RESUMEN
This work reports the main conclusions of a study on the mechanical behavior of concrete under ISO 834 fire with different cooling methods. The aim of this research was to provide reliable data for the analysis of structures damaged by fire. The experimental program used cylindrical concrete test specimens subjected to ISO 834 heating in a furnace up to maximum gas temperatures of 400, 500, 600, 700, and 800 °C. The compressive strength was measured in three situations: (a) at the different temperature levels reached in the furnace; (b) after a natural cooling process; and (c) after aspersion with water at ambient temperature. The results indicate that the concrete residual compressive strength is fairly dependent on the maximum temperature reached in the furnace and revealed that concrete of a lower strength preserved relatively higher levels of strength. The cooling method significantly influenced the strength, albeit at a lower intensity. In all cases, the residual strength remained in the range of 38% to 67% of the strength at ambient temperature. The statistical analysis showed that the data obtained by the experimental program are significant and confirmed the influence of the conditions imposed on the residual strength.
RESUMEN
The present study evaluated the mechanical behaviour of thin high-performance cementitious composite slabs reinforced with short steel fibres. For this purpose, slabs with 1%, 3% and 5% vol. of steel fibres were moulded using the slurry infiltration method. Fibres concentrated in the region subjected to traction during bending stresses. After curing for 28 days, all slabs underwent flexural testing. The slabs with 5% fibre showed significantly higher flexural strength, deflection and toughness compared to those of the control group without reinforcement. The dense fibre distribution, resulting from the production process, led to profiles with multiple random cracks in the region of failure of the slabs as the fibre content increased. The results of the statistical analysis showed the intensity of the correlation between the variables and revealed that the increase of the fibre content significantly influenced the parameters of mechanical behaviour (load, flexural strength, deflection, toughness and toughness factor). Images obtained by optical microscopy aided in understanding the fibre-matrix interface, showing the bonding surface between the constituents of the composite.