RESUMEN
Asymmetric polyphenylsulfone (PPSU) membranes were fabricated by a non-solvent induced phase inversion method. Glycerin and silica nanoparticles were added into the polymer solution to investigate their effects on the material properties and gas separation performance of prepared membranes. The morphology and structure of PPSU membranes were analyzed by scanning electron microscopy (SEM), the surface roughness of the selective layer was analyzed by atomic force microscopy (AFM), and the surface free energy was calculated based on the contact angle measurements by using various solvents. The gas separation performance of PPSU membranes was estimated by measuring the permeability of CO2 and CH4. The addition of glycerin as a nonsolvent into the polymer solution changed the cross-section structure from finger-like structure into sponge-like structure due to the delayed liquid-liquid demixing process, which was confirmed by SEM analysis. The incorporation of silica nanoparticles into PPSU membranes slightly increased the hydrophilicity, which was confirmed by water contact angle results. PPSU membrane fabricated from the polymer solution containing 10 wt.% glycerin showed the best CO2/CH4 selectivity of 3.86 and the CO2 permeability of 1044.01 Barrer. Mixed matrix PPSU membrane containing 0.1 wt.% silica nanoparticles showed the CO2/CH4 selectivity of 3.16 and the CO2 permeability of 1202.77 Barrer.
RESUMEN
Polyether block amide (PEBA) nanocomposite membranes, including Graphene (GA)/PEBA membranes are considered to be a promising emerging technology for removing CO2 from natural gas and biogas. However, poor dispersion of GA in the produced membranes at industrial scale still forms the main barrier to commercialize. Within this frame, this research aims to develop a new industrial approach to produce GA/PEBA granules that could be used as a feedstock material for mass production of GA/PEBA membranes. The developed approach consists of three sequential phases. The first stage was concentrated on production of GA/PEBA granules using extrusion process (at 170-210 °C, depending on GA concentration) in the presence of Paraffin Liquid (PL) as an adhesive layer (between GA and PEBA) and assisted melting of PEBA. The second phase was devoted to production of GA/PEBA membranes using a solution casting method. The last phase was focused on evaluation of CO2/CH4 selectivity of the fabricated membranes at low and high temperatures (25 and 55 °C) at a constant feeding pressure (2 bar) using a test rig built especially for that purpose. The granules and membranes were prepared with different concentrations of GA in the range 0.05 to 0.5 wt.% and constant amount of PL (2 wt.%). Also, the morphology, physical, chemical, thermal, and mechanical behaviors of the synthesized membranes were analyzed with the help of SEM, TEM, XRD, FTIR, TGA-DTG, and universal testing machine. The results showed that incorporation of GA with PEBA using the developed approach resulted in significant improvements in dispersion, thermal, and mechanical properties (higher elasticity increased by ~10%). Also, ideal CO2/CH4 selectivity was improved by 29% at 25 °C and 32% at 55 °C.