Nanoporous Gold-Based Biofuel Cells on Contact Lenses.

A lactate/O2 enzymatic biofuel cell (EBFC) was prepared as a potential power source for wearable microelectronic devices. Mechanically stable and flexible nanoporous gold (NPG) electrodes were prepared using an electrochemical dealloying method consisting of a pre-anodization process and a subsequent electrochemical cleaning step. Bioanodes were prepared by the electrodeposition of an Os polymer and Pediococcus sp. lactate oxidase onto the NPG electrode. The electrocatalytic response to lactate could be tuned by adjusting the deposition time. Bilirubin oxidase from Myrothecium verrucaria was covalently attached to a diazonium-modified NPG surface. A flexible EBFC was prepared by placing the electrodes between two commercially available contact lenses to avoid direct contact with the eye. When tested in air-equilibrated artificial tear solutions (3 mM lactate), a maximum power density of 1.7 ± 0.1 µW cm-2 and an open-circuit voltage of 380 ± 28 mV were obtained, values slightly lower than those obtained in phosphate buffer solution (2.4 ± 0.2 µW cm-2 and 455 ± 21 mV, respectively). The decrease was mainly attributed to interference from ascorbate. After 5.5 h of operation, the EBFC retained 20% of the initial power output.

Immobilization of Redox Enzymes on Nanoporous Gold Electrodes: Applications in Biofuel Cells.

Nanoporous gold (NPG) electrodes were prepared by dealloying sputtered gold:silver alloys. Electrodes of different thicknesses and pore sizes areas were prepared by varying the temperature and duration of the dealloying procedure; these were then used as supports for FAD-dependent glucose dehydrogenase (GDH) (Glomorella cingulata) and bilirubin oxidase (BOx) (Myrothecium verrucaria). Glucose dehydrogenase was immobilized by drop-casting a solution of the enzyme with an osmium redox polymer together with a crosslinked polymer, whereas bilirubin oxidase was attached covalently through carbodiimide coupling to a diazonium-modified NPG electrode. The stability of the bilirubin-oxidase-modified NPG electrode was significantly improved in comparison with that of a planar gold electrode. Enzyme fuel cells were also prepared; the optimal response was obtained with a BOx-modified NPG cathode (500 nm thickness) and a GDH-modified anode (300 nm), which generated power densities of 17.5 and 7.0 µW cm-2 in phosphate-buffered saline and artificial serum, respectively.