RESUMEN
Pulsed electrodeposition prepared porous alumina templates with Ni nanowires pore filling ranged from 1 to 100%, depending on the alumina barrier-layer thickness, were probed by continuous wave ferromagnetic resonance at room temperature. For completely filled samples, a single resonance peak was observed in the whole range of angles between the applied magnetic field and normal to the sample plane. Its position was described by Kittel formula that takes into account shape anisotropy of individual Ni wires and dipolar interactions between them. For the samples with lower pore filling the effective anisotropy field decreased and the resonance linewidth in the perpendicular configuration increased. Also a quite intense second peak was observed at lower fields for these samples. These changes are associated with reduction of pore filling percentage that can lead to decrease of dipolar interactions between nanowires and to appearance of magnetic inhomogeneities inside wires.
RESUMEN
We report magnetic, dynamic and transport properties of discontinuous metal-insulator multilayers Fe/MgO grown on amorphous Corning glass and single-crystalline MgO (001) substrates. The films of structure Substrate/MgO (3 nm)/[Fe (0.6 nm)/MgO (3.0 nm)] x 10 were prepared in ultra-high vacuum conditions using Pulsed Laser Deposition. It was shown that conditions of epitaxial growth are favorable for MgO substrates. As a result a substantial increase of tunneling magnetoresistance caused by spin-filtering effect was observed and reasonably theoretically explained. The value of TMR - 9.2% at room temperature in 18 kOe magnetic field is three times higher comparing to that for the samples grown on Corning glass substrates.
RESUMEN
X-band ferromagnetic resonance (FMR) was used to characterize in-plane magnetic anisotropies in rectangular and square arrays of circular nickel and Permalloy microdots. In the case of a rectangular lattice, as interdot distances in one direction decrease, the in-plane uniaxial anisotropy field increases, in good agreement with a simple theory of magnetostatically interacting uniformly magnetized dots. In the case of a square lattice a four-fold anisotropy of the in-plane FMR field H(r) was found when the interdot distance a gets comparable to the dot diameter D. This anisotropy, not expected in the case of uniformly magnetized dots, was explained by a non-uniform magnetization m(r) in a dot in response to dipolar forces in the patterned magnetic structure. It is well described by an iterative solution of a continuous variation procedure. In the case of perpendicular magnetization multiple sharp resonance peaks were observed below the main FMR peak in all the samples, and the relative positions of these peaks were independent of the interdot separations. Quantitative description of the observed multiresonance FMR spectra was given using the dipole-exchange spin wave dispersion equation for a perpendicularly magnetized film where in-plane wave vector is quantized due to the finite dot radius, and the inhomogenetiy of the intradot static demagnetization field in the nonellipsoidal dot is taken into account. It was demonstrated that ferromagnetic resonance force microscopy (FMRFM) can be used to determine both local and global properties of patterned submicron ferromagnetic samples. Local spectroscopy together with the possibility to vary the tip-sample spacing enables the separation of those two contributions to a FMRFM spectrum. The global FMR properties of circular submicron dots determined using magnetic resonance force microscopy are in a good agreement with results obtained using conventional FMR and with theoretical descriptions.
RESUMEN
We present an exact solution of a one-dimensional Ising chain with both nearest-neighbor and random long-range interactions. Not surprisingly, the solution confirms the mean-field character of the transition. This solution also predicts the finite-size scaling that we observe in numerical simulations.