RESUMEN
The long-term performance, or resistance to elemental release, is the defining characteristic of a nuclear waste form. In the case of multiphase ceramic waste forms, correlating the long-term performance of multiphase ceramic waste forms in the environment to accelerated chemical durability testing in the laboratory is non-trivial owing to their complex microstructures. The fabrication method, which in turn affects the microstructure, is further compounding when comparing multiphase ceramic waste forms. In this work, we propose a "designer waste form" prepared via spark plasma sintering to limit interaction between phases and grain growth during consolidation, leading to monolithic high-density waste forms, which can be used as reference materials for comparing the chemical durability of multiphase waste forms. Designer waste forms containing varying amounts of hollandite in the presence of zirconolite and pyrochlore in a fixed ratio were synthesized. The product consistency test (PCT) and vapor hydration test (VHT) were used to assess the leaching behavior. Samples were unaffected by the VHT after 1500 h. As measured by the PCT, the fractional Cs release decreased as the amount of hollandite increased. Elemental release from the zirconolite and pyrochlore phases did not appear to significantly contribute to the elemental release from the hollandite phase in the designer waste forms.
RESUMEN
Transmittance measurements on various single crystal ferroelectric and dielectric materials, BaTiO(3), SrTiO(3), LiNbO(3), LiTaO(3), (PbMg(1/3)Nb(2/3)O(3))0.73-(PbTiO(3))0.27, LaAlO(3), and Bi(4)Ge(3)O(12), over a broad millimeter-wave (MMW) frequency range have been performed. Frequency dependence of the complex dielectric permittivity has been measured in the MMW region using high-power sources for the first time, using a free-space, quasi-optical MMW spectrometer equipped with high-power backward wave oscillators (BWOs) as sources of coherent radiation, tunable in the range from 30 to 120 and 180 to 260 GHz. These results are compared with MMW permittivity of these materials obtained by other methods as well as to RF, microwave, and optical frequency permittivities for all the materials tested. The effects of both crystallographic orientation and quality of the surface polishing of the crystals have been examined. Uncertainties and possible sources of instrumentation and measurement errors related to the freespace MMW technique are discussed. This work demonstrates that precise MMW permittivity data can be obtained even on relatively small and thin crystals of different surface conditions and orientations using the high-power BWO-based quasioptical approach.