Antibacterial Effect of Ozone on Cariogenic Bacteria and Its Potential Prejudicial Effect on Dentin Bond Strength-An In Vitro Study.

Ozone is increasingly utilized in dental caries treatment due to its antibacterial properties. In a context of limited studies and no consensus on protocols, this research aims to assess ozone's antibacterial efficacy on cariogenic bacteria and its potential adverse impact on dentin bond strength. Streptococcus mutans, Streptococcus sobrinus, Lactobacillus casei, and Actinomyces naeslundii suspensions were exposed to 40 µg/mL of ozone gas and 60 µg/mL of ozonated water (80 s) via a medical ozone generator. Negative and positive control groups (chlorhexidine 2%) were included, and UFC/mL counts were recorded. To examine microtensile bond strength (µTBS), 20 human molars were divided into four groups, and class I cavities were created. After ozone application, samples were restored using an etch-and-rinse and resin composite, then sectioned for testing. The SPSS v. 28 program was used with a significance level of 5%. The µTBS results were evaluated using one-way ANOVA, Tukey HSD, and Games-Howell. Bacterial counts reduced from 106 to 101, but dentin µTBS was significantly impacted by ozone (ANOVA, p < 0.001). Despite ozone's attractive antibacterial activity, this study emphasizes its detrimental effect on dentin adhesion, cautioning against its use before restorative treatments.

Impact of Shelf-Life Simulation on a Self-Adhesive Composite: Polymerization Kinetics, Chemical and Color Stability.

PURPOSE: To determine the polymerization kinetics and color stability of a self-adhesive and conventional resin composite after accelerated shelf-life simulation. MATERIALS AND METHODS: Two composites were tested - universal Filtek Z250 (3M Oral Care) and self-adhesive Constic (DMG). They were stored for 2 months in an incubator to simulate an Arrhenius aging model (60°C) and tested at 5 different time points. Polymerization kinetics (n = 3) were studied using an attenuated total reflectance technique (ATR), through continuous FTIR spectral acquisition (20 min). Spectra were obtained before, during and after 20 s of light curing. With the spectral data, qualitative analysis was performed yielding chemical stability, and quantitative data including extrapolated degree of conversion (DCmax) and polymerization rate (Rpmax) were assessed. To evaluate color stability (n = 3), a spectrophotometer was used to record CIELAB color parameters. Inferential statistics, including repeated measures two-way ANOVA were carried out at a significance level of 5%. RESULTS: The composites did not appear to undergo significant chemical changes after 2 months of accelerated aging. There was a significant impact of aging on the mean DCmax (p < 0.001). Similarly, a reduction in Rpmax, measured for both composites, was also noted (ANOVA; Z = 203.7; p < 0.001). The two-way ANOVA confirmed that the composite had no influence on the color stability (F = 0.94; p = 0.34), while aging did (p = 0.013). CONCLUSION: Minimal changes in absorbance levels were noted for both composites, without overly affecting their chemical composition. The presence of an acidic monomer did not seem to potentiate the degradation of the self-adhesive composite. This composite even showed greater color stability after aging.

Spectrophotometric Analysis of Coronal Discoloration In Vitro Induced by Bioceramic Cements.

The aim of this study was to evaluate and quantify, in vitro, the extent of coronal discoloration induced by bioceramic materials over time. In total, 44 human monoradicular teeth were divided into four groups (n = 11), according to the applied material: Negative control (NC); White MTA ProRoot® (WMTAP); Biodentine™ (BD); and TotalFill® BC RRM™ Putty (TF). Teeth were immersed in saline solution and incubated at 37 °C; the following periods of time were defined: before incubation: [t0]-without bioceramic material, t1-immediately after the bioceramic material placement; after incubation: t24h-24 h, t7d-7 days, and 30d-30 days. Descriptive and inferential statistical analysis were performed. Cochran's Q test was used to evaluate coronal discoloration across the different groups, while the Kruskal-Wallis test was employed to determine differences in discoloration among the groups at each time interval. Additionally, the Friedman test was applied to analyze the variations in discoloration within each group over time. A significance level of 5% was set. All experimental groups revealed coronal discoloration over time: NC (p = 0.001), WMTAP (p < 0.001), BD (p = 0.001), and TF (p = 0.006). No significant differences were observed between groups for each time interval (p > 0.05). The WMTAP group varied the most considering the intervals [t0-t1] and [t24h-t7d] (p = 0.037) compared to the remaining experimental groups.

Comparative Assessment of Different Pre-Treatment Bonding Strategies to Improve the Adhesion of Self-Adhesive Composites to Dentin.

The aim of this study is to compare the adhesive interface formed in dentin, using self-adhesive composites applied with different bonding strategies, by testing the microtensile bond strength (µTBS) and ultramorphology through the use of light microscopy. Permanent, sound human molars were randomly allocated to six experimental groups. The groups included a negative control group, where only etching was performed via EtchOnly; a positive control group where an adhesive was applied, OptiBondFL (OBFL); and an experimental group where a primer was applied using a co-curing strategy together with a composite (Primer_CoCuring). The samples were sectioned into microspecimens for µTBS (n = 8) and into 1-mm thick slabs for light microscopy using Masson's trichrome staining protocol (n = 3). The statistical analysis included a two-way ANOVA for µTBS data and Tukey's HSD was used as a post-hoc test (significance level of 5%; SPSS v. 26.0). The results of the µTBS revealed that the self-adhesive composite (F = 6.0, p < 0.018) and the bonding strategy (F = 444.1, p < 0.001) significantly affected the bond strength to dentin. However, their interactions were not significant (F = 1.2, p = 0.29). Etching dentin with no additional treatment revealed the lowest µTBS (VF_EtchOnly = 2.4 ± 0.8 MPa; CC_EtchOnly = 2.0 ± 0.4 MPa), which was significantly different from using a primer (VF_CoCu = 8.8 ± 0.8 MPa; CC_CoCu = 6.3 ± 1.0 MPa) or using the full adhesive (VF_OptiBondFL = 22.4 ± 0.3 MPa; CC_OptibondFL = 21.2 ± 0.4 MPa). Microscopy images revealed that the experimental Primer_CoCuring was the only group with no collagen fibers exposed to the dentin−composite interface. Overall, the use of a primer, within the limitations of this study, increased the bonding of the self-adhesive composite and provided sufficient infiltration of the collagen based on light-microscopic imaging.

Collagen-depletion strategies in dentin as alternatives to the hybrid layer concept and their effect on bond strength: a systematic review.

Strategies aiming to improve the longevity of resin-dentin adhesive interface developed so far have only been able to retard the problem. Different approaches are thus needed. The objective of this review was to determine whether the use of collagen-depletion strategies after acid-etching procedures may improve the bond strength of resin-based materials to dentin. A systematic review was planned following 2021 PRISMA statement guidelines, with a search strategy performed in five electronic databases: PubMed/Medline, Scopus, EMBASE, SciELO and IADR Abstract Archive (last search: 17/01/2022). Inclusion criteria encompassed studies which evaluated a collagen-depletion strategy in acid-etched human dentin and tensile/shear bond strength tests. Risk of bias assessment was carried out by two reviewers, working independently on an adapted five-domain risk of bias (RoB) checklist for laboratory studies. Results were synthesized qualitatively, as a meta-analysis was not possible due to limited number of studies and their RoB. A total of eight studies were eligible for inclusion in the systematic review after inclusion/exclusion criteria application. Out of these, two evaluated the effect of using NaOCl followed by an antioxidant, and the remaining six evaluated different enzymatic treatments (bromelain, chondroitinase ABC, papain, and trypsin). None of the studies reported a decrease of bond strength when a collagen-depletion strategy was used, in comparison to traditional hybrid layers (control). All enzymatic treatment studies which respected the inclusion criteria improved the bond strength to dentin. Some specific collagen-depletion strategies seem to play a favorable role in improving immediate bond strengths to dentin. Further research with sound methodology is required to consolidate these findings, since limitations in RoB and a low number of studies were found. The assessment of further proteolytic agents and long-term outcomes is also required.

Improving Properties of an Experimental Universal Adhesive by Adding a Multifunctional Dendrimer (G-IEMA): Bond Strength and Nanoleakage Evaluation.

A vast number of adhesive formulations exist currently. However, available adhesives still have several drawbacks such as increased hydrophilicity, polymerization deficiency, potential cytotoxicity and limited monomer interdiffusion within dentin. To improve material properties, a Bisphenol A-free adhesive containing a novel dendrimer G(2)-isocyanatoethyl methacrylate (G-IEMA) in replacement of Bis-GMA was made and tested. Sound human molars were sectioned to expose mid-coronal dentin, which was bonded using four adhesives­Futurabond, Scotchbond Universal and experimentals EM1 and EM2. The experimental adhesive EM2 contained G-IEMA, while EM1 had Bis-GMA. Groups were further allocated to two different adhesive strategies: etch-and-rinse (20 s etching) or self-etch. Immediate (24 h) microtensile bond strength to dentin (n = 5) was tested using a universal testing machine (1 mm/min, 5 kN; Shimadzu AGS-X Autograph, Tokyo, Japan), while the ultrastructure of the interface (n = 2) was assessed using scanning electron microscopy-energy dispersive spectroscopy (SEM-EDS). Nanoleakage expression was evaluated using silver nitrate penetration and posterior SEM-EDS analysis (n = 3). Linear mixed models/Generalized models were used for inferential statistics (5% significance level). Bond strength results did not depend on the adhesive choice, although differences were found between strategies (p < 0.001). Regarding nanoleakage, when applied in an etch-and-rinse mode, experimental adhesives scored lower nanoleakage means than Futurabond and Scotchbond Universal. The novel adhesive shows interesting interfacial properties, with favorable nanoleakage results and a bond strength to dentin that matches current commercial adhesives.

Polymerizable Matrix Metalloproteinases' Inhibitors with Potential Application for Dental Restorations.

Collagen cleavage by matrix metalloproteinase (MMP) is considered a major cause of dental resins long term failure. Most MMP inhibitors display significant toxicity and are unsuitable for dental resins' applications. Here we report a study of a new class of inhibitors that display the unique property of being co-polymerizable with other vinyl compounds present in commercial dental resins, limiting their release and potential toxicity. Computational affinity towards the active site of different MMP-1; -2; -8; -9 and -13 of several compounds showed interesting properties and were synthesized. These free compounds were tested concerning their toxicity upon contact with two different cell types, with no substantial decrease in cell viability at high concentrations. Even so, compound's safety can be further improved upon copolymerization with commercial dental resins, limiting their release.

Challenges in Matrix Metalloproteinases Inhibition.

Matrix metalloproteinases are enzymes that degrade the extracellular matrix. They have different substrates but similar structural organization. Matrix metalloproteinases are involved in many physiological and pathological processes and there is a need to develop inhibitors for these enzymes in order to modulate the degradation of the extracellular matrix (ECM). There exist two classes of inhibitors: endogenous and synthetics. The development of synthetic inhibitors remains a great challenge due to the low selectivity and specificity, side effects in clinical trials, and instability. An extensive review of currently reported synthetic inhibitors and description of their properties is presented.

Dentin Bonding and SEM Analysis of a New Experimental Universal Adhesive System Containing a Dendrimer.

Due to their polymerization characteristics, hyper-branched dendrimers have lately shown to be promising candidates for use in dental materials. In this study, a new dental adhesive system was prepared, using a dendrimer derived from 2-isocyanatoethyl methacrylate (G-IEMA), and its adhesive properties were investigated. The exposed dentin was treated with four universal adhesives (UAs): SBU (Scotchbond Universal™), FUT (Futurabond M+™), AE1 (experimental adhesive with Bis-GMA) and AE2 (experimental adhesive with G-IEMA), using Etch & Rinse (ER) or Self Etch (SE) protocols. Composite build-ups were prepared and stored for 24 h at 37 °C in distilled water. Composite/dentin beams were prepared with cross-sectional areas of 1 ± 0.3 mm2 and µTBS (Micro-tensile bond strength) test was performed at 0.5 mm/min. Failures modes were evaluated by stereomicroscopy, and bonding interfaces were observed by scanning electron microscopy (SEM). Statistical analysis of µTBS data was performed using General Linear (GLM) and Linear Mixed Models (LMM). The effect of adhesive type on µTBS was significant (p = 0.010), with AE1 presenting significantly higher µTBS than SBU (p = 0.019). No other differences between adhesives were observed. ER showed significantly better results than SE (p = 0.019), and no significant interactions between the adhesives and protocols were determined. Results obtained so far pinpoint the emergence of a new paradigm in the dental materials field, as G-IEMA can be used successfully as an alternative to Bis-GMA.

Human ex vivo dentin-pulp complex preservation in a full crown model.

OBJECTIVES: Currently, there is lack of human in vitro full tooth models that hold the odontoblast layer with pulp tissue in their native environment. The appearance of new in vitro and in vivo models has provided new understanding of the potential of tissue engineering in dental pulp regeneration. However, the development of new in vitro full tooth models will allow us to get closer to in vivo conditions. Thus, the aim of this study is to preserve a living dentin-pulp complex, in a novel in vitro full crown model, after tooth extraction. METHODS: Twenty intact third molars, after preparation, were divided into four groups, with five samples each. We placed the negative control samples (C) in saline, and the tested groups were placed (T) in supplemented DMEM, at two different times: 1 and 7 days. The specimens were processed for light microscopy observation. RESULTS: Contrary to C-groups, T-groups showed a functional dentin-pulp complex. The treated dentin-pulp complex presents normal histological appearance. CONCLUSIONS: This study showed that it is possible to preserve a living dentin-pulp complex after tooth extraction during 7 days.

Multinuclear magnetic resonance studies on the chemical interaction of a self-etching adhesive with radicular and coronal human dentin.

This study presents evidence at molecular level for the chemical interaction between human dentin from different tooth regions and a monomer with phosphate groups, incorporated in the formulation of a simplified adhesive system. Because dentin was observed as a powder, previous verification was obtained for an eventual collagen denaturation due to the grinding process. The presence of chemical bonds involving coronal (CD) or radicular dentin (RD) was investigated using multinuclear magnetic resonance (MR) techniques. Narrow signals were identified in the carbon magic angle spinning (MAS) spectra of CD and RD treated with the adhesive, which were assigned to methylenic groups in methacryloyloxydecyl dihydrogen phosphate (MDP) bound to hydroxyapatite Ca2+; 1H spectra of the adhesive components and treated dentin, in ethanol, support this conclusion. (31)P MAS spectra obtained from both dentin regions present additional shielding and broadening effects subsequent to application and photopolymerization of the adhesive, which were higher for CD. Multinuclear MR studies provided evidence for the interaction of the adhesive with dentin, which involves hydroxyapatite and is stronger for CD than for RD, but no direct proof was obtained on bonding to collagen.

Dentin regional bond strength of self-etch and total-etch adhesive systems.

OBJECTIVES: To evaluate the microtensile bond strength (MTBS) of self-etch (with or without H(3)PO(4)-etching) and total-etch bonding systems bonded to different regions of dentin. METHODS: Long flat dentin cavity preparations extending from top-crown to root-apex within the same tooth were performed and bonded: using two-step (Clearfil SE Bond/SEB, Resulcin Aqua Prime/RES) and one-step (Etch & Prime 3.0/EP, One-Up Bond F/OUB, Prompt L-Pop/PLP, Solist/SOL and Futurabond/FUT) self-etch adhesives; these same adhesives were also applied following H(3)PO(4)-etching of dentin and finally two more groups were bonded with total-etch adhesives (Single Bond/SB and Prime & Bond NT/PBNT). Build-ups of resin composite were constructed incrementally to ensure sufficient bulk for the MTBS test and the different regions of dentin were identified by painting with different colours on the top of the resin composite. Specimens were sliced into beams and tested in tension. ANOVA and multiple comparisons tests were used (p<0.05). RESULTS: Regardless of the tested dentin region, SEB attained the highest MTBS to smear layer-covered surfaces (i.e., coronal dentin: 42.7MPa), while H(3)PO(4)-etching of dentin hampered bonds (i.e., coronal dentin: 27.7MPa). When bonding with PBNT, SB, RES, EP, PLP, SOL and FUT, MTBS was similar for different dentin regions. H(3)PO(4)-etching of dentin did not alter the attained MTBS. SIGNIFICANCE: SEB yielded the highest MTBS to all regions of dentin. When bonding to parallel-cut dentin, previous H(3)PO(4)-etching of dentin did not increase MTBS and differences in bond strength among dentin regions were absent.

A European perspective on fluoride use in seven countries.

OBJECTIVES: The aim of this study was to collate data on national policies for the use of fluoride in the seven European countries participating in the FLINT project. METHODS: Policies on the use of fluoride were obtained for each of the study areas. Data collected included the presence of water fluoridation and regulations governing fluoride toothpaste and fluoride supplements. RESULTS: In Ireland 74% of the population had a fluoridated water supply but in all the other countries fluoride toothpaste was the principal form of delivering fluoride, usually recommended as a dose of a pea-sized amount. Fluoride supplement use varied considerably between countries. The Netherlands had the clearest regulations covering the use of fluoride supplements and definition of at-risk individuals. Most countries, even if they recognized particular caries-risk did not define the term clearly. In Iceland all children were regarded as being at high risk of developing caries. CONCLUSION: Considerable variation exists between European countries in their policies for fluoride use and no clear definitions of high-caries-risk individuals were found. The results show that there is even a lack of coherent thought and planning within the different countries, let alone between them.