Direct imaging of the magnetization reversal in microwires using all-MOKE microscopy.

We report a method of imaging of the magnetization reversal process using analysis of real-time images of magnetic domain structures in cylindrically shaped microwires. This method uses wide-field polarizing optical microscopy and is based on the magneto-optical Kerr effect (MOKE). The aperture diaphragm in MOKE microscope was used to control the incident angles of the light rays that reached the non-planar surface of the microwire and also determined the MOKE geometries. The movement of the non-central position of the hole in this diaphragm leads to a change in the orientation of the plane of incidence of the light along the perpendicular or the parallel direction to the axial direction of the wire. The visualization of the surface magnetic domain structures is obtained using polar and longitudinal MOKE geometries. The hysteresis loops were obtained by plotting the averaged image contrast as a function of the external magnetic field. The separation of the all-magnetization components is performed using different MOKE geometries in a microscope. We demonstrate the use of vector magnetometry to analyze the orientation of the magnetization in a cylindrically shaped microwire under the influence of an external magnetic field.

Domain-wall movement control in Co/Au multilayers by He(+)-ion-bombardment-induced lateral coercivity gradients.

Defined perpendicular anisotropy gradients in the Co sublayers of a [Co(0.6 nm)/Au(2 nm)](3) sputter-deposited multilayer have been introduced by light ion bombardment through a wedged Au stopper layer. Within such a layer system, domain walls between up- and down-magnetized areas are controllably movable by an external perpendicular homogeneous magnetic field. This method and layer system is very promising for a controlled magnetic particle transport within the stray fields of the moving domain walls.

New possibilities for tuning ultrathin cobalt film magnetic properties by a noble metal overlayer.

Complementary multiscale magneto-optical studies based on the polar Kerr effect are carried out on an ultrathin cobalt wedge covered with a silver wedge and subsequently with the Au thick layer. A few monolayers of Ag are found to have a substantial effect on magnetic anisotropy, the coercivity field, and Kerr rotation. The silver overlayer thickness-driven magnetic reorientation from easy axis to easy plane generates a new type of 90 degrees magnetic wall for cobalt thicknesses between 1.3 and 1.8 nm. The tuning of the wall width in a wide range is possible. Tailoring of the overlayer structure can be used for ultrathin film magnetic patterning.