Biological Effects of PMMA and Composite Resins on Human Gingival Fibroblasts: An In Vitro Comparative Study.

The use of temporary resin for provisional restorations is a fundamental step to maintain the position of prepared teeth, to protect the pulpal vitality and the periodontal health as well as the occlusion. The present study aimed at evaluating the biological effects of two resins used in dentistry for temporary restorations, Coldpac (Yates Motloid) and ProTemp 4™ (3M ESPE ™), and their eluates, in an in vitro model of human gingival fibroblasts (hGFs). The activation of the inflammatory pathway NFκB p65/NLRP3/IL-1ß induced by the self-curing resin disks was evaluated by real-time PCR, Western blotting and immunofluorescence analysis. The hGFs adhesion on resin disks was investigated by means of inverted light microscopy and scanning electron microscopy (SEM). Our results suggest that hGF cells cultured in adhesion and with eluate derived from ProTemp 4™ (3M ESPE ™) resin evidenced a downregulation in the expression of the inflammatory mediators such as NFκB p65, NLRP3 and IL-1ß compared to the cells cultured with Coldpac (Yates Motloid) after 24 h and 1 week of culture. Furthermore, the cells cultured with ProTemp 4™ (3M ESPE ™) after 24 h and 1 week of culture reported a higher cell viability compared to the cells cultured with Coldpac (Yates Motloid), established by MTS cell analysis. Similar results were obtained when hGFs were placed in culture with the eluate derived from ProTemp 4™ (3M ESPE ™) resin which showed a higher cell viability compared to the cells cultured with eluate derived from Coldpac (Yates Motloid). These results highlighted the lower pro-inflammatory action and improved cell biocompatibility of ProTemp 4™ (3M ESPE ™), suggesting a better performance in terms of cells-material interaction.

Alveolar Ridge Preservation Using the One-Piece Autologous Tuberosity Graft: A Clinical, Radiological, and Histological Pilot Study.

This prospective study investigated clinically and radiologically the effectiveness of the use of a combined hard and soft tissue graft retrieved from the maxillary tuberosity and designed for alveolar ridge preservation following tooth extraction. Seven patients scheduled for a single mono-rooted tooth extraction were included in the study. After atraumatic extraction, sockets were filled with a "one-piece" dual tissue graft harvested from the tuberosity using an adjusted trephine. CBCTs were performed before the extraction and 4 months after ridge preservation, to analyze the vertical and horizontal alterations of the ridge, using ITK-Snap software. Clinical measurements of both soft and hard tissues were also assessed during the extraction and implant placement. All sites healed uneventfully. After 4 months, the 3D super-imposition of both CBCTs showed a mean bone volume resorption of 65 ± 76.7 mm3 (10.2 ± 10%). The mean horizontal reduction at 2, 4, and 6 mm from the top of the crest was respectively 1.5 ± 1.3 mm, 0.47 ± 1.4 mm and 0.57 ± 0.7 mm, while the mean vertical loss was 0.026 mm ± 2 mm. The mean soft tissue horizontal gain was 1.73 ± 1.12 mm. The "one-piece" autologous tuberosity graft was proven to be a safe and effective alveolar ridge preservation technique and may represent a feasible, user-friendly, time saving, low-cost solution for minimizing dimensional loss following tooth extraction.

Effect of temperature on presepsin pre-analytical stability in biological fluids of preterm and term newborns.

OBJECTIVES: Thermostability is one of the pre-requisites for the reliability of analytes in clinical practice and biomedical research. Although presepsin represents a promising new biomarker for the early diagnosis of sepsis in newborns, data on its stability under different storage conditions are lacking. We aimed to investigate presepsin thermostability in blood, urine and saliva samples after thawing at 4 predetermined monitoring time-points in a cohort of preterm and term infants. METHODS: We conducted an observational study, where each case served as its own control, in 24 preterm and term infants. Blood, urine and saliva samples were stored at -80 °C for 18 months, and presepsin measured in different biological fluids at thawing (T0), 24 (T1), 48 (T2) and at 72 (T3) hours after thawing. RESULTS: No significant differences (p>0.05, for all) in presepsin levels were observed at T0-T3 in the different biological fluids. Furthermore, no differences at T0-T3 were observed in presepsin levels between blood and saliva fluids, whilst urine levels were significantly higher (p<0.05, for all) than blood and saliva at T0-T3. CONCLUSIONS: Results on presepsin pre-analytical thermo-stability in different biological fluids after long-term refrigeration support the reliability of this biomarker in the diagnosis and monitoring of perinatal sepsis.

Finite element analysis in implant dentistry: State of the art and future directions.

OBJECTIVE: To discuss the state of the art of Finite Element (FE) modeling in implant dentistry, to highlight the principal features and the current limitations, and giving recommendations to pave the way for future studies. METHODS: The articles' search was performed through PubMed, Web of Science, Scopus, Science Direct, and Google Scholar using specific keywords. The articles were selected based on the inclusion and exclusion criteria, after title, abstract and full-text evaluation. A total of 147 studies were included in this review. RESULTS: To date, the FE analysis of the bone-dental implant system has been investigated by analyzing several types of implants; modeling only a portion of bone considered as isotropic material, despite its anisotropic behavior; assuming in most cases complete osseointegration; considering compressive or oblique forces acting on the implant; neglecting muscle forces and the bone remodeling process. Finally, there is no standardized approach for FE modeling in the dentistry field. SIGNIFICANCE: FE modeling is an effective computational tool to investigate the long-term stability of implants. The ultimate aim is to transfer such technology into clinical practice to help dentists in the diagnostic and therapeutic phases. To do this, future research should deeply investigate the loading influence on the bone-implant complex at a microscale level. This is a key factor still not adequately studied. Thus, a multiscale model could be useful, allowing to account for this information through multiple length scales. It could help to obtain information about the relationship among implant design, distribution of bone stress, and bone growth. Finally, the adoption of a standardized approach will be necessary, in order to make FE modeling highly predictive of the implant's long-term stability.

Nanostructured Calcium-Incorporated Surface Compared to Machined and SLA Dental Implants-A Split-Mouth Randomized Case/Double-Control Histological Human Study.

Background: Implant surface topography is a key element in achieving osseointegration. Nanostructured surfaces have shown promising results in accelerating and improving bone healing around dental implants. The main objective of the present clinical and histological study is to compare, at 4 and 6 weeks, (w) bone-to-implant contact in implants having either machined surface (MAC), sandblasted, large grit, acid-etched implant surface (SLA) medium roughness surface or a nanostructured calcium-incorporated surface (XPEED®). Methods: 35 mini-implants of 3.5 × 8.5 mm with three different surface treatments (XPEED® (n = 16)­SLA (n = 13)­MAC (n = 6), were placed in the posterior maxilla of 11 patients (6 females and 5 males) then, retrieved at either 4 or 6w in a randomized split-mouth study design. Results: The BIC rates measured at 4w and 6w respectively, were: 16.8% (±5.0) and 29.0% (±3.1) for MAC surface; 18.5% (±2.3) and 33.7% (±3.3) for SLA surface; 22.4% (±1.3) and 38.6% (±3.2) for XPEED® surface. In all types of investigated surfaces, the time factor appeared to significantly increase the bone to implant contact (BIC) rate (p < 0.05). XPEED® surface showed significantly higher BIC values when compared to both SLA and MAC values at 4w (p < 0.05). Also, at 6w, both roughened surfaces (SLA and XPEED®) showed significantly higher values (p < 0.05) than turned surface (MAC). Conclusions: Nanostructured Calcium titanate coating is able to enhance bone deposition around implants at early healing stages.

Accuracy of DICOM-DICOM vs. DICOM-STL Protocols in Computer-Guided Surgery: A Human Clinical Study.

Guided implant surgery can enhance implant placement positioning, increasing predictability and decreasing postoperative complications., To date, the best protocol to be used for template realization is still unknown. Thus, the aim herein was to clinically compare the accuracy of two different protocols. A total of 48 implants were divided into Group A (24 implants), in which a stereolithographic template was realized using the digital imaging and communications in medicine (DICOM) data arrived from cone beam computer tomographies (CBCTs) (patients and prothesis alone), and Group B (24 implant), in which a standard intraoral stent with a standardized extraoral support was used for patients' intraoral impressions and CBCT. The preimplant virtual planning and postsurgery CBCT images of both groups were superimposed, and differences were registered in terms of average deviations at the platform (a) and implant apex (b), mean depth change (c), and angular deviation (d). The results demonstrated that there were no statistically significant differences between groups (p = 0.76) for the parameters measured. However, statistically significant differences (p < 0.05) were found between maxillary and mandible implant surgery, as the latter showed greater accuracy. Additional studies are necessary to further reduce discrepancies between planning and surgical procedures.

Implant Periapical Lesion: Clinical and Histological Analysis of Two Case Reports Carried Out with Two Different Approaches.

Periapical implantitis (IPL) is an increasingly frequent complication of dental implants. The causes of this condition are not yet entirely clear, although a bacterial component is certainly part of the etiology. In this case series study, two approaches will be described: because of persistent IPL symptoms, a patient had the implant removed and underwent histological analysis after week 6 from implantation. The histomorphometric examination revealed a 35% bone-implant contact area involving the coronal two-thirds of the implant. The apical portion of the fixture on the other hand was affected by an inflammatory process detectable on radiography as a radiolucent area. The presence of a probable root fragment, detectable as an imprecise radiopaque mass in the zone where the implant was later placed, confirms the probable bacterial etiology of this case of IPL. On the other hand, in case number 2, the presence of IPL around the fixture was solved by surgically removing the implant apical third as well as the adjacent tooth apex. It may be concluded from our histological examination that removal of the apical portion of the fixture should be considered an effective treatment for IPL since the remaining implant segment remains optimally osseointegrated and capable of continuing its function as a prosthetic abutment. Careful attention, however, is required at the implantation planning stage to identify in advance any sources of infection in the edentulous area of interest which might compromise the final outcome.

Radiographic and Histomorphologic Evaluation of the Maxillary Bone after Crestal Mini Sinus Lift Using Absorbable Collagen-Retrospective Evaluation.

BACKGROUND: After tooth extraction, the alveolar bone loses volume in height and width over time, meaning that reconstructive procedures may be necessary to perform implant placement. In the maxilla, to increase the bone volume, a mini-invasive surgery, such as a sinus lift using the crestal approach, could be performed. METHODS: A crestal approach was used in this study to perform the sinus lift, fracturing the bone and inserting collagen (Condress®). The single dental implant was placed in the healed bone after six months. RESULTS: The newly formed bone was histologically analyzed after healing. Histomorphological analyses confirmed the quality of the new bone formation even without graft biomaterials. This is probably due to the enlargement of the space, meaning more vascularization and stabilization of the coagulum. CONCLUSION: Using just collagen could be sufficient to induce proper new bone formation in particular clinical situations, with a minimally invasive surgery to perform a sinus lift.

Lithium disilicate and zirconia reinforced lithium silicate glass-ceramics for CAD/CAM dental restorations: biocompatibility, mechanical and microstructural properties after crystallization.

OBJECTIVES: The objective of this study was to define the impact of heating rate on the crystal growth, the mechanical properties, and the biocompatibility of three different kinds of CAD/CAM glass-ceramics treated with a conventional furnace. METHODS: Lithium disilicate (IPS EMax-CAD, Ivoclar Vivadent) (LS2) and two zirconia reinforced lithium silicate (ZLS) ceramics (Vita Suprinity PC, VITA Zahnfabrik; Celtra Duo, Dentsply Sirona) (ZLSS; ZLSC) were used. The mechanical properties and the crystal growth were evaluated on 42 specimens (n = 14 per group). The thermal treatments recommended by the manufacturers were carried out. All groups were tested for fracture toughness (Ft) and Vickers hardness (Hv). Scanning electron microscope (SEM) images were taken after a slight surface etching with hydrofluoric acid solution (1% for 20 s). Differential Thermal Analysis (DTA) was performed and cellular adhesion with human periodontal ligament stem cells (hPDLSCs) culture was qualitatively assayed. Data were analyzed with Repeated Measurements ANOVA and ANOVA followed by Tukey post hoc test. RESULTS: The crystals' mean size (±SD) after heat treatment was 1650.0 (±340.0) nm for LS2, 854.5 (±155.0) nm for ZLSS and 759.9 (±118.4) nm for ZLSC (p < 0.05 among the groups). As consequence of crystallization, the Hv was 6.1 ± 0.3 GPa for LS2, 7.6 ± 0.7 GPa for ZLSS and 7.1 ± 0.5 GPa for ZLSC (p < 0.05 for LS2 vs ZLSS and ZLSC), while the Ft was 2.2 ± 0.1 MPa m1/2 for LS2, 4.7 ± 0.8 MPa m1/2 for ZLSS and 3.8 ± 0.6 MPa m1/2 for ZLSC (p < 0.05 among the groups). The DTA curves showed a crystallization process for LS2, ZLSS and ZLSC at a temperature range 810-840 °C. The amount of adherent hPDLSCs was superior on LS2 than on ZLS. CONCLUSIONS: All the CAD/CAM materials can be properly crystallized if heat treated following the manufacturers' instructions. The crystallization process highly depends on temperature. ZLS glass ceramics show significantly inferior crystals dimensions and higher fracture toughness and Vickers hardness than LS2 ceramic. hPDLSCs cultured on LS2 have a superior adhesion than those cultured on ZLS. CLINICAL SIGNIFICANCE: The value of this study relies on the demonstration that a proper heat-treatment of CAD/CAM lithium disilicate and ZLS glass ceramics generates products that are suitable for clinical use . The differences highlightable in mechanical properties and biocompatibility behavior do not affect their successful clinical application.

Water-Airborne-Particle Abrasion as a Pre-Treatment to Improve Bioadhesion and Bond Strength of Glass-Ceramic Restorations: From In Vitro Study to 15-Year Survival Rate.

The purposes of this study were to evaluate the efficacy of water-airborne-particle abrasion (WAPA) as pre-etching procedure for tooth surfaces to increase bond strength, and to compare the survival rate of WAPA vs. non-WAPA glass-ceramic restorations with a 15-year follow-up. The occlusal surfaces of 20 human molars were sectioned and flattened. The prepared surfaces areas were subdivided into two parts: one received WAPA treatment (prophy jet handpiece with 50 µm aluminium oxide particles) followed by acid etching (37% phosphoric acid for 20 s/3-step etch-and-rinse); the other one was only acid-etched. In total, 108 specimens were obtained from the teeth, of which 80 were used to measure the micro-tensile bond strength (µTBS) in the WAPA (n = 40) and control (n = 40) groups, while the remaining specimens (n = 28) were investigated via SEM to evaluate the micromorphology and roughness (Ra) before and after the different treatment steps. The survival rate (SR) was performed on 465 glass-ceramic restorations (131 patients) comparing WAPA treatment (n = 183) versus non-WAPA treatment (n = 282). The bond strength was 63.9 ± 7.7 MPa for the WAPA group and 51.7 ± 10.8 MPa for the control group (p < 0.001). The Ra was 98 ± 24 µm for the enamel control group, 150 ± 35 µm for the enamel WAPA group, 102 ± 27 µm for the dentin control group and 160 ± 25 µm for the dentin WAPA group. The Ra increase from the WAPA procedure for enamel and dentin was statistically significant (p < 0.05). Under SEM, resin tags were present in both groups although in the WAPA they appeared to be extended in a 3D arrangement. The SR of the WAPA group (11.4 years) was 94%, while the SR of the non-WAPA group (12.3 years) was 87.6% (p < 0.05). The WAPA treatment using aluminium oxide particles followed by a 3-step etch-and-rinse adhesive system significantly improved bioadhesion with an increased bond strength of 23.6% and provided superior long-term clinical performance of glass-ceramic restorations.

Customized-3D zirconia barriers for guided bone regeneration (GBR): clinical and histological findings from a proof-of-concept case series.

OBJECTIVES: The aim of this case series was to evaluate, clinically and histologically, customized-3D zirconia barriers manufactured for guided bone regeneration (GBR) procedures. METHODS: Seven healthy consecutive patients with severe bone atrophy (two of them with a bilateral atrophy) were selected for a GBR procedure with a zirconia barrier. In a 3D software (DentalCad, Exocad GmbH, Germany), a virtual bone graft was designed and a shell was designed covering the graft; a standard tessellation language (.STL) file was obtained and milled (M1, Zirkonzahn, Italy) using a 1200 MPa zirconia (Prettau, Zirkonzahn, Italy). Nine GBR surgeries (8 upper-posterior jaw, 1 lower-posterior jaw) were performed using autogenous bone chips mixed with xenograft (SmartBone, IBI-SA, Switzerland / BioOss, Geistlich, Switzerland) covered with a zirconia barrier, fixed by means of screws. After healing, implant sites were prepared with a trephine bur, collecting a bone biopsy, and dental implants were inserted (Neodent, Straumann Group, Switzerland). Specimens were histologically analyzed. RESULTS: Eight successful surgeries were recorded; one zirconia barrier got exposed after one month of healing but no signs of infection were present till the barrier was removed. In all cases it was possible to insert implants with no additional bone augmentation procedures. Histological evaluations showed the presence of intense deposition of new bone. CONCLUSIONS: Within the limitations of the present case series, the tested customized-3D zirconia barriers confirmed good clinical and histological performances, and, even in case of premature exposure, did not show signs of infection. Preliminary results suggest they are effective for GBR procedures. Further research is necessary with a larger sample size. CLINICAL SIGNIFICANCE: The presented barriers could be a viable alternative to titanium-reinforced polytetrafluoroethylene membranes and customized meshes.

Collagen Fibres Orientation in the Bone Matrix around Dental Implants: Does the Implant's Thread Design Play a Role?

The aim of this study was to analyse the influence of different thread shapes of titanium dental implant on the bone collagen fibre orientation (BCFO) around loaded implants. Twenty titanium dental implants, divided for thread shapes in six groups (A-F) were analysed in the present study. All implants were immediately loaded and left in function for 6 months before retrieval. The parameters evaluated under scanning electron microscope were the thread width, thread depth, top radius of curvature, flank angle, and the inter-thread straight section. Two undecalcified histological sections were prepared from each implant. Birefringence analysis using circularly polarized light microscopy was used to quantitively measure BCFO. For groups A-F, respectively, transverse BCFO was 32.7%, 24.1%, 22.3%, 18.2%, 32.4%, and 21.2%, longitudinal BCFO was 28.2%, 14.5%, 44.9%, 33.1%, 37.7%, and 40.2%. The percentage differences between transverse and longitudinal orientation were 4.50% (A), 9.60% (B), -22.60% (C), -14.90% (D), -5.30% (E), and -19.00% (F). Following loading, the amount of transverse and longitudinal BCFO were significantly influenced by the thread shape. The greater flank angles and narrower inter-thread sections of the "V" shaped and "concave" shaped implant threads of groups A and B, respectively, promoted the predominance of transverse BCFO, compared to groups C-F (p < 0.05). A narrow inter-thread straight section promotes transverse BCFO, as do "V" shaped and "concave" shaped threads, which can thus be considered desirable design for implant threads.

Advances in Dental Materials "at a Glance."

Dental materials play a fundamental role in the rehabilitation of tooth structures and regeneration of oral tissues [...].

Graphene Oxide affects Staphylococcus aureus and Pseudomonas aeruginosa dual species biofilm in Lubbock Chronic Wound Biofilm model.

Chronic wound management becomes a complex procedure because of the persistence of forming biofilm pathogens that do not respond to antimicrobial treatment. The aim of this paper is to detect the Graphene Oxide-GO effect on Staphylococcus aureus and Pseudomonas aeruginosa dual species wound biofilm in Lubbock Chronic Wound Biofilm-LCWB model. LCWB is a recognized model that mimics the spatial microbial colonization into chronic wounds and reproduces the wound and its clot. Staphylococcus aureus PECHA 10 and P. aeruginosa PECHA 4, are the pathogens used in the study. The GO effect on both in forming and mature biofilms, is detected by the evaluation of the CFU/mg reduction, the cell viability and ultrastructural analysis of the treated LCWBs. Graphene Oxide, at 50 mg/l, shows a significant antibiofilm effect in forming and mature LCWBs. In particular, during the biofilm formation, GO reduces the S. aureus and P. aeruginosa growth of 55.05% ± 4.73 and 44.18% ± 3.91 compared to the control. In mature biofilm, GO affects S. aureus and P. aeruginosa by reducing their growth of 70.24% ± 4.47 and 63.68% ± 17.56, respectively. Images taken by SEM show that GO display a disaggregated microbial effect also disrupting the fibrin network of the wound-like biofilm framework. In conclusion, GO used against microorganisms grown in LCWB, displays a significant inhibitory action resulting in a promising tool for potential application in wound management.

Gingival Response to Dental Implant: Comparison Study on the Effects of New Nanopored Laser-Treated vs. Traditional Healing Abutments.

The health of peri-implant soft tissues is important for the long-term success rate of dental implants and the surface topography is pivotal in influencing it. Thus, the aim of this study was to evaluate, in human patients, the inflammatory mucosal microenvironment in the tissue surrounding a new, nanoscale, laser-treated healing abutment characterized by engineered nanopores versus a standard machined-surface. Analyses of anti- and pro-inflammatory markers, cytokeratins, desmosomal proteins and scanning electron microscopy were performed in 30 soft-tissue biopsies retrieved during second-stage surgery. The results demonstrate that the soft tissue surrounding the laser-treated surface was characterized by a lower grade of inflammation than the one facing the machined-surface, which, in turn, showed a disrupted epithelium and altered desmosomes. Moreover, higher adhesion of the epithelial cells on the laser-treated surface was detected compared to the machined one. In conclusion, the laser-treated surface topography seems to play an important role not only in cell adhesion, but also on the inflammatory makers' expression of the soft tissue microenvironment. Thus, from a clinical point of view, the use of this kind of topography may be of crucial importance not only on healing abutments but also on prosthetic ones.

Influence of Dentine Pre-Treatment by Sandblasting with Aluminum Oxide in Adhesive Restorations. An In Vitro Study.

Dentine pretreatment through sandblasting procedures has been widely studied but no curve test results are currently available. Thus, the aim herein was to in vitro compare the adhesive strength in sandblasted or not samples using a universal testing machine. Thirty -two bovine teeth were divided into two groups, namely test (n = 16 bars), sandblasting with aluminum oxide particles (50 µm) was performed before the adhesion procedures), and control (n = 16 bars), where no sandblasting procedure was performed. A bi-material curve test was used to evaluate the characteristics of the dentine pretreatment in terms of tensile stress and fracture strength. A scanning electron microscope (SEM) was used to analyze the fracture topography in the composite, bonding, dentin, and at the relative interfaces. The results demonstrated a statistically significant difference between the two groups in terms of tensile stress at maximum load showing values of 84.300 ± 51.342 MPa and 35.071 ± 16.609 MPa, respectively for test and control groups (p = 0.033). Moreover, a fracture strength test showed values of 18.543 ± 8.145 MPa for test and 8.186 ± 2.833 MPa for control group (p = 0.008). In conclusion, the sandblasting treatment of the dentine significantly influenced the mechanical resistance of the adhesion in this in vitro study.

Graftless Maxillary Sinus Floor Augmentation with Simultaneous Porcine Bone Layer Insertion: A 1- to 5-Year Follow-up Study.

PURPOSE: Evidence suggests that maxillary sinus floor augmentation via a lateral approach can be performed without positioning a bone graft inside, when one or more implants can be placed simultaneously. The aim of this study was to test if the placement of a porcine cortical bone layer underneath the sinus membrane can increase bone formation and implant stability. MATERIALS AND METHODS: One hundred seventy-two patients with posterior maxilla atrophy needing implant rehabilitation were selected. Two hundred six sinus augmentation procedures were performed via a lateral approach, and 295 implants were placed in the same session of the sinus elevation surgery. In all the surgeries, a porcine cortical bone layer was placed underneath the sinus membrane, without using any graft material. After 6 to 7 months of healing, the implants were uncovered, then restored with porcelain-fused-to-metal crowns and monitored with a followup of 1 to 5 years. RESULTS: The implant cumulative success rate was 95.2%, while the residual bone crest height changed from 2.67 ± 1.11 mm to 12.54 ± 1.42 mm, with an increase of 9.87 mm on average. Marginal bone resorption was 0.83 mm on average after 1 year of loading, while the mean implant stability measured at the moment of implant placement and 6 to 7 months later increased from an implant stability quotient (ISQ) of 62.61 ± 5.7 to an ISQ of 70.07 ± 8.2. CONCLUSION: This study confirms the validity of the graftless sinus elevation surgery when simultaneous implant placement is performed. The use of a porcine cortical bone layer seems to increase, from a radiologic point of view, the amount of bone around the implants, reducing healing time, cost, and biologic complications for the patient.

A 4 Year Human, Randomized, Radiographic Study of Scalloped versus Non-Scalloped Cemented Implants.

Marginal bone loss (MBL) is a key factor in long-term implant success rate. Among the different factors that influence MBL, it is the different implant shoulder designs, such as scalloped or non-scalloped, which have been widely studied on screw retained but not on cemented retained implants. Thus, the aim of the present study was to evaluate the MBL around scalloped and non-scalloped cemented retained dental implants after 4 years of loading, in humans. A total of 15 patients were enrolled in the present study. A radiographic and clinical examination was performed after implant placement (T0) and after 4 years from it (T1). The results demonstrated a differential MBL (T1-T0) of 2.436 ± 1.103 mm and 1.923 ± 1.021 mm, respectively for test (scalloped) and control (non-scalloped) groups with a statistically significant difference between them. On the other hand, no statistically significant differences were found between the groups in terms of prosthetic complication and abutment decementation, whilst ceramic crowns chipping was shown in both groups. In conclusion, the use of a scalloped platform did not provide better results on the maintenance of MBL after 4 years follow-up. In this study, this probably was determined by multiple factors, among which was the subcrestal insertion of scalloped implants.

Fracture Resistance of Zirconia-Reinforced Lithium Silicate Ceramic Crowns Cemented with Conventional or Adhesive Systems: An In Vitro Study.

In recent years, Zirconia-reinforced Lithium Silicate ceramic (ZLS), combining lithium-silicate and zirconia features, has shown to have excellent mechanical and aesthetic characteristics. Thus, the aim of this study was to compare the fracture strength of ZLS single crowns cemented with two different cementation techniques. Twenty crowns were realised and cemented on teeth replicas achieved from an extracted premolar human tooth. The samples were divided into two groups of 10 specimens each, Glass-ionomeric cement (GIC) group and Self-Adhesive Resin Cement (ARC) group. The mechanical test was performed using a universal testing machine. The specimens were then evaluated with a scanning electron microscope (SEM) to identify for all crowns and related abutments the pattern of fracture after the breaking point. The data obtained were statistically analysed. The mean fracture toughness values and standard deviations (±SD) were 2227 ± 382 N and 3712 ± 319 N respectively for GIC and ARC groups. In fact, t-test showed a statistically significant difference between the two groups (p < 0.001). Moreover, the SEM results demonstrated portions of abutments still attached to the crown fragments in the ARC group, whilst these were not present in the GIC group. Within the limitations of this study, these results suggest the use of adhesive cementation for ZLS crowns, which significantly increase the compressive strength of ZLS restorations compared to GIC.

Penetration of Different Impression Materials into Exposed Dentinal Tubules during the Impression Procedure.

Adhesive restorations have been shown to guarantee excellent performance and longevity, although this comes with some disadvantages. Among these, the vulnerability of dentine to different agents has been widely evaluated. The aim of this study was to evaluate the possible penetration of impression materials into freshly cut dentine. Dentine from 27 teeth was impressed with polyether (Impregum Penta L) (nine teeth) and with polyvinyl siloxane (Aquasil Ultra LV) (nine teeth). The surface of nine teeth after the impressions were used as the control. Specifically, the extroflections caused by the imprinting of the dentinal tubules on the impression material, the so-called impression tags, were measured. Furthermore, the presence of the material inside the tubules was examined. Scanning electron microscopy analysis showed material tags for all of the experimental groups. The mean lengths (±SD) were 22.6 (±11.0) µm for polyether, 21.8 (±12.8) µm for polyvinyl siloxane and 11.3 (±7.0) µm for the tooth control, with mean diameters (±SD) of 2.8 (±0.5), 2.4 (±0.7) and 3.1 (±0.7) µm, respectively. Fractal analysis showed fractal dimensions of 1.78 (±0.03), 1.77 (±0.03) and 1.71 (±0.03), respectively. These data demonstrated that the impression materials can remain inside the dentinal tubules, which can adversely affect the adhesive procedures.