Exciton-Phonon Interactions in Strained Domes of Monolayer MoS2 Studied by Resonance Raman Spectroscopy.

This work describes a resonance Raman study performed in the domes of monolayer MoS2 using 23 different laser excitation energies covering the visible and near-infrared (NIR) ranges. The multiple excitation results allowed us to investigate the exciton-phonon interactions of different phonons (A'1, E', and LA) with different excitonic optical transitions in biaxially strained monolayer MoS2. The analysis of the intensities of the two first-order peaks, A'1 and E', and the double-resonance 2LA Raman band as a function of the laser excitation furnished the values of the energies of the indirect exciton and the direct excitonic transitions in the strained MoS2 domes. It was noticed that the out-of-plane A'1 phonon mode is significantly enhanced only by the indirect exciton I and the C exciton, whereas the in-plane E' mode is only enhanced by the C exciton of the MoS2 dome, thus revealing the weak interaction of these phonons with the A and B excitons in the strained MoS2 domes. On the other hand, the 2LA Raman band is significantly enhanced at the indirect exciton I and by the A (or B) exciton but not enhanced by the C exciton, thus showing that the LA edge phonons that participate in the double-resonance process in MoS2 have a weak interaction with the C exciton.

Visible Out-of-plane Polarized Luminescence and Electronic Resonance in Black Phosphorus.

Black phosphorus (BP) is unique among layered materials because of its homonuclear lattice and strong structural anisotropy. While recent investigations on few-layer BP have extensively explored the in-plane (a, c) anisotropy, much less attention has been given to the out-of-plane direction (b). Here, the optical response from bulk BP is probed using polarization-resolved photoluminescence (PL), photoluminescence excitation (PLE), and resonant Raman scattering along the zigzag, out-of-plane, and armchair directions. An unexpected b-polarized luminescence emission is detected in the visible, far above the fundamental gap. PLE indicates that this emission is generated through b-polarized excitation at 2.3 eV. The same electronic resonance is observed in resonant Raman with the enhancement of the Ag phonon modes scattering efficiency. These experimental results are fully consistent with DFT calculations of the permittivity tensor elements and demonstrate the remarkable extent to which the anisotropy influences the optical properties and carrier dynamics in black phosphorus.

Comparison between hydroxyapatite/soapstone and hydroxyapatite/reduced graphene oxide composite coatings: Synthesis and property improvement.

Economic viability and eco-friendliness are important characteristics that make implants available to the population in a sustainable way. In this work, we evaluate the performance of a low-cost, widely available, and eco-friendly material (talc from soapstone) relative to reduced graphene oxide as reinforcement to brittle hydroxyapatite coatings. We employ a low-cost and straightforward technique, electrodeposition, to deposit the composite coatings on the titanium substrate. Corrosion, wear, and biocompatibility tests indicate that the reduced graphene oxide can be effectively replaced by talc without reducing the mechanical, anticorrosion, and biocompatible composite coatings properties. Our results indicate that talc from soapstone is a promising material for biomedical applications.

Resonant laser-induced formation of double-walled carbon nanotubes from peapods under ambient conditions.

The selective excitation of fullerenes encapsulated in single-walled carbon nanotubes (SWCNTs) is carried out by irradiating them using a UV laser, the wavelength of which corresponds exactly to their maximum of absorption. Under such conditions, fullerenes strongly absorb the laser energy, open, and break, while the containing SWCNT merely acts as both a nanoreactor and a mold which is only weakly heated by the laser. The containing tube confines the fullerene fragments, promotes their reconstruction into an inner tube, and protects them from air oxidation. This leads to the overall formation of double-walled carbon nanotubes (DWCNTs). The transformation is found to strongly depend on the laser irradiance and dose. This proves that the related mechanism is a multiphoton photolysis, different from the previous heat-induced transformation attempts found in the literature, whether the heat is produced by means of a thermostat, infrared laser, or nonresonant UV laser. The actual peapod-to-DWCNT transformation is monitored by Raman spectroscopy and high-resolution transmission electron microscopy.

Correlation between thermal, optical and morphological properties of heterogeneous blends of poly(3-hexylthiophene) and thermoplastic polyurethane.

A correlation between thermal, optical and morphological properties of self-sustained films formed from blends of poly(3-hexylthiophene) (P3HT) and thermoplastic polyurethane (TPU), with 1, 10 and 20 wt% of P3HT in TPU, is established. Images of scanning electron microscopy (SEM) show the formation of domains of P3HT into the TPU matrix, characterizing the blend material as heterogeneous. The heat capacity (C(p)) dependence on P3HT contents was investigated in a large temperature interval. In the region of the TPU glass transition, the difference between the experimental and predicted ΔC(p) values is more pronounced for the 1 wt% case, which strongly suggests that in this case there is a higher influence of the P3HT chains on the TPU matrix. The SEM images for the 1 wt% blended film present the formation of the smallest P3HT domains in the TPU matrix. The relatively high reduction of the PL intensity of the pure electronic transition peak in the 1 wt% blended film, in comparison to the other blended films and also to a pure P3HT film, favours the assumption that the smallest P3HT domains are at the origin of a more structural disordered character. This fact is in agreement with the results obtained by Raman spectroscopy and also by photoluminescence resolved by polarization in stretched self-sustained films, showing an ample correlation between morphological, thermal and optical properties of these blended materials. In addition, the thermoplastic properties of the polyurethane configure very good conditions for tensile drawing of P3HT and other conjugated polymer molecules.