RESUMEN
Saliva substitutes with enhanced dentin remineralization properties were expected to help manage caries progression in patients with xerostomia. This in vitro study examined the rheological properties and remineralization action of experimental saliva substitutes containing propolis extract and aloe vera extract on demineralized dentin. Four experimental saliva substitutes were formulated with varying concentrations of propolis extract (P) and aloe vera extract (A) were prepared. A commercial saliva substitute (Biotene Oral Rinse) was used as a commercial comparison. The rheological properties and viscosity of these materials were measured using a strain-controlled rheometer (n = 3). The remineralizing actions of saliva substitutes on demineralized dentin after 2 weeks were determined using ATR-FTIR and SEM-EDX (n = 8). The results were expressed as a percentage increase in the mineral-to-matrix ratio. Biotene demonstrated a significantly higher viscosity (13.5 mPa·s) than experimental saliva substitutes (p<0.05). The addition of extracts increased the viscosity of the saliva substitutes from 4.7 mPa·s to 5.2 mPa·s. All formulations showed minimal shear thinning behavior, which was the viscoelastic properties of natural saliva. The formulation containing 5 wt% of propolis exhibited the highest increase in the median mineral-to-matrix ratio (25.48%). The SEM-EDX analysis revealed substantial mineral precipitation in demineralized dentin, especially in formulations with 5 wt% or 2.5 wt% of propolis. The effect of the aloe vera extract was minimal. The addition of propolis and aloe vera extracts increased the viscosity of saliva substitutes. the addition of propolis for 2.5 or 5 wt% to saliva substitutes increased mineral apatite precipitation and tubule occlusion. To conclude, the saliva substitute containing propolis extract demonstrated superior remineralizing actions compared with those containing only aloe vera extract.
Asunto(s)
Aloe , Dentina , Extractos Vegetales , Própolis , Reología , Saliva Artificial , Própolis/química , Própolis/farmacología , Aloe/química , Extractos Vegetales/química , Extractos Vegetales/farmacología , Saliva Artificial/química , Dentina/química , Dentina/efectos de los fármacos , Humanos , Viscosidad , Remineralización Dental/métodos , Espectroscopía Infrarroja por Transformada de FourierRESUMEN
Silver diamine nitrate (SDN) is expected to help control caries similar to silver diamine fluoride (SDF). The aim of this study was to determine the mineral precipitation in demineralized dentin and the cytotoxicity of SDN and SDF to dental pulp cells. Demineralized dentin specimens were prepared, and SDF, SDN, or water (control) was applied. The specimens were then remineralized in simulated body fluid for 2 weeks. The mineral precipitation in the specimens was examined using FTIR-ATR, SEM-EDX, and synchrotron radiation X-ray tomographic microscopy (SRXTM). Additionally, the cytotoxicity of SDF and SDN to human dental pulp stem cells was analyzed using an MTT assay. The increase in FTIR spectra attributable to apatite formation in demineralized dentin in the SDF group was significantly higher compared to the SDN and control groups (p < 0.05). Dentinal tubule occlusion by the precipitation of silver salts was detected in both SDF and SDN groups. The mineral density as shown in SRXTM images and cytotoxicity of both SDN and SDF groups were comparable (p > 0.05). In conclusion, SDF demonstrated superior in vitro apatite formation compared to SDN. However, the degree of mineral precipitation and cytotoxic effects of both were similar.
RESUMEN
Silver diamine fluoride (SDF) is a cost-effective method for arresting active dental caries. However, the limited cooperation of patients may lead to an SDF application time that is shorter than the recommended 1-3 min for carious lesions. Therefore, the aim of this study was to assess the effect of different application times of SDF on the degree of mineral precipitation in demineralized dentin. Demineralized dentin specimens from permanent maxillary molars were treated by applying 38% SDF for 30, 60, or 180 s. Water was applied in the control group. The specimens were immersed in simulated body fluid for 2 weeks, and the mineral precipitation in demineralized dentin was then analyzed using FTIR-ATR, SEM-EDX, and synchrotron radiation X-ray tomographic microscopy (SRXTM). The FTIR-ATR results showed a significant increase in mineral precipitation in the 180 s group after 1 week. However, after 2 weeks, the SRXTM images indicated comparable mineral density between the 30, 60, and 180 s groups. The precipitation of silver chloride and calcium phosphate crystals that occluded dentinal tubules was similar in all experimental groups. In conclusion, an application time of either 30, 60, or 180 s promoted a comparable degree of mineral precipitation in demineralized dentin.