Wide bandgap oxidized graphenes have garnered particular interest among the materials explored for these applications because of their exceptional semiconducting and optical properties. This study aims to investigate the tunability of the related properties in reduced graphene oxide (rGO) for potential use in energy conversion, storage, and optoelectronic devices. To accomplish this, we scrutinized crucial parameters of the synthesis process such as reduction time and temperature. Our findings demonstrate that controlling these parameters makes it possible to customize the optical bandgap of reduced graphene oxide within a range of roughly 2.2 eV-1.6 eV. Additionally, we observed that reduced graphene oxide has strong and superior absorption in the visible region, which is attributable to the existence of OFGs and defects. Notably, our results indicate that the absorption coefficients of reduced graphene oxide are up to almost three times higher (7426 ml mg-1 m-1) than those observed in dispersions of exfoliated graphene and graphene oxide (GO). To complement our findings, we employed several spectroscopic and morphological characterizations, including scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), and electrical measurements. The implications of our results are significant for the development and design of future semiconductors for energy conversion and optoelectronic applications.
RESUMEN
In this study, we investigate how changing important synthesis-related parameters can affect and control the optical characteristics of graphene oxide (GO) and reduced graphene oxide (rGO). These parameters include drying time and reduction time at two different temperatures. We obtain an understanding of their impact on optical transitions, optical bandgap, absorption coefficient, and absorbance spectrum width by analyzing these factors. Accordingly, GO has an optical bandgap of about 4 eV, which is decreased by the reduction process to 1.9 eV. Both GO and rGO display greater absorption in the visible spectrum, which improves photon capture and boosts efficiency in energy conversion applications. Additionally, our results show that GO and rGO have higher absorption coefficients than those previously reported for dispersions of exfoliated graphene. Defects in GO and rGO, as well as the presence of functional oxygen groups, are the main contributors to this increased absorption. Several measurements are carried out, including spectroscopic and morphological studies, to further support our findings.
RESUMEN
The development of efficient energy storage systems is critical in the transition towards sustainable energy solutions. In this context, the present work investigates the viability of using orange juice, as a promising and sustainable precursor, for the synthesis of activated carbon electrodes for supercapacitor technologies. Through the carbonization-activation process and controlling the preparation parameters (KOH ratio and activation time), we have tailored the specific surface area (SSA) and pore size distribution (PSD) of the resulting carbon materials-crucial parameters that support supercapacitive performance. Several spectroscopic, morphological, and electrochemical techniques are used to characterize the obtained carbon materials. In particular, our optimization efforts revealed that a 5:1 KOH ratio with an activation time up to 120 min produced the highest SSA of about 2203 m2/g. Employing these optimal conditions, we fabricated symmetric coin cell supercapacitors using Na2SO4 as the electrolyte, which exhibited interesting specific capacitance (~56 F/g). Durability testing over 5000 cycles sustained the durability of the as-made activated carbon electrodes, suggesting an excellent retention of specific capacitance. This study not only advances the field of energy storage by introducing a renewable material for electrode fabrication but also contributes to the broader goal of waste reduction through the repurposing of food byproducts.
RESUMEN
Graphene oxide (GO) and its reduced form, reduced graphene oxide (rGO), are among the most predominant graphene derivatives because their unique properties make them efficient adsorbent nanomaterials for water treatment. Although extra-functionalized GO and rGO are customarily employed for the removal of pollutants from aqueous solutions, the adsorption of heavy metals on non-extra-functionalized oxidized graphenes has not been thoroughly studied. Herein, the adsorption of mercury(II) (Hg(II)) on eco-friendly-prepared oxidized graphenes is reported. The work covers the preparation of GO and rGO as well as their characterization. In a further stage, the description of the adsorption mechanism is developed in terms of the kinetics, the associated isotherms, and the thermodynamics of the process. The interaction between Hg(II) and different positions of the oxidized graphene surface is explored by DFT calculations. The study outcomes particularly demonstrate that pristine rGO has better adsorbent properties compared to pristine GO and even other extra-functionalized ones.
RESUMEN
Reduced graphene oxide (rGO) is one of the most well-known graphene derivatives, which, due to its outstanding physical and chemical properties as well as its oxygen content, has been used for wastewater treatment technologies. Particularly, extra functionalized rGO is widely preferred for treating wastewater containing dyes or heavy metals. Nevertheless, the use of non-extra functionalized (pristine) rGO for the removal of cationic pollutants is not explored in detail or is ambiguous. Herein, pristine rGO-prepared by an eco-friendly protocol-is used for the removal of cationic pollutants from water, i.e., methylene blue (MB) and mercury-(II) (Hg-(II)). This work includes the eco-friendly synthesis process and related spectroscopical and morphological characterization. Most importantly, the investigated rGO shows an adsorption capacity of 121.95 mg g-1 for MB and 109.49 mg g-1 for Hg (II) at 298 K. A record adsorption time of 30 min was found for MB and 20 min for Hg (II) with an efficiency of about 89% and 73%, respectively. The capture of tested cationic pollutants on rGO exhibits a mixed physisorption-chemisorption process. The present work, therefore, presents new findings for cationic pollutant adsorbent materials based on oxidized graphenes, providing a new perspective for removing MB molecules and Hg(II) ions.
RESUMEN
Graphene oxide (GO) exhibits different properties from those found in free-standing graphene, which mainly depend on the type of defects induced by the preparation method and post-processing. Although defects in graphene oxide are widely studied, we report the effect of drying time in GO and how this modifies the presence or absence of edge-, basal-, and sp3-type defects. The effect of drying time is evaluated by Raman spectroscopy, UV-visible spectroscopy, and transmission electron microscopy (TEM). The traditional D, G, and 2D peaks are observed together with other less intense peaks called the D', D*, D**, D+G, and G+D. Remarkably, the D* peak is activated/deactivated as a direct consequence of drying time. Furthermore, the broad region of the 2D peak is discussed as a function of its deconvoluted 2D1A, 2D2A, and D+G bands. The main peak in UV-visible absorption spectra undergoes a redshift as drying time increases. Finally, TEM measurements demonstrate the stacking of exfoliated GO sheets as the intercalated (water) molecules are removed.
RESUMEN
Porous carbon materials are currently subjected to strong research efforts mainly due to their excellent performances in energy storage devices. A sustainable process to obtain them is hydrothermal carbonization (HTC), in which the decomposition of biomass precursors generates solid products called hydrochars, together with liquid and gaseous products. Hydrochars have a high C content and are rich with oxygen-containing functional groups, which is important for subsequent activation. Orange pomace and orange peels are considered wastes and then have been investigated as possible feedstocks for hydrochars production. On the contrary, orange juice was treated by HTC only to obtain carbon quantum dots. In the present study, pure orange juice was hydrothermally carbonized and the resulting hydrochar was filtered and washed, and graphitized/activated by KOH in nitrogen atmosphere at 800 °C. The resulting material was studied by transmission and scanning electron microscopy, Raman spectroscopy, X-ray photoelectron spectroscopy, X-ray diffraction, and nitrogen sorption isotherms. We found porous microspheres with some degree of graphitization and high nitrogen content, a specific surface of 1725 m2/g, and a pore size distribution that make them good candidates for supercapacitor electrodes.