Hydrothermally synthesized Ag-TiO2 nanofibers (NFs) for photocatalytic dye degradation and antibacterial activity.

This work successfully utilised eco-friendly green synthesis to produce Ag-TiO2 nanofibers (NFs). As pollution and energy limitations have become global issues, there is an ongoing need to develop more effective catalysts through straightforward and environmentally friendly methods. The Ag-TiO2 nanofibers (NFs) XRD pattern exhibits an anatase TiO2 and FCC crystal structure of Ag nanoparticles. The SEM investigation revealed a nanofiber-like surface morphology. The Ag-TiO2 nanofibers (NFs) exhibits an optical band gap energy is 2.5 eV. Methylene blue (MB), malachite green (MG), Congo red (CR), and crystal violet (CV) dye aqueous solutions were used to evaluate the photocatalytic performance of the synthesized Ag-modified TiO2 nanofibers (NFs) under direct sunlight irradiation. The effects of catalyst size on the efficient breakdown of MB dye were also investigated. The optimum catalyst concentration was found to be at 0.02 mg/mL. At 120 min of direct sunlight, the highest photosynthetic degradation efficiency (DE percentage) of 94% was achieved for MB dye. Ag-TiO2 nanofibers (NFs) have been demonstrated to have exceptional antibacterial activity against Gram-positive bacteria such as Staphylococcus aureus and Gram-negative bacteria E-Coli. Because of these great qualities, it seems likely that the Ag-TiO2 nanofibers (NFs) made could be a great photocatalyst for getting dye pollutants out of wastewater.

Graphene loaded TiO2 submicron spheres scattering layer for efficient dye-sensitized solar cell.

Dye-Sensitized Solar Cells (DSSCs) have attracted great attention due to environmentally friendly low-cost processing, excellent working ability in diffuse light, and potential to meet the power demands of future buildings due the true class of building integrated photovoltaics (BIPV). Nevertheless, DSSCs have relatively low photoconversion efficiency (PCE) due to multiple issues. Several strategies have been employed to enhance its PCE. For instance, bi-layered structure of photoelectrode i.e., mesoporous TiO2 transparent layer with top scattering layer was introduced which scatter light inside on large angles improves the harvesting ability of photoelectrode thus enhanced PCE. However, scattering layer is composed of aggregated small particles which offer sluggish electron transport due to multiple grain boundaries, consequently, unwanted recombination reaction which leads to poor PCE. This issue has been addressed for transparent layer immensely but ignored for scattering layer. Mostly for scattering layer in previous studies novel structures have been proposed to enhance scattering properties and dye adsorption only. Therefore, in this study for the first time presenting dual functional graphene/TiO2 scattering layer in which solvent exfoliated graphene is incorporated in TiO2 submicron spheres which enhanced electron transport properties, while submicron spheres scatter light effectively. Scattering and electron transport characteristics of DSSCs are thoroughly investigated with the function of graphene loading. Electrochemical impedance spectroscopy (EIS) has revealed that diffusion coefficient length and coefficient and conductivity attained maximum value at 0.01 wt%. while other important parameters such as electron lifetime and electron density in conduction band have been improved till 0.020 wt% graphene loading. However, results indicated that with 0.01 w% graphene 33% higher PCE was achieved than without scattering layer and 13% higher than scattering layer without graphene. The depraving in PCE at >0.01 wt% graphene despite of excellent electron transport improvement is attributed to the loss of diffuse reflectance and higher optical absorption by graphene.

Hydrophobic ammonium based ionic liquids for efficient extraction of textile dyes from aqueous media: Extraction study and antibacterial evaluation.

Alizarin red S (ARS) extraction from aqueous medium was carried out using hydrophobic ionic liquids (ILs) containing trioctylammonium cation paired with 4-tert-butylbenzoate ([TOA][Butbenz] (IL1), 4-phenylbutanoate ([TOA][PheBut] (IL2), 3-4-dimethylbenzoate ([TOA][DMbenz] (IL3), naphthoate, ([TOA][Naph]) (IL4), salicylate ([TOA][Sali]) (IL5) and nonanedioate ([TOA]2[Nona]) (IL6). The findings demonstrated that all of the tested ILs were efficient for extracting ARS, however, [TOA]2[Nona] was more effective than others. For the extraction of ARS from the aqueous phase, the effects of various parameters including the initial pH of the dye solution, contact time, ILs to dye volume ratio (VIL:VW), dye concentration, temperature, and salt effect were investigated. The spontaneity of the liquid-liquid extraction of ARS from the aqueous phase to the IL phase was confirmed by thermodynamic parameters. More than 90% of the ARS was extracted from the aqueous phase to the IL phase throughout all experiments. Interaction of selected IL with dyes were confirmed using FTIR analysis. The standard bacterial strains of Escherichia coli (E. coli) ATCC BAA-2471 (gram negative) and Methicillin-resistant Staphylococcus (MRSA) ATCC 43300 (gram positive) were used for evaluating antibacterial activity. The lower dose (250 ppm), the ILs1, 2, 3, 4, 5, and 6 inhibited 0.40, 1.50, 6.50, 1.50, 2.50, and 0.50 mm growth of E. coli, and 4.0, 2.0, 16.50, 0.40, 5.0, and 3.50 mm growth of MRSA, respectively. The experimental findings confirmed that the present ILs can be utilized as an effective solvent for ARS and other dyes extraction from aqueous media.