Ferromagnetic Mn-doped Si0.3Ge0.7 nanodots self-assembled on Si(100).

Densely packed epitaxial Mn-doped Si(0.3)Ge(0.7) nanodots self-assembled on Si(100) have been obtained. Their structural properties were studied using reflection high-energy electron diffraction, energy dispersive x-ray diffraction, atomic force microscopy, extended x-ray absorption fine structure measurements and high-resolution transmission electron microscopy. Mn(5)Ge(1)Si(2) crystallites embedded in Si(0.3)Ge(0.7) were found. They exhibit a ferromagnetic behaviour with a Curie temperature of about 225 K.

Self-amplified spontaneous emission free-electron laser with an energy-chirped electron beam and undulator tapering.

We report the first experimental implementation of a method based on simultaneous use of an energy chirp in the electron beam and a tapered undulator, for the generation of ultrashort pulses in a self-amplified spontaneous emission mode free-electron laser (SASE FEL). The experiment, performed at the SPARC FEL test facility, demonstrates the possibility of compensating the nominally detrimental effect of the chirp by a proper taper of the undulator gaps. An increase of more than 1 order of magnitude in the pulse energy is observed in comparison to the untapered case, accompanied by FEL spectra where the typical SASE spiking is suppressed.

Crystallization process of carbonate substituted hydroxyapatite nanoparticles in toothpastes upon physiological conditions: an in situ time-resolved X-ray diffraction study.

The crystallization process in recently developed toothpastes, containing nanoparticles of carbonate substituted hydroxyapatite (nano-CHA), was investigated. For this purpose, the non-conventional Energy Dispersive X-Ray Diffraction technique, that demonstrated to be a powerful tool to follow in situ phase transformations, was applied, for the first time, to products of pharmaceutical-cosmetic interest. Two types of toothpastes, containing 15 and 20 wt% of nano-CHA, respectively, have been studied. It was observed that, after mixing the toothpastes with water and saliva in order to reproduce in vivo conditions, a crystallization of nano-CHA takes place. Such process occurs in a characteristic time of (22 +/- 1) min for the toothpaste containing 15 wt% of nano-CHA and of (3.9 +/- 0.5) min for the one containing 20% of nano-CHA. For both toothpastes, a 10% increase in grain dimensions was observed over an average characteristic time of (55 +/- 5) min.

Energy dispersive X-ray diffraction study of phase development during hardening of calcium phosphate bone cements with addition of chitosan.

The aim of this work was to study the phase transformation during the setting reaction of two calcium phosphate bone cements based on either alpha tricalcium phosphate (alpha-TCP) or tetracalcium phosphate (TetCP) initial solid phase, and a magnesium carbonate-phosphoric acid solution as the hardening liquid. Low molecular weight (38.2 kDa) chitosan was used to retard the cement's setting reaction. To follow the kinetics of the phase development, an energy dispersive X-ray diffraction technique was applied. This technique allowed the collection of diffraction patterns from the cement pastes in situ starting from 1 min of the setting process. In the case of the TetCP-based cement, the appearance and evolution of an intermediate phase was detected.