Influence of mechanochemically fabricated nano-hardystonite reinforcement in polycaprolactone scaffold for potential use in bone tissue engineering: Synthesis and characterization.

Bone tissue engineering (BTE) has gained significant attention for the regeneration of bone tissue, particularly for critical-size bone defects. The aim of this research was first to synthesize nanopowders of hardystonite (HT) through ball milling and then to manufacture composite scaffolds for BTE use out of polycaprolactone (PCL) containing 0, 3, 5, and 10 wt% HT by electrospinning method. The crystallite size of the synthesized HT nanopowders was 42.8 nm. including up to 5 wt% HT into PCL scaffolds resulted in significant improvements, such as a reduction in the fiber diameter from 186.457±15.74 to 150.021±21.99 nm, a decrease in porosity volume from 85.2±2.5 to 80.3±3.3 %, an improvement in the mechanical properties (ultimate tensile strength: 5.7±0.2 MPa, elongation: 47.5±3.5 %, tensile modulus: 32.7±0.9 MPa), an improvement in the hydrophilicity, and biodegradability. Notably, PCL/5%HT exhibited the maximum cell viability (194±14 %). Additionally, following a 4-week of submersion in simulated body fluid (SBF), the constructed PCL/HT composite scaffolds showed a remarkable capacity to stimulate the development of hydroxyapatite (HA), which increased significantly for the 5 wt% HT scaffolds. However, at 10 wt% HT, nanopowder agglomeration led to an increase in the fiber diameter and a decrease in the mechanical characteristics. Collectively, the PCL/5%HT composite scaffolds can therefore help with the regeneration of the critical-size bone defects and offer tremendous potential for BTE applications.

Antibacterial and Virucidal Evaluation of Ultrafine Wire Arc Sprayed German Silver Coatings.

Copper and its alloys are known as antimicrobial agents that can be used in public places; however, pure copper has a low wear resistance and tends to lose its gloss relatively fast and stainless steel is still more desirable because of its mechanical properties and stable appearance. In this research, German silver coatings, a copper-nickel alloy, are studied as a superior alternative for pure copper coatings. German silver coating on mild steel substrates and stainless steel with two different surface roughnesses was prepared and placed into water bath up to 6 months to investigate the corrosion and exposure effects on the antibacterial behavior. A range of techniques was used to study the microstructure, surface morphology and mechanical properties such as microhardness, coating bonding adhesion, surface roughness and wettability of the coating. Colony count method was used to measure the antibacterial properties, and samples were tested against influenza A virus to evaluate the virucidal activity. The coating thickness was around 130 µm and contained 15% pores and oxides with splats forming inside the coating structure. Inside each splat, columnar grains could be seen with an average of 700 nm width and 4 µm length. The bonding strength of the coating was about 15 MPa, the hardness of coatings was about 180 HV, and the average surface roughness of the as-sprayed samples was about 10 µm. German silver coatings can destroy both Staphylococcus aureus and Escherichia coli by more than 90% after 6 h of exposure time, and it also has a high-level of virucidal activity against influenza A virus after 2 h exposure time. Antibacterial behavior did not show any significant changes after 6 months of immersing samples in water bath. Thus, thermally sprayed German silver coatings exhibited silvery color for a long period of time, while its antimicrobial efficiency was comparable to pure copper coatings. Supplementary Information: The online version contains supplementary material available at 10.1007/s11666-022-01528-4.

A three-dimensional nerve guide conduit based on graphene foam/polycaprolactone.

In this study, a novel nerve guide conduit was developed, based on a three-dimensional (3D) graphene conductive core grown, by chemical vapor deposition (CVD) coupled with a polycaprolactone (PCL) polymer coating. Firstly, the monolithic 3D-graphene foam (3D-GF) was synthesized on Ni foam templates via inductive heating CVD, subsequently, Ni/Graphene samples were dipped successively in PCL and cyclododecane (CDD) solutions prior to the removal of Ni from the 3D-GF/PCL scaffold in FeCl3. Our results showed that the electrical conductivity of the polymer composites reached to 25 S.m-1 after incorporation of 3D-GF. Moreover, the mechanical properties of 3D-GF/PCL composite scaffold were enhanced with respect to the same geometry of PCL scaffolds. The wettability, surface porosity, and morphology did not show any significant changes, while the PC12 cell proliferation and extension were increased for the developed 3D-GF/PCL nanocomposite. It can be concluded that 3D-GF/PCL nanocomposites could be good candidates to utilize as a versatile system for the engineering of peripheral nerve tissue.

Microstructure and Corrosion Characterization of a MgO/Hydroxyapatite Bilayer Coating by Plasma Electrolytic Oxidation Coupled with Flame Spraying on a Mg Alloy.

Thermally sprayed hydroxyapatite coatings are one of the main strategies to improve the bioactivation of metal implants. However, the naturally low corrosion resistance of these coatings is the main challenge for their use. In this study, plasma electrolytic oxidation (PEO) was used to create an intermediate layer. The anodization process was used for comparison. According to the polarization curves, the PEO layer was more effective than the anodized layer in reducing the corrosion current density (I corr of 0.05 × 10-9 A/cm2 vs I corr of 0.05 A/cm2). The results of electrochemical impedance spectroscopy showed higher resistance of the sample with a PEO interlayer than that of the sample with an anodized interlayer. The results of the hydrogen evolution test revealed that the PEO layer as a middle layer served as the main barrier for reducing the magnesium corrosion rate, especially during the initial immersion time.

Thermochemical CO2 splitting performance of perovskite coated porous ceramics.

In this paper, we investigate the redox performance of perovskite coated porous ceramics with various architectures. For this purpose, reticulated porous ceramics (RPCs) in three different pore sizes (5, 12, 75 ppi) were fabricated to represent a broad range of structures and pore sizes. The perovskite material is based on lanthanum manganite and was synthesized and doped with Ca and Al through the Pechini method. Using a deep coating method, the surface of RPC substrates was modified by a thin-film coating with a thickness of ∼15 µm. We evaluated the CO2 conversion performance of the developed materials in a gold-image IR furnace. X-ray micro-computed tomography along with SEM/EDX were utilized in different steps of the work for a thorough study of the bulk and surface features. Results reveal that the intermediate pore size of 12 ppi delivers the maximum perovskite loading with a high degree of coating homogeneity and connectivity while CO2 conversion tests showed the highest CO yield for 75 ppi. Our results show that the extreme conditions inside the furnace combined with the flow of gaseous phases cause the RPCs to shrink in length up to 23% resulting in the alteration of the pore phase and elimination of small pores reducing the total specific surface area. Further our results reveal an important mechanism resulting in the inhibition of CO2 conversion where the perovskite coating layer migrates into the matrix of the RPC frame.