Effect of the Dislocation Substructure Parameters of Hadfield Steel on Its Strain Hardening.

This article presents a study of changes in the microstructure of Hadfield steel depending on the tensile deformation and cold rolling with the strain/stress level. It has been established that the change in the "σ-ε" curve (at ε = 5%) is accompanied by a 1.5-times decrease in the strain-hardening coefficient. At ε = 0 to 5%, the structure contains dislocation loops, the interweaving of elongated dislocations, single-layer stacking faults. At ε = 5%, the structure contains multilayer stacking faults and mechanical microtwins. At ε > 5%, there is an intense microtwinning with no long dislocations and stacking faults. The most intense twinning develops in the range of deformation degrees of 5-20%, while the number of twins in the pack increases from 3-4 at ε = 10% to 6-8 at ε = 20%. When mechanical twinning is included, a cellular dislocation substructure begins to develop intensively. The cell size decreases from 700 nm at ε = 5% to 150 nm at ε = 40%. Twinning develops predominantly in systems with the largest Schmid factor and facilitates the dislocation glide. The results may be of interest to the researchers of the deformation processes of austenitic alloys.

Kinetic and Isotherm Study of As(III) Removal from Aqueous Solution by PET Track-Etched Membranes Loaded with Copper Microtubes.

This paper reports on the synthesis and structure elucidation of track-etched membranes (TeMs) with electrolessly deposited copper microtubes (prepared in etched-only and oxidized polyethylene terephthalate (PET) TeMs), as well as on the comparative testing of arsenic (III) ion removal capacities through bath adsorption experiments. The structure and composition of composites were investigated by X-ray diffraction technique and scanning electron and atomic force microscopies. It was determined that adsorption followed pseudo-second-order kinetics, and the adsorption rate constants were calculated. A comparative study of the applicability of the adsorption models of Langmuir, Freundlich, and Dubinin-Radushkevich was carried out in order to describe the experimental isotherms of the prepared composite TeMs. The constants and parameters of all of the above equations were determined. By comparing the regression coefficients R2, it was shown that the Freundlich model describes the experimental data on the adsorption of arsenic through the studied samples better than others. Free energy of As(III) adsorption on the samples was determined using the Dubinin-Radushkevich isotherm model and was found to be 17.2 and 31.6 kJ/mol for Cu/PET and Cu/Ox_PET samples, respectively. The high EDr value observed for the Cu/Ox_PET composite indicates that the interaction between the adsorbate and the composite is based on chemisorption.