Exploring the diverse performance of nickel and cobalt spinel ferrite nanoparticles in hazardous pollutant removal and gas sensing performance.

A simple sol-gel combustion process was employed for the creation of MFe2O4 (M=Ni, Co) nanoparticles. The synthesized nanoparticles, acting as both photocatalysts and gas sensors, were analyzed using various analytical techniques. MFe2O4 (M=Ni, Co) material improved the degradation of methylene blue (MB) under UV-light irradiation, serving as an enhanced electron transport medium. UV-vis studies demonstrated that NiFe2O4 achieved a 60% degradation, while CoFe2O4 nanostructure exhibited a 76% degradation efficacy in the MB dye removal process. Furthermore, MFe2O4 (M=Ni, Co) demonstrated chemosensitive-type sensor capabilities at ambient temperature. The sensor response and recovery times for CoFe2O4 at a concentration of 100 ppm were 15 and 20, respectively. Overall, the synthesis of MFe2O4 (M=Ni, Co) holds the potential to significantly improve the photocatalytic and gas sensing properties, particularly enhancing the performance of CoFe2O4. The observed enhancements make honey MFe2O4 (M=Ni, Co) a preferable choice for environmental remediation applications.

Cobalt oxide coupled with graphitic carbon nitride composite heterojunction for efficient Z-scheme photocatalytic environmental pollutants degradation performance.

The Co3O4/g-C3N4 Z-scheme composite heterojunction has been effectively built in a facile sonication-assisted hydrothermal manner. The as-synthesized optimal 0.2 M Co3O4/g-C3N4 (GCO2) composite photocatalysts (PCs) revealed admirable degradation efficiency towards methyl orange (MO, 65.1%) and methylene blue (MB, 87.9%) organic pollutant compared with bare g-C3N4 within 210 min under light irradiation. Besides, the features of investigating structural, morphological and optical properties have evidence that the unique decoration effect of Co3O4 nanoparticles (NPs) on the g-C3N4 structure with intimate interface heterojunction of well-matched band structures noticeably facilitates the photo-generated charge transport/separation efficiency, reduces the recombination rates and widens the visible-light fascination which could advantageous to upgrading photocatalytic action with superior redox ability. Especially, the probable Z-scheme photocatalytic mechanism pathway is also elucidated in detail based on the quenching results. Hence, this work delivers a facile and hopeful candidate for contaminated water remediation via visible-light photocatalysis over the efficient g-C3N4-based catalysts.

Biodegradable composites from poly(butylene adipate-co-terephthalate) with carbon nanoparticles: Preparation, characterization and performances.

The development of composites for food packaging that have good mechanical and antimicrobial characteristics is still a major challenge. In applications like food packaging, the usage of poly (butylene adipate-co-terephthalate) (PBAT), which has an adversative effect on the environment and reduces petroleum resources, has grown widespread. The present work reveals PBAT composites reinforced with CNPs at a few percentages up to 5.0 wt %. The PBAT/CNPs composites were produced using the solvent casting method. The results of TGA studies, CNPs significantly enhanced the thermal stability of composites using PBAT. The mechanical strength of the PBAT composites was improved by increasing CNPs concentration. Tensile strength increased from 7.38 to 10.22 MPa, respectively. The oxygen transmission rate (OTR) decreased with increasing the CNPs concentrations. The barrier properties (H2O and O2) of PBAT were improved by the presence of CNPs. WVTR was calculated to be 108.6 ± 1.8 g/m2/day for PBAT. WVTR reduced when CNPs concentration in PBAT increased. The PCN-5.0 film sample had the lowest WVTR value, 34.1 ± 3.1 g/m2/day. For PCN-3.0, WVTR dropped by 45.39%, indicating and even with a 3.0 wt% loading of CNPs in PBAT, the rise is noticeable. Contact angle measurements indicate that PBAT/CNPs composites becomes hydrophobic after reinforcing. Gram-positive (S. aureus) and Gram-negative (E. coli) food-borne pathogenic microorganisms showed enhanced antimicrobial activity against the developed PBAT composites. The carrot pieces preserved their freshness for an extended period of 12 days while packaged in the PBAT/CNPs composite film, indicating that the film is an effective and excellent packaging for food materials.

Synergistic influence of vanadium pentoxide-coupled graphitic carbon nitride composite for photocatalytic degradation of organic pollutant: Stability and involved Z-scheme mechanism.

The removal of dyes from wastewater by photocatalytic technologies has received substantial attention in recent years. In the present study, novel Z-scheme V2O5/g-C3N4 photocatalytic composites were organized via simple hydrothermal processes and a sequence of several characterization aspects. The degradation results showed that the optimum Z-scheme GVO2 heterostructure composite photocatalysts (PCs) had a better efficiency (90.1%) and an apparent rate (0.0136 min-1) for the methylene blue (MB) aqueous organic dye degradation, which was about 6.18-fold higher than that of pristine GCN catalyst. Meanwhile, the GVO2 heterostructured PCs showed better recycling stability after five consecutive tests. Moreover, the free radical trapping tests established that •O2- and h+ species were the prime reactive species in the photocatalytic MB degradation process in the heterostructured PCs. The photocatalytic enhanced activity was primarily recognized as the synergistic interfacial construction of the Z-scheme heterojunctions among V2O5 and GCN, which improved the separation/transfer, lower recombination rate, extended visible-light utilization ability, and enhanced reaction rate. Therefore, the existing study affords a simple tactic for the development of a direct Z-scheme for photocatalytic heterojunction nanomaterials for potential environmental remediation applications.