RESUMEN
The efficient operation of a metal hydride reactor depends on the hydrogen sorption and desorption reaction rate. In this regard, special attention is paid to heat management solutions when designing metal hydride hydrogen storage systems. One of the effective solutions for improving the heat and mass transfer effect in metal hydride beds is the use of heat exchangers. The design of modern cylindrical-shaped reactors makes it possible to optimize the number of heat exchange elements, design of fins and cooling tubes, filter arrangement and geometrical distribution of metal hydride bed elements. Thus, the development of a metal hydride reactor design with optimal weight and size characteristics, taking into account the efficiency of heat transfer and metal hydride bed design, is the relevant task. This paper discusses the influence of different configurations of heat exchangers and metal hydride bed for modern solid-state hydrogen storage systems. The main advantages and disadvantages of various configurations are considered in terms of heat transfer as well as weight and size characteristics. A comparative analysis of the heat exchangers, fins and other solutions efficiency has been performed, which makes it possible to summarize and facilitate the choice of the reactor configuration in the future.
RESUMEN
Radiation damage is one of the significant factors limiting the operating time of many structural materials working under extreme conditions. One of the promising directions in the development of materials that are resistant to radiation damage and have improved physical and mechanical properties is the creation of nanoscale multilayer coatings (NMCs). The paper is devoted to the experimental comprehension of changes in the defect structure and mechanical properties of nanoscale multilayer coatings (NMCs) with alternating layers of Zr and Nb under irradiation. Series of Zr/Nb NMCs with different thicknesses of individual layers were fabricated by magnetron sputtering and subjected to H+ irradiation. The evolution of structure and phase states, as well as the defect state under proton irradiation, was studied using the methods of high-resolution transmission electron microscopy (HRTEM), X-ray diffraction analysis (XRD), glow discharge optical emission spectroscopy (GDOES), and positron annihilation spectroscopy (PAS). The layer-by-layer analysis of structural defects was carried out by Doppler broadening spectroscopy (DBS) using a variable-energy positron beam. To estimate the binding energy and the energy paths for the hydrogen diffusion in Zr/Nb NMCs, calculations from the first principles were used. When the thickness of individual layers is less than 25 nm, irradiation causes destruction of the interfaces, but there is no significant increase in the defect level, the S parameter (open volume defects amount) before and after irradiation is practically unchanged. After irradiation of NMC Zr/Nb with a thickness of layers 50 and 100 nm, the initial microstructure is retained, and the S parameter is significantly reduced. The GDOES data reveal the irregular H accumulation at the interface caused by significant differences in H diffusion barriers in the bulk of Zr and Nb multilayers as well as near the interface's region.
RESUMEN
Influence of manufacturing parameters (beam current from 13 to 17 mA, speed function 98 and 85) on microstructure and hydrogen sorption behavior of electron beam melted (EBM) Ti-6Al-4V parts was investigated. Optical and scanning electron microscopies as well as X-ray diffraction were used to investigate the microstructure and phase composition of EBM Ti-6Al-4V parts. The average α lath width decreases with the increase of the speed function at the fixed beam current (17 mA). Finer microstructure was formed at the beam current 17 mA and speed function 98. The hydrogenation of EBM Ti-6Al-4V parts was performed at the temperatures 500 and 650 °Ð¡ at the constant pressure of 1 atm up to 0.3 wt %. The correlation between the microstructure and hydrogen sorption kinetics by EBM Ti-6Al-4V parts was demonstrated. Lower average hydrogen sorption rate at 500 °C was in the sample with coarser microstructure manufactured at the beam current 17 mA and speed function 85. The difference of hydrogen sorption kinetics between the manufactured samples at 650 °C was insignificant. The shape of the kinetics curves of hydrogen sorption indicates the phase transition αH + βH→βH.