RESUMEN
The delamination of ultra-high molecular weight polyethylene (UHMWPE) in artificial joints is a major cause limiting the long-term clinical results of arthroplasty. However, the conventional test method using simple reciprocation to evaluate the delamination resistance of UHMWPE materials has insufficient detection sensitivity. To reproduce delamination, the unconformity contact must be maintained throughout the test so that the maximum stress is generated below the surface. Therefore, a test method that applies a U-shaped motion comprising two long-linear and one short linear sliding motion was developed. The sensitivity, robustness, and reproducibility of the U-shaped delamination test were investigated and compared with the traditional test method. The traditional test method could reproduce delamination only in materials that had degraded considerably, whereas the U-shaped delamination test could reproduce delamination in a wide range of materials, demonstrating its superior sensitivity. Additionally, using a higher load helped accelerate the test without affecting the test results. The optimal length of the short linear sliding motion was confirmed to be 1 mm. Finally, the inter-laboratory reproducibility of the U-shaped delamination test was confirmed using the round-robin test. The U-shaped delamination test demonstrates high sensitivity, robustness, and reproducibility and contributes to the selection and development of UHMWPE materials and artificial joints with a lower risk of delamination.
Asunto(s)
Ensayo de Materiales , Polietilenos , Polietilenos/química , Reproducibilidad de los Resultados , Prótesis Articulares , Pruebas Mecánicas , Artroplastia de Reemplazo/instrumentaciónRESUMEN
Taper fretting corrosion is considered a potentially limiting factor for total hip arthroplasty longevity. Recently, attention has been focused on new materials for ceramic femoral heads, for example, zirconia-toughened alumina (ZTA), since they have an alternative bearing surface that can improve the wear resistance. Moreover, ceramics have high chemical stability and corrosion resistance. In this study, we evaluated the effects of ZTA and Co-Cr-Mo alloy femoral heads on their taper fretting and/or corrosion characteristics under a controlled hip simulator test. After the test, less fretting and corrosion were observed in the taper surface of the trunnion against the ZTA femoral head than for that against the Co-Cr-Mo alloy femoral head. In addition, corrosion damages were only observed in the lateral-distal taper surface (noncontact area) of the trunnion in the Co-Cr-Mo alloy femoral head group. The ZTA femoral head group also eliminated the potential for Co ion release into the lubricants from taper corrosion, reducing the possibility of adverse local tissue inflammatory responses. In conclusion, ZTA femoral heads showed markedly less fretting corrosion compared to Co-Cr-Mo alloy femoral heads and have a lower potential for metal ion release. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 106B: 2815-2826, 2018.