Critical-sized bone defects regeneration using a bone-inspired 3D bilayer collagen membrane in combination with leukocyte and platelet-rich fibrin membrane (L-PRF): An in vivo study.

OBJECTIVES: We aim to develop a 3D-bilayer collagen (COL) membrane reinforced with nano beta-tricalcium-phosphate (nß-TCP) particles and to evaluate its bone regeneration in combination with leukocyte-platelet-rich fibrin (L-PRF) in vivo. BACKGROUND DATA: L-PRF has exhibited promising results as a cell carrier in bone regeneration in a number of clinical studies, however there are some studies that did not confirm the positive results of L-PRF application. METHODS: Mechanical & physiochemical characteristics of the COL/nß-TCP membrane (1/2 & 1/4) were tested. Proliferation and osteogenic differentiation of seeded cells on bilayer collagen/nß-TCP thick membrane was examined. Then, critical-sized calvarial defects in 8 white New Zealand rabbits were filled with either Col, Col/nß-TCP, Col/nß-TCP combined with L-PRF membrane, or left empty. New bone formation (NBF) was measured histomorphometrically 4 & 8 weeks postoperatively. RESULTS: Compressive modulus increases while porosity decreases with higher ß-TCP concentrations. Mechanical properties improve, with 89 % porosity (pore size ∼100 µm) in the bilayer-collagen/nß-TCP membrane. The bilayer design also enhances the proliferation and ALP activity. In vivo study shows no significant difference among test groups at 4 weeks, but Col/nß-TCP + L-PRF demonstrates more NBF compared to others (P < 0.05) after 8 weeks. CONCLUSION: The bilayer-collagen/nß-TCP thick membrane shows promising physiochemical in vitro results and significant NBF, as ¾ of the defect is filled with lamellar bone when combined with L-PRF membrane.