene (PTFE) membranes can be completely covered with a 35 nm thick PDA A/W film after only 3h of reaction. Finally the oxidation of a monomer followed by a polymerization in water is not exclusive to polydopamine since we also transferred polyaniline functional films from the air/water interface to solid substrates. These findings suggest that self-assembly from a solution containing hydrophilic monomers undergoing a chemical transformation (here oxidation and oligomerization) could be a general method to produce films at the liquid/air interface.
RESUMEN
The shape-persistent monomer 3 with its three 1,8-diazaanthracene (DAA) units is spread and compressed at the air/water interface and the layer then converted into a 1.5 nm thick covalent monolayer sheet by photoirradiation under ambient conditions. The sheet obtained under these extremely mild conditions is mechanically stable to carry its own weight when spanned over TEM grids. While its molecular structure cannot be given yet with certainty, it is likely to be the result of [4 + 4]-cycloaddition dimerizations between the DAA units of neighboring monomers. Evidence is based on the wavelength of the monomer fluorescence emission, the kinetics of this emission's intensity decay with irradiation time, and the mechanical sheet stability that suggests a surpassing of percolation threshold. Finally, the thermal stability of the sheet is investigated.
RESUMEN
Oligofunctional terpyridine-based monomers are spread at an air/water interface, where they are connected with transition metal salts such as Fe(II) into mechanically coherent monolayer sheets of macroscopic dimension. The conversions of these processes are determined by XPS for several monomer/metal ion combinations. The sheets are transferred onto TEM grids, the 20 × 20 square micrometer sized holes of which can be spanned. AFM indentation experiments provide in-plane elastic moduli which are compared with naturally occurring sheets such as graphene. The new organometallic sheets are also used to create multilayer assemblies on square centimeter length scales on solid substrates. Finally some directions are provided where this research can lead to in future and where its application potential lies.
Asunto(s)
Compuestos Ferrosos/química , Piridinas/química , Modelos Moleculares , Estructura Molecular , Tamaño de la Partícula , Propiedades de SuperficieRESUMEN
A two-dimensional polymer (2DP) based on the dimerization of anthraceno groups arranged in a triptycene motif is reported. A photoinduced polymerization is performed in the crystalline state and gives a lamellar 2DP via a crystal-to-crystal (but not single-crystal to single-crystal) transformation. Solvent-induced exfoliation provides monolayer sheets of the 2DP. The 2DP is considered to be a tiling, a mathematical approach that facilitates structural elucidation.
RESUMEN
We describe the challenges involved with extending the limited lateral size of two-dimensional polymers (2DPs). An amphiphilic monomer with three-fold symmetry is chosen to form an ideally tessellated monolayer at the air/water interface. Anthracene [4+4] photo-dimerization is chosen as the growth reaction. Formation of covalent net-points upon anthracene dimerization has an influence on the mechanical coherence of the resulting sheets which could be investigated qualitatively and quantitatively by means of AFM nano-indentation.