Correspondence between try-in pastes and resin cements, and color stability of bonded lithium disilicate disks.

This study investigates the color correspondence of resin cements and try-in pastes, and the color stability of bonded lithium disilicate ceramic disks. Resin composite disks were fabricated (n = 36) to serve as the background for lithium disilicate disks prepared in two thicknesses (0.5 and 1.0 mm, n = 18 each). Two brands were used for try-in and cement procedures: Variolink Veneer and AllCem Veneer. For baseline, water was applied between the ceramic disks and their respective backgrounds to achieve the control group. This set was subjected to color measurement using an intraoral measurement device (T0). The try-in was inserted between background and ceramic, and this set was subjected to color measurement (T1). After adhesive procedures, the ceramic disk was placed under cement, and color measurement was performed with uncured cement (T2) and 24 h after light-curing (T3). Each set was immersed in distilled water and thermal-cycled, with color measurement being performed after 10,000 (T4) and 20,000 (T5) cycles. Color differences were calculated by CIELab (rEab) and CIEDE2000 (rE00). Data were analyzed by two-way ANOVA for repeated measurements and Tukey's test (α=5%). There was color correspondence of try-in and resin cement for the Variolink system, regardless of the ceramic thickness (p > 0.05). For the AllCem system, the thickness significantly influenced the color measurement (p < 0.001). The Variolink system also demonstrated color stability after 20,000 thermal cycles with rEab < 3.46 and rE00 < 2.25. It was concluded that the color correspondence between a try-in and its respective cement may vary according to resin cement composition.

Correspondence between try-in pastes and resin cements, and color stability of bonded lithium disilicate disks

Abstract: This study investigates the color correspondence of resin cements and try-in pastes, and the color stability of bonded lithium disilicate ceramic disks. Resin composite disks were fabricated (n = 36) to serve as the background for lithium disilicate disks prepared in two thicknesses (0.5 and 1.0 mm, n = 18 each). Two brands were used for try-in and cement procedures: Variolink Veneer and AllCem Veneer. For baseline, water was applied between the ceramic disks and their respective backgrounds to achieve the control group. This set was subjected to color measurement using an intraoral measurement device (T0). The try-in was inserted between background and ceramic, and this set was subjected to color measurement (T1). After adhesive procedures, the ceramic disk was placed under cement, and color measurement was performed with uncured cement (T2) and 24 h after light-curing (T3). Each set was immersed in distilled water and thermal-cycled, with color measurement being performed after 10,000 (T4) and 20,000 (T5) cycles. Color differences were calculated by CIELab (rEab) and CIEDE2000 (rE00). Data were analyzed by two-way ANOVA for repeated measurements and Tukey's test (α=5%). There was color correspondence of try-in and resin cement for the Variolink system, regardless of the ceramic thickness (p > 0.05). For the AllCem system, the thickness significantly influenced the color measurement (p < 0.001). The Variolink system also demonstrated color stability after 20,000 thermal cycles with rEab < 3.46 and rE00 < 2.25. It was concluded that the color correspondence between a try-in and its respective cement may vary according to resin cement composition.

In vitro Effects of Lemongrass Extract on Candida albicans Biofilms, Human Cells Viability, and Denture Surface.

The purpose of this study was to investigate whether immersion of a denture surface in lemongrass extract (LGE) has effects on C. albicans biofilms, human cell viability and denture surface. Minimal inhibitory concentration (MIC) and minimal fungicidal concentration (MFC) were performed for LGE against C. albicans. For biofilm analysis, discs were fabricated using a denture acrylic resin with surface roughness standardization. C. albicans biofilms were developed on saliva-coated discs, and the effects of LGE at MIC, 5XMIC, and 10XMIC were investigated during biofilm formation and after biofilm maturation. Biofilms were investigated for cell counting, metabolic activity, and microscopic analysis. The cytotoxicity of different concentrations of LGE to peripheral blood mononuclear cells (PBMC) was analyzed using MTT. The effects of LGE on acrylic resin were verified by measuring changes in roughness, color and flexural strength after 28 days of immersion. Data were analyzed by ANOVA, followed by a Tukey test at a 5% significance level. The minimal concentration of LGE required to inhibit C. albicans growth was 0.625 mg/mL, while MFC was 2.5 mg/mL. The presence of LGE during biofilm development resulted in a reduction of cell counting (p < 0.05), which made the MIC sufficient to reduce approximately 90% of cells (p < 0.0001). The exposure of LGE after biofilm maturation also had a significant antifungal effect at all concentrations (p < 0.05). When compared to the control group, the exposure of PBMC to LGE at MIC resulted in similar viability (p > 0.05). There were no verified differences in color perception, roughness, or flexural strength after immersion in LGE at MIC compared to the control (p > 0.05). It could be concluded that immersion of the denture surface in LGE was effective in reducing C. albicans biofilms with no deleterious effects on acrylic properties at MIC. MIC was also an effective and safe concentration for use.