RESUMEN
Composites comprising copper-doped zinc sulfide phosphor microparticles embedded in polydimethylsiloxane (ZnS:Cu-PDMS) have received significant attention over the past decade because of their bright and durable mechanoluminescence (ML); however, the underlying mechanism of this unique ML remains unclear. This study reports empirical and theoretical findings that confirm this ML is an electroluminescence (EL) of the ZnS:Cu phosphor induced by the triboelectricity generated at the ZnS:Cu microparticle-PDMS matrix interface. ZnS:Cu microparticles that exhibit bright ML are coated with alumina, an oxide with strong positive triboelectric properties; the contact separation between this oxide coating and PDMS, a polymer with strong negative triboelectric properties, produces sufficient interfacial triboelectricity to induce EL in ZnS:Cu microparticles. The ML of ZnS:Cu-PDMS composites varies on changing the coating material, exhibiting an intensity that is proportional to the amount of interfacial triboelectricity generated in the system. Finally, based on these findings, a mechanism that explains the ML of phosphor-polymer elastic composites (interfacial triboelectric field-driven alternating-current EL model) is proposed in this study. It is believed that understanding this mechanism will enable the development of new materials (beyond ZnS:Cu-PDMS systems) with bright and durable ML.
RESUMEN
We demonstrate wide colour tunability of polydimethylsiloxane-based alternating-current-driven electroluminescent devices with intrinsically stretchable characteristics achieved by simply modulating the electrical frequency. By employing both a screen-printed emitting layer and frequency-dependent colour tuning of ZnS:Cu-based phosphors, we demonstrate various coloured patterned images in a single device. We also show enhanced colour-tuning performance by mixing multi-colour phosphors, which results in a broad range of available coordinates in colour space. We believe that our demonstrated method could be used for manipulating broader colour expression as well as in various applications involving stretchable devices.
RESUMEN
We report an optical film with electrically tunable birefringence in which the liquid crystals (LCs), mixed with the host polymer, form long-range ordering. The film was prepared through polymerization without phase separation between the LCs and polymers. Driving voltage below 30 V for full switching of birefringence is achieved in a 6 µm-thick film. Electro-optical investigations for the film suggest that the long-range ordering of the LCs mixed in the film caused by polymerization lead to rotations of the LCs as well as optical anisotropy in the film. These films with electrically tunable birefringence could have applications as flexible light modulators and phase retardation films for 2D-3D image switching.
RESUMEN
The prospective application of luminescence to imaging devices is shown using a combination of color-tunable and patternable mechanoluminescent materials. A white light source is demonstrated by using an alternative color tuning method, induced under high vibration conditions. As the implementation is fairly straightforward, it is expected that the present results will find a number of potential uses in current industrial applications.
RESUMEN
The polymer-dispersed liquid crystal (PDLC) was used as a dielectric layer of electroluminescent (EL) device to provide multi-function of electroluminescence and electro-optic shutter. A 50 µm-thick PDLC layer was formed between a transparent electrode and a ZnS:Cu phosphor layer. The electro-optic properties of the EL device were not distorted by the introduction of the PDLC layer. The extraction efficiency of luminescence was improved by more than 14% by PDLC layer. The transmittance of the PDLC was also founded not to be degraded significantly by excitation frequency. Therefore, the electroluminescence of the device was ignited by excitation frequency at a given voltage for full transparency of the PDLC. This device has great potential for applications in transparent displays with the function of a privacy window.