RESUMEN
The dip coating process is one of the recognized techniques used to generate polymeric coatings on stents in an easy and low-cost way. However, there is a lack of information about the influence of the process parameters of this technique on complex geometries such as stents. This paper studies the dip coating process parameters used to provide a uniform coating of PLA with a 4-10 µm thickness. A stainless-steel tube (AISI 316L) was laser-cut, electropolished, and dip-coated in a polylactic acid (PLA) solution whilst changing the process parameters. The samples were characterized to examine the coating's uniformity, thickness, surface roughness, weight, and chemical composition. FTIR and Raman investigations indicated the presence of PLA on the stent's surface, the chemical stability of PLA during the coating process, and the absence of residual chloroform in the coatings. Additionally, the water contact angle was measured to determine the hydrophilicity of the coating. Our results indicate that, when using entry and withdrawal speeds of 500 mm min-1 and a 15 s immersion time, a uniform coating thickness was achieved throughout the tube and in the stent with an average thickness of 7.8 µm.
RESUMEN
Throughout history, different techniques have been used for the development of scaffolds for Tissue Engineering. Among them, three-dimensional (3D) printing for this application has been recently enhanced due to its ease in defining the structure of the material. In this sense, a novel potential alternative could be the development of a three-part device whose leading utility is to improve the introduction of the scaffold in a bioreactor. Thus, the device consists of a polycaprolactone support on which smart gelatin (GE) matrix, and finally, on top, a collagen (C) scaffold. This gelatin matrix is included to integrate the scaffold into the support, but once both are assembled, it must be removed, leaving only the support and the scaffold. Thus, in the present work, a small gelatin matrix has been evaluated. To this end, matrices with different gelatin percentages were studied, evaluating their mechanical and morphological properties at different temperatures (22 and 37 °C) to control their deposition and elimination. The results show the high application of this smart matrix for the development of scaffolds via 3D bioprinting for Tissue Engineering.