Analytical Calculation of Relationship Temperature and Fatigue and Creep Strength Based on Thermal Activation.

The purpose of this study was to formulate a mathematical expression for the temperature dependence of adhesive strength using various parameters. Adhesive structures are typically exposed to a broad temperature range, spanning from low to high temperatures; therefore, understanding how their strength depends on temperature is crucial. The strength was measured through tensile, fatigue, and creep tests at temperatures ranging from -60 °C to 135 °C. The properties of these test types were thoroughly investigated by analyzing the strength of the test results from a thermal activity perspective. The results demonstrate that there is a clear relationship between temperature and strength. The intensity decreased with temperature according to the exponential function and could be accurately represented using the parameters of thermal activity. The temperature at which the strength begins to decrease in the fatigue test was higher than in the static tests. Consequently, we were able to accurately express the relationship between the temperature and intensity using certain parameters. Few studies successfully developed a precise nonlinear relationship between temperature and intensity using approximate expressions.

Outstanding Robust Photo- and Thermo-Electric Applications with Stabilized n-Doped Carbon Nanotubes by Parylene Coating.

Stabilization techniques for n-doped carbon nanotubes (CNTs) are essential for the practical use of CNT devices. However, none of the reported n-dopants have sufficient robustness in a practical environment. Herein, we report a highly stable technique for fabricating n-doped CNT films. We elucidate the mechanism by which air stability can be achieved by completely covering CNTs with n-dopants to prevent oxidation; consequently, the stability is lost when exposed to scratches or moisture. Therefore, we introduce parylene as a protective layer for n-doped CNTs and achieve air stability for more than 365 d. Moreover, we demonstrate outstanding robust thermo-electric power generation from strong acids, alkalis, and alcohols, which cannot be realized with conventional air-stable n-dopants. The proposed stabilization technique is versatile and can be applied to various n-dopants. Thus, it is expected to be a key technology in the practical application of CNT devices.

Creep Crack Growth Behavior during Hot Water Immersion of an Epoxy Adhesive Using a Spring-Loaded Double Cantilever Beam Test Method.

Double cantilever beam (DCB) tests were conducted by immersing the specimens in temperature-controlled water while applying a creep load using a spring. By introducing a data reduction scheme to the spring-loaded DCB test method, it was confirmed that only a single parameter measurement was sufficient to calculate the energy release rate (ERR). Aluminum alloy substrates bonded with an epoxy adhesive were used, and DCB tests were performed by changing the initial load values, spring constants, and immersion temperatures for two types of surface treatment. The initial applied load and spring constant had no effect on the ERR threshold. In contrast, the threshold decreased with the increasing immersion temperature, but even in the worst case, it was 15% of the critical ERR in the static tests. Using the creep crack growth relationship, it was revealed that there were three phases of creep immersion crack growth in the adhesive joints, and each phase was affected by the temperature. The spring-loaded DCB test method has great potential for investigating the combined effects of creep, moisture, and temperature, and this study has demonstrated the validity of the test method. The long-term durability of adhesive joints becomes increasingly important, and this test method is expected to become widespread.