Internal and Marginal Fit and Fracture Strength of Narrow Diameter Dental Implant-Abutment Assembly.

The aim of this study was to assess the internal and vertical marginal fit of metallic copings to abutments and the fracture strength of different narrow diameter dental implant/abutments, either submitted to thermomechanical cycling or not. Sixty-four implant/abutments (n=16) were divided into 4 groups according to diameter and abutment type: G3.5-UAC (morse taper implant Ø3.5mm + universal abutment with beveled chamfer finish); G2.9-UAS (morse taper implant Ø2.9mm + universal abutment with shoulder finish); G2.8-AA (morse taper friction implant Ø2.8mm + anatomical abutment) and G2.5-HP (one-piece implant Ø2.5mm with indexed hexagonal platform). Each group was divided into two subgroups (n=8): submitted and not submitted to thermomechanical cycling (TMC). To assess internal and vertical marginal fit of metallic copings, the assemblies were scanned using microtomography (micro-CT) (n=5). The samples were subjected to the compressive strength test on a universal test machine. Group G3.5-UAC showed the highest marginal misfit regardless of TMC (p<0.05). All other groups were similar after TMC. Group G2.8-AA showed the lowest internal misfit both with and without TMC (p<0.05). Group G2.8-AA showed the highest fracture strength, similar only to G2.5-HP without TMC and G3.5-UAC with TMC. The type of abutment affects the internal and marginal fit of metallic copings and the anatomical abutment led to the best internal and marginal coping fit. The narrow diameter dental implant/abutments differ in terms of fracture strength, the strongest assembly was that composed by implant of type V grade titanium without internal threads (friction implant).

Internal and marginal fit and fracture strength of narrow diameter dental implant-abutment assembly

Abstract The aim of this study was to assess the internal and vertical marginal fit of metallic copings to abutments and the fracture strength of different narrow diameter dental implant/abutments, either submitted to thermomechanical cycling or not. Sixty-four implant/abutments (n=16) were divided into 4 groups according to diameter and abutment type: G3.5-UAC (morse taper implant Ø3.5mm + universal abutment with beveled chamfer finish); G2.9-UAS (morse taper implant Ø2.9mm + universal abutment with shoulder finish); G2.8-AA (morse taper friction implant Ø2.8mm + anatomical abutment) and G2.5-HP (one-piece implant Ø2.5mm with indexed hexagonal platform). Each group was divided into two subgroups (n=8): submitted and not submitted to thermomechanical cycling (TMC). To assess internal and vertical marginal fit of metallic copings, the assemblies were scanned using microtomography (micro-CT) (n=5). The samples were subjected to the compressive strength test on a universal test machine. Group G3.5-UAC showed the highest marginal misfit regardless of TMC (p<0.05). All other groups were similar after TMC. Group G2.8-AA showed the lowest internal misfit both with and without TMC (p<0.05). Group G2.8-AA showed the highest fracture strength, similar only to G2.5-HP without TMC and G3.5-UAC with TMC. The type of abutment affects the internal and marginal fit of metallic copings and the anatomical abutment led to the best internal and marginal coping fit. The narrow diameter dental implant/abutments differ in terms of fracture strength, the strongest assembly was that composed by implant of type V grade titanium without internal threads (friction implant).

Resumo O objetivo deste estudo foi avaliar a adaptação marginal e interna de cópings metálicos em pilares sobre implantes, e a resistência a fratura de diferentes conjuntos de implantes/pilares de diâmetro reduzido, submetidos à ciclagem termomecânica ou não. Sessenta e quatro implantes/pilares (n=16) foram divididos em 04 grupos de acordo com o tipo de pilar e diâmetro do implante: G3.5-UAC (implante cone morse Ø3.5mm + munhão universal com término em chanfro); G2.9-UAS (implante cone morse Ø2.9mm + munhão universal com término em ombro); G2.8-AA (implante cone morse friccional Ø2.8mm + munhão anatômico); e G2.5-HP (implante de corpo único de Ø2.5mm com plataforma hexagonal indexada). Cada grupo foi dividio em dois subgrupos (n=8): submetidos ou não à ciclagem termomecânica (TMC). As amostras foram escaneadas por microtomografia (micro-CT) para avaliar a adaptação interna e marginal vertical dos copings metálicos. As amostras foram submetidas à resistência à compressão em uma maquina de ensaios universal. O grupo G3.5-UAC apresentou os maiores valores de desadaptação marginal independentemente da TMC (p<0,05). Todos os outros grupos foram similares entre si após TMC. O grupo G2.8-AA demonstrou o menor desajuste interno independentemente de TMC (p<0,05). O grupo G2.8-AA demonstrou a maior resistência à fratura, similar apenas ao grupo G2.5-HP sem TMC e G3.5-UAC com TMC. O tipo de pilar influencia a adaptação interna e marginal vertical de copings metálicos. O grupo do pilar anatômico (sem entalhes na superfície) levou à melhor adaptação, enquanto o grupo com plataforma expandida hexagonal e os grupos com munhão universal (com entalhes na superfície) proporcionaram os maiores desajustes (especialmente com termino em chanfro). Os implantes/pilares de diâmetro reduzido diferem em termos de resistencia à fratura, sendo que o conjunto mais resistente foi aquele composto por titânio tipo V e sem roscas internas (implante friccional).

Mechanical properties and superficial characterization of a milled CAD-CAM glass fiber post.

Computer-aided design and computer-aided manufacturing (CAD-CAM) technology may be used to produce custom intraradicular posts, but studies are lacking. The purpose of this in vitro study was to evaluate the flexural properties (strength and modulus), failure mode, superficial morphology, and roughness of two CAD-CAM glass fiber posts (milled at different angulations) compared with a commercially available prefabricated glass fiber post. Three groups were tested (n = 10): PF (control group)- prefabricated glass fiber post; C-Cd-diagonally milled post; and C-Cv-vertically milled post. A 3-dimensional virtual image was obtained from a prefabricated post, which guided the posterior milling of posts from a glass fiber disk (Trilor Blanks; Bioloren). Surface roughness and morphology were evaluated using confocal laser microscopy. Flexural strength and modulus were evaluated with the 3-point bend test. Data were submitted to one-way analysis of variance followed by the Student-Newman-Keuls post hoc test (α = 0.05). The fractured surfaces were evaluated with scanning electron microscopy. The superficial roughness was highest for PF and similar for the experimental groups. Morphological analysis shows different sizes and directions of the glass fibers along the post. The flexural strength was highest for PF (900.1 ±â€¯30.4 > C-Cd - 357.2 ±â€¯30.7 > C-Cv 101.8 ±â€¯4.3 MPa) as was the flexural modulus (PF 19.3 ±â€¯2.0 GPa > C-Cv 10.1 ±â€¯1.9 GPa > C-Cd 7.8 ±â€¯1.3 GPa). A CAD-CAM milled post seems a promising development, but processing requires optimizing, as the prefabricated post still shows better mechanical properties and superficial characteristics.

Enxerto ósseo interposicional: uma alternativa viável para ganho ósseo vertical / Interpositional bone graft: a viable alternative to vertical bone augmentation

Nos planejamentos cirúrgicos para a Implantodontia, diferentes abordagens terapêuticas são possíveis para o tratamento dos defeitos ósseos, quando relacionados a defeitos em espessura. Porém, quando nos deparamos com defeitos verticais, a resolução torna-se mais complexa, uma vez que as técnicas aposicionais de enxertia são deficientes para o ganho ósseo vertical. Para tanto, a utilização da técnica de osteotomias segmentares seguida de enxertos de interposição fornece previsibilidade e segurança clínica. Com o objetivo de demonstrar essa técnica, apresenta-se um caso clínico de osteotomia segmentar seguida de enxerto interposicional com hidroxiapatita sintética reabsorvível na região anterior da maxila

In planning for surgical implants, some therapeutic approaches are possible for treating bone defects in thickness. However, when facing vertical defects, the resolution becomes more complex, since appositional grafting techniques are deficient for vertical bone gain. Therefore, using the technique of segmental osteotomies followed by interposition grafts provides predictable and clinically safe resolution. To demonstrate this technique, this paper presents a case of segmental osteotomy followed by interpositional graft with resorbable synthetic hydroxyapatite in the anterior maxilla

Análise dos níveis de cinza de pinos intra-radiculares de fibra de carbono radiografados com filme Insight no programa Digora / Gray level analysis of intrarradicular carbon fiber post in digitalized x-rays using Insight films in the Digora program

Os objetivos deste trabalho foram: 1) mensurar a densidade óptica (níveis de cinza) de pinos de fibra de carbono C-Post n. 1, 1,4mm de diâmetro (Bisco), no interior de condutores radiculares de 22 incisivos centrais superiores tratados endodonticamente com cimento a base de óxido de zinco e eugenol; 2) comparar os pinos pré-fabricados de fibra de carbono com a dentina mesial e distal adjacente, no programa Digora. Foi realizada uma sequência de tomadas radiográficas utilizando filmes InSight e simulador de tecido moles de cera utilidade de 1 cm de espessura nas raízes preparadas com o pino inserido nos condutos. Os filmes foram processados automaticamente numa processadora AT2000 da Air Techniques Inc. As radiografias foram escaneadas e digitalizadas no programa Digora, obtendo os valores de densidade óptica da dentina mesial e distal e do pino no interior dos condutos. Os resultados foram analisados estatisticamente por t-Student. Verificou-se que o pino dentro dos condutos apresentou valores de níveis de cinza (pixels) maiores que os das dentinas adjacentes mesial e distais. Os valores médios das dentinas mesiais e distais mostraram-se diferentes, ao nível de 1%

Análise dos níveis de cinza de pinos intra-radiculares de fibra de vidro por meio de imagens digitalizadas: estudo in vitro / Analysis of gray levels of fiber posts through digital images: in vitro study

O objetivo da pesquisa foi comparar e correlacionar os níveis de cinza dos pinos intra-radiculares de fibra de vidro Fibrekor Post® (jeneric/Pentron) com a dentina radicular por meio dos sistemas digital Digora® e DentScan DentView®. A coroa de 22 incisivos centrais superiores foi secionada; os condutos radiculares, obturados pela técnica convencional e posteriormente preparados para receber os pinos de fibras de vidro com frequesas de 1,5mm de diâmetro do kit Fibrekor Post®. Foram realizados três sequências radiográficas, com filmes periapicais n 2 Ultraspeed® da Kodak, dos pinos no inteior do conduto e da dentina radicular, com técnica padronizada. As radiografias foram digitalizadas e os valores dos níveis de cinza foram obtidos pelas ferramentas dos sistemas digitais Digora® e DentScan DentView®, sendo posteriormente submetidos aos testes estatatístico t-student e de correlação de Pearson para uma probabilidade de erro de 1 por cento. Verificou-se que os valores médios dos níveis de cinza dos pinos nos interior dos condutos foram: 146,71 no sistema Digora® e 199,50 no sistema DentScan DentView®. Esses valores mostraram-se superiores aos da dentina radicular mesial e distal nos dois sistemas digitais. os níveis de cinza obtidos no sistema Digora® apresentaram um coeficiente de correlaçoa de Pearson positivo em relação ao DentScan DentView®. Conclui-se que os pinos de fibra de vidro Fibrekor Post® com 1,5 mm de diâmetro apresentaram uma imagem radiopaca no interior dos condutos radiculares dos incisivos centrais superiores

Análise dos níveis de cinza de pinos intrarradiculares de quartzo em radiografias digitalizadas utilizando filmes de diferentes sensibilidades / Analyse of the grey levels intraroot quartz post in digitized x-rays with films of the differents sensibilities

Objetivos: Analisar os níveis de cinza de pinos intrarradiculares de quartzo em radiografias digitalizados com filmes de diferentes sensibilidades. Metodologia: Foram selecionados 22 incisivos centrais superiores, que tiveram suas coroas seccionadas, seu canais tratados e preparados para receber o pino pré-fabricado Light-PostDT número 1. Após a verificação radiográfica da correta execução dos passos anteriores, radiografou-se o pino dentro do conduto dos espécimes com três incidências para cada amostra; este procedimento foi realizado com dois filmes de diferentes sensibilidades, com o tempo de exposição de 0,43 s para o InSight e 0,9 s para o Ultra-speed. Posteriormente foram feitas as digitalizações das imagens para leitura ótica das mesmas no programa Digora (Soderex). Resultados: O nível médio de cinza para o filme Ultra-speed dos pinos no interior de conduto foi de 249,35 e para dentina adjacente foi de 225,43; já no filme InSight o nível médio de cinza dos pinos no interior do conduto foi de 242,90e para dentina adjacente foi de 212,10. Ambos para um nível de significância de 1 por cento (p=0,010). Conclusão: Através do teste de comparação de médias pareadas t-Student, verificou-se que não houve diferença estatisticamente significante nos níveis de cinza entre as dentinas mesial e distal para ambos os filmes; já o pino apareceu com os níveis de cinza significantemente superiores à dentina adjacente. O filme InSight mostrou densidade óptica inferior no pino e na dentina adjacente com relação ao filme Ultra-speed

Tomografia linear X tomografia computadorizada / Linear tomography X computadorized tomography

Esta revisäo teve a finalidade de comparar as vantagens e as desvantagens do uso das tomografias lineares e computadorizadas