Luminescence investigation of CaY2 Al4 SiO12 :Dy3+ phosphor synthesized by sol-gel method.

Dy3+ -doped CaY2 Al4 SiO12 phosphors were prepared using the sol-gel method. X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), and energy dispersive spectroscopy analyses (EDS) were used to analyse the crystal structure, morphology, and elemental composition of the prepared samples. The luminescence behaviour of the sample was investigated using photoluminescence (PL) and thermoluminescence (TL) techniques. The prepared CaY2 Al4 SiO12 :xDy3+ phosphor showed a characteristic blue and yellow emission at ~480 and 583 nm, respectively, with an excitation wavelength of 350 nm. The most intense PL emission was found for a 4 mol% doping concentration of Dy3+ ions. The CIE diagram of the phosphor showed bluish-white colour emission. For TL studies, the prepared phosphors were irradiated with a 60 Co γ (gamma) source and the TL glow curve of the CaY2 Al4 SiO12 :0.04Dy3+ phosphor showed three overlapped peaks. For the Gaussian peaks, Chen's peak shape method was applied to determine the kinetic parameters of the samples.

Investigations on luminescence behaviour of Ce-activated BaMgAl10 O17 phosphor.

The present paper describes the synthesis of cerium-doped barium magnesium aluminate phosphor by combustion method. The crystal structure of synthesized phosphor belongs to the P63 /mmc space group and is related to the ß-alumina structure. The photoluminescence emission spectra exhibited a broad peak centered at 440 nm showing the Ce3+ emission. The thermoluminescence properties of phosphors under ultraviolet irradiation were investigated. The activation energy was calculated by Chen's empirical method. Fracto-mechanoluminescence properties were also investigated. The phosphor showed mechanoluminescence (ML) properties without irradiation and the ML intensity increased linearly with the impact height of the moving piston. Therefore this compound may have a use as a damage sensor. Copyright © 2016 John Wiley & Sons, Ltd.

Photoluminescence and thermoluminescence studies of CaAl2O4:Dy(3+) phosphor.

Calcium aluminate phosphors activated by Dy(3+) have been prepared by a combustion method at a temperature of 600°C. Photoluminescence (PL) and thermoluminescence (TL) properties of gamma-irradiated Dy-doped calcium aluminate were investigated. The PL spectrum shows a broad peak around 488 nm and 573 nm, under 347 nm excitation. Thermoluminescence studies were performed for different concentrations of Dy. Optimum intensity of photoluminescence was found for 0.02 mol% concentration of Dy. It was found that initially the peak TL intensity increases with increasing concentration of Dy in the CaAl2O4 host, attains a maximum value for 0.05 mol% concentration and decreases with further increase in the doping concentration due to concentration quenching.