RESUMEN
A dentin biomodification strategy with selective proanthocyanidin (PAC)-enriched extracts reinforces dentin and dentin-resin interfaces. Enrichment of the extracts according to the degree of polymerization allows exploration of bioactive principles of PACs and structure-activity relationships. This study investigated the sustained dentin matrix biomodification and dentin-resin bioadhesion of 2 fractions consisting exclusively of B-type PAC dimers with or without a single galloyl motif (specifically, DIMERG and DIMERNG) and their precursor material, enriched grape seed extract (e-GSE; Vitis vinifera). The biomodification potential was determined by long-term evaluation of the apparent modulus of elasticity and collagen solubility (hydroxyproline release). Chemical characterization of the dentin matrix was performed by attenuated total reflectance-Fourier-transform infrared spectroscopy. The bioadhesive properties were assessed by a microtensile bond strength test at different time points, and macro-hybrid layers were produced to verify the degree of conversion of the adhesive resin. Fractions consisting of DIMERG, DIMERNG, and their precursor, e-GSE, increased the modulus of elasticity at all time points and reduced collagen degradation. Specimens treated with DIMERNG remained stable throughout 12 mo of storage, whereas a significant drop in the modulus of elasticity was observed for the DIMERG and e-GSE groups at 6 mo. The fractions and precursor did not affect the degree of resin conversion at the hybrid layer. Changes in infrared resonances corresponding to collagen cross-links in the dentin matrix occurred for all treatments. Higher bond strength was observed for dentin treated with e-GSE as compared with DIMERG and DIMERNG; all biointerfaces remained stable after 12 mo. Nongalloylated PACs mediate stable dentin biomodification, which includes protective activity against collagen degradation and reinforcement of the anchoring dentin matrix. Collectively, PACs with a higher degree of oligomerization offer a robust bioadhesion between the hydrophilic dentin matrix and the hydrophobic adhesive.
Asunto(s)
Recubrimiento Dental Adhesivo , Dentina , Extracto de Semillas de Uva , Proantocianidinas , Colágeno , Cementos Dentales , Recubrimientos Dentinarios , Ensayo de Materiales , Proantocianidinas/farmacología , Resistencia a la TracciónRESUMEN
OBJECTIVE: To evaluate the color stability and surface roughness of 3 dental composites subjected to cigarette smoke and brushing. METHODS: Twenty specimens were prepared for each type of restorative material used: nanohybrid (Tetric N-Ceram); hybrid (Z250-3M ESPE) and silorane-based microhybrid (Filtek P90-3M ESPE), which were divided into 2 groups (n=10), according to the type of finishing/polishing received: Group 1 - papers with decreasing abrasive grit and Group 2 - polyester matrix (without polishing). After initial readouts of color (Easy Shade-VITA) and surface roughness (SJ-201P Mitutoyo), specimens were subjected to action of smoke from 20 cigarettes, (Marlboro Red-Philip Morris). After each cigarette, the samples were submitted to brushing in a standardised device. After this, final readouts were taken to calculate change in color (ΔE and ΔL) and roughness (ΔRa), which were statistically analysed (2-way ANOVA, Bonferroni, and Student's-t tests respectively, p<0.05). RESULTS: Tetric N-Ceram presented color change at clinically unacceptable levels (ΔE>3.3) when the polyester strip was used for finishing, a result differing (p<0.05) from those of the other composites, which presented no difference between them (p>0.05). Unpolished composites presented higher Ra values than those that were polished (p<0.05), with exception of the silorane based composite. CONCLUSION: Absence of polishing increases cigarette capacity to stain composites and surface roughness of composites, with exception of the silorane based type.