Phase transformation and room temperature stabilization of various Bi2O3 nano-polymorphs: effect of oxygen-vacancy defects and reduced surface energy due to adsorbed carbon species.

We report the grain growth from the nanoscale to microscale and a transformation sequence from Bi →ß-Bi2O3→γ-Bi2O3→α-Bi2O3 with the increase of annealing temperature. The room temperature (RT) stabilization of ß-Bi2O3 nanoparticles (NPs) was attributed to the effect of reduced surface energy due to adsorbed carbon species, and oxygen vacancy defects may have played a significant role in the RT stabilization of γ-Bi2O3 NPs. An enhanced red emission band was evident from all the samples attributed to oxygen-vacancy defects formed during the growth process in contrast with the observed white emission band from the air annealed Bi ingots. Based on our experimental findings, the air annealing induced oxidation of Bi NPs and transformation mechanism within various Bi2O3 nano-polymorphs are presented. The outcome of this study suggests that oxygen vacancy defects at the nanoscale play a significant role in both structural stabilization and phase transformation within various Bi2O3 nano-polymorphs, which is significant from theoretical consideration.

Impact of Nonideal Nanoparticles on X-ray Photoelectron Spectroscopic Quantitation: An Investigation Using Simulation and Modeling of Gold Nanoparticles.

Quantitative X-ray photoelectron spectroscopic (XPS) analysis combined with spectral modeling of photoelectrons can be valuable while investigating the surface chemistry of nanoparticles (NPs) with different morphologies. Herein, with the use of NIST Simulation of Electron Spectra for Surface Analysis (SESSA), a comparative analysis of experimental and simulated photoelectron peak intensities in gold nanoparticles (AuNPs) of different morphologies is presented. Three sets of supported AuNPs with different morphologies were selected from a series of as synthesized Au-TiO2 catalyst samples. Using transmission electron microscopy (TEM) analyzed morphological information on the AuNPs as input model parameters in SESSA, XPS spectra were generated from the respective input NP morphologies. A degree of greater mismatch between SESSA simulated and experimental XPS spectra was observed while using the TEM obtained average diameter of the nanoparticles. The degree of mismatch lowered when the true nonspherical shape of the nanoparticles as obtained from TEM images was taken into account for the simulation. This demonstrates the impact of surface morphology on the XPS peak intensities which needs to be incorporated to obtain precise quantified information from the supported nanoparticles. This work demonstrates the applicability of SESSA in combination with experimental XPS and TEM measurements for precise quantification of XPS spectra from complex, nonideal shaped nanoparticles. This study can be extended to include a broad range of nanoparticles with ideal or nonideal geometries, thus providing a simple method to utilize quantitative XPS analysis to a wide range of nanomaterials.

Iron phthalocyanine modified mesoporous titania nanoparticles for photocatalytic activity and CO2 capture applications.

An iron(II)phthalocyanine (Fepc) modified mesoporous titania (Fepc-TiO2) nanocatalyst with a specific surface area of 215 m(2) g(-1) has been synthesized by a hydrothermal method. Fepc-TiO2 degrades one of the highly toxic chemical warfare agents, sulfur mustard (SM), photocatalytically under sunlight with an exposure time of as low as 70 min. Furthermore, the mesoporous Fepc-TiO2 also captured 2.1 mmol g(-1) of CO2 at 273 K and 1 atm.

Photocatalytic inactivation of spores of Bacillus anthracis using titania nanomaterials.

Studies on photocatalytic inactivation of spores of Bacillus anthracis have been carried out using nanosized titania materials and UVA light or sun light. Results demonstrated pseudo first order behaviour of spore inactivation kinetics. The value of kinetic rate constant increased from 0.4h(-1) to 1.4h(-1) indicating photocatalysis facilitated by addition of nanosized titania. Nanosized titania exhibited superior inactivation kinetics on par with large sized titania. The value of kinetic rate constant increased from 0.02 h(-1) to 0.26 h(-1) on reduction of size from 1000 nm to 16 nm depicting the enhanced rate of inactivation of Bacillus anthracis Sterne spores on the decrease of particle size.

Decontamination of Yperite using mesoporous mixed metal oxide nanocrystals.

Mixed metal oxide nanocrystals of AP-Al(2)O(3), AP-Al(2)O(3)-Fe(2)O(3), AP-Al(2)O(3)-V(2)O(5) and AP-Al(2)O(3)-CuO have been prepared by aerogel process. XRD data of prepared materials revealed the formation of nanocrystals with a size range of 3-15 nm diameters. N(2) BET investigations on these materials revealed larger values of surface area ranging from 350 to 540 m(2)/g. Reactivity of these nanocrystalline materials against Yperite was examined by gas chromatography, gas chromatography-mass spectrometry and infrared spectroscopy techniques. AP-Al(2)O(3)-Fe(2)O(3), AP-Al(2)O(3)-V(2)O(5) and AP-Al(2)O(3)-CuO nanocrystals exhibited superior decontamination properties against Yperite than AP-Al(2)O(3). The reactions exhibited pseudo first order behaviour. 100% of Yperite was found to be decontaminated on Al(2)O(3)-Fe(2)O(3), Al(2)O(3)-V(2)O(5) and Al(2)O(3)-CuO where only 75% of the same was found to be decontaminated on AP-Al(2)O(3) within 40 h.