RESUMEN
We report the critical current density (Jc) and vortex pinning properties in single crystals of a novel iron-based superconductor (IBS) KCa2Fe4As4F2 with large Jc in the pristine state, before and after introduction of artificial defects by swift-particle irradiation. The effects of 2.6 GeV U and 3 MeV proton irradiations in KCa2Fe4As4F2 single crystals on transition temperature Tc and Jc, including its dose dependence, are systematically studied. Jc~8 MA/cm2 under a self-field at 2 K in the pristine crystal is strongly enhanced up to 19.4 and 17.5 MA/cm2 by irradiation of 2.6 GeV U-ions and 3 MeV protons, respectively. Suppression of Tc and dose dependence of Jc in KCa2Fe4As4F2 is different from that in a representative IBS of (Ba,K)Fe2As2, which can be explained by considering the presence of embedded defects in pristine KCa2Fe4As4F2. The vortex dynamics in the pristine and proton irradiated KCa2Fe4As4F2 single crystals are also investigated from the analyses of the field dependence of Jc and the normalized magnetic relaxation rate. In addition to the contribution of embedded defects, weak collective pinning is considered for comprehensive analyses. Vortex dynamics in KCa2Fe4As4F2 is similar to those in (Ba,K)Fe2As2 to some extent, and different from that in anisotropic Li0.8Fe0.2OHFeSe. Large anisotropy, due to the presence of insulating blocking layers in KCa2Fe4As4F2, which leads to much lower irreversibility field (Hirr) compared with 122-type IBSs, strongly affect the vortex dynamics.
RESUMEN
Charge order is universal to all hole-doped cuprates. Yet, the driving interactions remain an unsolved problem. Electron-electron interaction is widely believed to be essential, whereas the role of electron-phonon interaction is unclear. We report an ultrahigh-resolution resonant inelastic x-ray scattering (RIXS) study of the in-plane bond-stretching phonon mode in stripe-ordered cuprate La1.675Eu0.2Sr0.125CuO4 Phonon softening and lifetime shortening are found around the charge ordering wave vector. In addition to these self-energy effects, the electron-phonon coupling is probed by its proportionality to the RIXS cross section. We find an enhancement of the electron-phonon coupling around the charge-stripe ordering wave vector upon cooling into the low-temperature tetragonal structure phase. These results suggest that, in addition to electronic correlations, electron-phonon coupling contributes substantially to the emergence of long-range charge-stripe order in cuprates.
RESUMEN
The interplay between superconductivity and magnetism is one of the oldest enigmas in physics. Usually, the strong exchange field of ferromagnet suppresses singlet superconductivity via the paramagnetic effect. In EuFe2(As0.79P0.21)2, a material that becomes not only superconducting at 24.2 K but also ferromagnetic below 19 K, the coexistence of the two antagonistic phenomena becomes possible because of the unusually weak exchange field produced by the Eu subsystem. We demonstrate experimentally and theoretically that when the ferromagnetism adds to superconductivity, the Meissner state becomes spontaneously inhomogeneous, characterized by a nanometer-scale striped domain structure. At yet lower temperature and without any externally applied magnetic field, the system locally generates quantum vortex-antivortex pairs and undergoes a phase transition into a domain vortex-antivortex state characterized by much larger domains and peculiar Turing-like patterns. We develop a quantitative theory of this phenomenon and put forth a new way to realize superconducting superlattices and control the vortex motion in ferromagnetic superconductors by tuning magnetic domains-unprecedented opportunity to consider for advanced superconducting hybrids.
RESUMEN
Superconductivity (SC) with the suppression of long-range antiferromagnetic (AFM) order is observed in the parent compounds of both iron-based and cuprate superconductors. The AFM wave vectors are bicollinear (π, 0) in the parent compound FeTe different from the collinear AFM order (π, π) in most iron pnictides. Study of the phase diagram of Fe1+yTe1-xSex is the most direct way to investigate the competition between bicollinear AFM and SC. However, presence of interstitial Fe affects both magnetism and SC of Fe1+yTe1-xSex, which hinders the establishment of the real phase diagram. Here, we report the comparison of doping-temperature (x-T) phase diagrams for Fe1+yTe1-xSex (0 ≤ x ≤ 0.43) single crystals before and after removing interstitial Fe. Without interstitial Fe, the AFM state survives only for x < 0.05, and bulk SC emerges from x = 0.05, and does not coexist with the AFM state. The previously reported spin glass state, and the coexistence of AFM and SC may be originated from the effect of the interstitial Fe. The phase diagram of Fe1+yTe1-xSex is found to be similar to the case of the "1111" system such as LaFeAsO1-xFx, and is different from that of the "122" system.
RESUMEN
Iron chalcogenide Fe(Te,Se) attracted much attention due to its simple structure, which is favorable for probing the superconducting mechanism. Its less toxic nature compared with iron arsenides is also advantageous for applications of iron-based superconductors. By intercalating spacer layers, superconducting transition temperature has been raised over 40 K. On the other hand, the presence of excess Fe is almost unavoidable in Fe(Te,Se) single crystals, which hinders the appearance of bulk superconductivity and causes strong controversies over its fundamental properties. Here we report a Systematical study of O2-annealing dynamics in Fe(1+y)Te(1-x)Sex by controlling the amount of O2, annealing temperature, and time. Bulk superconductivity can be gradually induced by increasing the amount of O2 and annealing time at suitable temperatures. The optimally annealed crystals can be easily obtained by annealing with ~1.5% molar ratio of oxygen at 400 °C for more than 1 hour. Superconductivity was witnessed to evolve mainly from the edge of the crystal to the central part. After the optimal annealing, the complete removal of excess Fe was demonstrated via STM measurements. Some fundamental properties were recharacterized and compared with those of as-grown crystals to discuss the influence of excess Fe.