RESUMEN
The flammability of combustible materials in a spacecraft is important for fire safety applications because the conditions in spacecraft environments differ from those on earth. Experimental testing in space is difficult and expensive. However, reducing buoyancy by decreasing ambient pressure is a possible approach to simulate on-earth the burning behavior inside spacecraft environments. The objective of this work is to determine that possibility by studying the effect of pressure on concurrent flame spread, and by comparison with microgravity data, observe up to what point low-pressure can be used to replicate flame spread characteristics observed in microgravity. Specifically, this work studies the effect of pressure and microgravity on upward/concurrent flame spread over 10 mm thick polymethyl methacrylate (PMMA) slabs. Experiments in normal gravity were conducted over pressures ranging between 100 and 40 kPa and a forced flow velocity of 200 mm/s. Microgravity experiments were conducted during NASA's Spacecraft Fire Experiment (Saffire II), on board the Cygnus spacecraft at 100 kPa with an air flow velocity of 200 mm/s. Results show that reductions of pressure slow down the flame spread over the PMMA surface approaching that in microgravity. The data is correlated in terms of a non-dimensional mixed convection analysis that describes the convective heat transferred from the flame to the solid, and the primary mechanism controlling the spread of the flame. The extrapolation of the correlation to low pressures predicts well the flame spread rate obtained in microgravity in the Saffire II experiments. Similar results were obtained by the authors with similar experiments with a thin composite cotton/fiberglass fabric (published elsewhere). Both results suggest that reduced pressure can be used to approximately replicate flame behavior of untested gravity conditions for the burning of thick and thin solids. This work could provide guidance for potential ground-based testing for fire safety design in spacecraft and space habitats.
RESUMEN
In the interest of fire prevention, most materials used in the interior construction of manned spacecraft are non-flammable, however, they do produce smoke when overheated. Spacecraft smoke detectors will ideally detect smoke generated by oxidative pyrolysis (such as smoldering) in order to allow the maximum time for the crew to respond before a larger flaming fire develops. An experiment on the International Space Station (ISS) characterized smoke from overheating common spacecraft materials. The following parameters were controlled: heating temperature, air flow past the samples and duration of aging. Two different spacecraft smoke detectors were included in the instrumentation and their performance with different smoke types has been evaluated. Additional equipment in the experiment included a thermal precipitator to sample particles for microscopic analysis upon return to Earth, and three commercial-off-the-shelf real-time instruments to measure particle mass and number concentration, and an ionization detector calibrated to estimate the first moment of the size distribution. Results from the ISS experiment show that smoke particles vary in morphology and average diameter, however, they are not significantly different from smoke particles generated in equivalent experiments performed in normal gravity. The two spacecraft smoke detectors did not successfully detect every type of smoke, which demonstrates that the next generation of spacecraft fire detectors must be improved and tested against smoke from relevant space materials.
RESUMEN
The flammability of combustible materials in spacecraft environments is of importance for fire safety applications because the environmental conditions can greatly differ from those on earth, and a fire in a spacecraft could be catastrophic. Moreover, experimental testing in spacecraft environments can be difficult and expensive, so using ground-based tests to inform microgravity tests is vital. Reducing buoyancy effects by decreasing ambient pressure is a possible approach to simulate a spacecraft environment on earth. The objective of this work is to study the effect of pressure on material flammability, and by comparison with microgravity data, determine the extent to which reducing pressure can be used to simulate reduced gravity. Specifically, this work studies the effect of pressure and microgravity on upward/concurrent flame spread rates and flame appearance of a burning thin composite fabric made of 75% cotton and 25% fiberglass (Sibal). Experiments in normal gravity were conducted using pressures ranging between 100 and 30 kPa and a forced flow velocity of 20 cm/s. Microgravity experiments were conducted during NASA's Spacecraft Fire Experiment (Saffire), on board of the Orbital Corporation Cygnus spacecraft at 100 kPa and an air flow velocity of 20 cm/s. Results show that reductions of ambient pressure slow the flame spread over the fabric. As pressure is reduced, flame intensity is also reduced. Comparison with the concurrent flame spread rates in microgravity show that similar flame spread rates are obtained at around 30 kPa. The normal gravity and microgravity data is correlated in terms of a mixed convection non-dimensional parameter that describes the heat transferred from the flame to the solid surface. The correlation provides information about the similitudes of the flame spread process in variable pressure and reduced gravity environments, providing guidance for potential on-earth testing for fire safety design in spacecraft and space habitats.