RESUMEN
Ti-15V-3Cr-3Al-3Sn (Ti-15-3) is a metastable beta alloy which is considered to be a potential alternative for Ti-6Al-4V alpha+beta alloy for aerospace applications, especially for sheet products. This paper describes the work carried out to enhance the fatigue life of Ti-15-3 in an economical way by means of laser peening without coating (LPwC) using Nd:YAG laser operating at a power density of 5 GW cm-2. In order to have a sufficient bulk hardness and high compressive stresses on the surface, as-received beta solution treated (ST) Ti-15-3 was subjected to aging (520 °C/10 h/Air-cooled) and then to LPwC. Laser peening induced a notable increase in Ra (arithmetic mean roughness), which was measured using MAHR GD-120 profilometer. The Electron Back Scatter Diffraction (EBSD) analysis of the aged sample (STA) revealed a significant increase in the alpha precipitation (20 vol%), and this led to a substantial increase in the hardness (~40%) and UTS (~50%). In addition to this, peening of aged (STA+LPwC) sample resulted in a considerable increase (~12%) in near-surface microhardness and compressive residual stress (maximum stress of -195 MPa at a depth of 150 µm). This increase in compressive stress and microhardness led to an enhancement in the fatigue life of the STA+LPwC sample by 210% when compared to STA sample. In spite of high surface roughness induced by the LPwC, fractography studies revealed that crack initiation was independent of surface roughness.
RESUMEN
A 55-year-old woman presented with fever, breathlessness and shock. She was diagnosed to have diabetes mellitus (Type 2) after admission. Blood culture grew Burkholderia pseudomallei. The patient responded to intravenous ceftozidime for two weeks and a prolonged course of six months with cotrimoxazole and doxycycline.