The nano-artificial periosteum made of PCL/MgO/AS-IV enhances MC3T3-E1 cell osteogenic differentiation and promotes bone defect repair via the EphB4/EphrinB2 signaling pathway.

Bone regeneration plays a pivotal role in periodontal tissue repair. With advancements in biotechnology materials, the utilization of nanotechnology offers a reliable platform for bone restoration in periodontitis. In this study, we successfully established a long-term bacterial infection model using Porphyromonas gingivalis (P. gingivalis) with MOI = 50. CCK-8 and ROS immunofluorescence results demonstrated that the combined effect of Mg2+ and AS-IV significantly enhanced cell proliferation and effectively suppressed the inflammatory response during bacterial infection. Alkaline phosphatase and alizarin red staining revealed that the synergistic action of Mg2+ and AS-IV notably promoted osteogenic differentiation of MC3T3-E1 cells under P. gingivalis-infected conditions. Considering the properties of these two biomaterials, we fabricated polycaprolactone (PCL) artificial periosteum loaded with MgO and AS-IV using an electrostatic spinning technique. The findings indicated that PCL/MgO/AS-IV artificial periosteum exhibited excellent biocompatibility and hydrophilicity, thereby substantially enhancing cellular adhesion to its surface as well as augmenting cellular value-added rate. Moreover, efficient drug release from the PCL/MgO/AS-IV artificial bone membrane conferred remarkable antimicrobial activity along with in vitro osteogenic potentiality. The in vivo experiments conducted on animals further substantiated the exceptional properties exhibited by PCL/MgO/AS-IV artificial periosteum in bone defect repair. Additionally, it was observed that PCL/MgO/AS-IV artificial periosteum could modulate EphB4-EphrinB2 signaling to enhance osteogenic differentiation under P.gingivalis-infected conditions.This exciting outcome suggests that PCL/MgO/AS-IV artificial periosteum holds great promise as a biomaterial for treating periodontal bone loss.

UCNPs-labeled electrospun scaffolds used to monitor in vivo degradation and bone tissue regeneration.

Biodegradable electrospun bone repair materials are effective means to treat bone defects. However, because the electrospun substrates are mostly organic polymer materials, there is a lack of real-time and intuitive monitoring methods for their degradation in vivo. Therefore, it is of great significance to develop in vivo traced electrospun bone repair materials for postoperative observation of their degradation. In this research, polycaprolactone/up-conversion nanoparticles/magnesium oxide (PCL/UCNPs/MgO) composite scaffolds were prepared by electrospun based on the luminescence characteristics of up-conversion nanoparticles (UCNPs) under near infrared excitation and the osteogenic ability of MgO. The in vivo and in vitro degradation results showed that with the increase of time, the electrospun scaffolds gradually degraded and its luminescence intensity decreased. The addition of UCNPs can effectively monitor the degradation of the scaffolds. In addition, the prepared electrospun scaffolds had great biocompatibility, among which PCL-1%UCNPs-1%MgO (P1U1M) electrospun scaffolds had obvious effect on promoting osteogenic differentiation of mouse embryonic osteoblasts cells (MC3T3-E1) in vitro. In conclusion, P1U1M electrospun scaffolds have the potential to induce bone regeneration at bone defect sites, and can monitor the degradation of electrospun scaffolds. It may be a potential candidate material for bone regeneration in defect area.